一種吸附膜的制備及其吸附性能

賈威

摘要：提出一種硅藻土膜制備的方法，利用聚乙烯醇樹(shù)脂經(jīng)加熱處理后包裹硅藻土經(jīng)過(guò)擠壓制備吸附膜對(duì)酚酞溶液進(jìn)行吸附脫色研究。試驗(yàn)結(jié)果表明：對(duì)酚酞去除率較高，隨著聚乙烯醇樹(shù)脂含量的增加，吸附性能顯著提高；并且隨著硅藻土的增加，去除率迅速增加，并考察了溫度對(duì)吸附膜穩(wěn)定性的影響，

關(guān)鍵詞：聚乙烯醇樹(shù)脂、硅藻土、酚酞、吸附

Preparation and adsorption properties of a kind of adsorption membrane

ABSTRACT：A method of preparation of diatomite membrane is proposed， using polyvinyl alcohol resin after heat treatment package diatomite after extrusion preparation adsorption film of phenolphthalein solution by adsorption decolorization. Test results show that the higher removal rate of phenolphthalein， along with the increase of the content of polyvinyl alcohol resins， adsorption performance is significantly improved； and with the increase of diatomite， the removal rate increased rapidly， and to investigate the effect of temperature on the stability of the adsorbed film.

KEY WORDS：Polyvinyl alcohol resin；diatomite；phenolphthalein， adsorption

一、引言

利用聚乙烯醇樹(shù)脂能黏結(jié)特性，并有一定彈性的黏性將加熱溶解的聚乙烯醇樹(shù)脂與細(xì)粉狀硅藻土黏結(jié)在一起，經(jīng)過(guò)擠壓形成有彈性的吸附薄膜。

1、試劑。固體石蠟；聚乙烯醇樹(shù)脂；硅藻土；添加劑所有化學(xué)試劑均為分析純級(jí)。

2、實(shí)驗(yàn)方法。先將聚乙烯醇樹(shù)脂放入燒杯中，在超級(jí)恒溫水浴箱中加熱至90℃左右，待融化后在攪拌器不斷攪拌下，加入溶劑油，攪拌均勻后加入硅藻土；再次攪拌均勻后，加入添加劑，攪拌均勻后經(jīng)過(guò)擠壓冷卻得到產(chǎn)品。

二、分析與討論

1、聚乙烯醇樹(shù)脂含量對(duì)去除率的影響如圖1：

由圖中可以看出聚乙烯醇樹(shù)脂含量增加，去除率增加顯著。

2、硅藻土含量對(duì)去除率的影響如圖2：

由圖中可以看出活性炭粉增加到0.55mol/g之后吸附率開(kāi)始下降。

3、溫度對(duì)吸附膜穩(wěn)定性的影響如圖3：

由圖中可以看出在隨著溫度的增加，吸附膜的穩(wěn)定性不斷降低，在60℃以下穩(wěn)定性最好。

參考文獻(xiàn)

[1] 何吉字，譚慧民 .高技術(shù)通訊 ，2003 ，（2）：41

[2] 葉成兵 ，張軍 .中國(guó)塑料 ，2003，17 （10）：1241-243.

[3] 張獎(jiǎng)池，周艷，鄒凌峰，等.石化技術(shù)，2002，9（2）：83-86.