    Plasma activation towards oxidized nanocarbons for efficient electrochemical synthesis of hydrogen peroxide

    2021-02-27 09:17:06WeiCAI蔡偉YanWANG王燕ChangshanXIAO肖長山HaobinWU吳浩斌andXinyaoYU遇鑫遙
    Plasma Science and Technology 2021年2期
    關(guān)鍵詞:長山王燕

    Wei CAI (蔡偉), Yan WANG (王燕), Changshan XIAO (肖長山),Haobin WU (吳浩斌)and Xinyao YU (遇鑫遙)

    1 School of Materials Science & Engineering, Zhejiang University, Hangzhou 310027, People’s Republic of China

    2 Institutes of Physical Science and Information Technology, Anhui University, Hefei 230601, People’s Republic of China

    3 Wendian College, Anhui University, Hefei 230601, People’s Republic of China

    Abstract Oxidized nanocarbons (ONCs) have been regarded as efficient electrocatalysts for H2O2 production.However,wet chemical procedures involving large volumes of strong acid and long synthetic time are usually needed to obtain these ONCs.Herein, a plasma activation strategy is developed as a rapid and environmentally benign approach to obtain various ONCs, including oxidized multiwalled carbon nanotubes, single-walled carbon nanotube, graphene, and super P carbon black.After a few minutes of plasma activation,oxygen-containing functional groups and defects can be effectively introduced onto the surface of nanocarbons.Enhanced electrocatalytic activity and selectivity are demonstrated by the plasma-ONCs for H2O2 production.Taking oxidized multiwalled carbon nanotubes as an example,high selectivity(up to 95%)and activity(0.75 V at 1 mA cm?2) can be achieved in alkaline solution.Moreover, ex situ x-ray photoelectron spectroscopy and in situ Raman measurements reveal that C–O, C=O, edge defect, and sp2 basal planar defect are probably the active sites.

    Keywords:plasma activation,hydrogen peroxide,nanocarbon,defect,oxygen functional groups

    1.Introduction

    Hydrogen peroxide (H2O2) is an important chemical reagent with high application value.It has been widely used in industry, medicine, environment and military industry, for example, as a disinfectant, bleaching agent and combustion supporting agent [1–3].Until now, there have been generally two methods to produce H2O2in industry.One is the traditional anthraquinone process with high energy consumption and serious pollution [1].The other is the direct synthesis from hydrogen and oxygen, which has potential safety hazards [4–7].At the same time, the instability of H2O2makes storage and transportation problem to be solved [8].Recently,the convenient and green 2e–-based electrocatalytic oxygen reduction reaction (ORR) method forin situgeneration of H2O2is attracting more and more attention [9–11].

    Generally speaking, in alkaline electrolyte, ORR can be carried out through two reaction paths [12–14]:

    Due to the competition of two reactions in ORR processes and the limitation of the kinetics, the key is to explore an electrocatalyst with high activity and selectivity for 2e–ORR[15–17].To this end,noble metals and their alloys(such as Pd-Au [18], Pt-Hg [19], Pd-Hg [20] etc) with low onset potential and high selectivity (more than 90%) have been developed [21–23].However, their large-scale application is seriously hindered because of the expensive price and lack of resources.Most recently, carbon materials with abundant reserves and large structural adjustability have been investigated as promising noble metal substitute catalysts for the electrocatalytic synthesis of H2O2[24–29].

    Among the reported carbon materials, oxidized nanocarbons (ONCs) are very efficient electrocatalysts for H2O2production.The surface oxygen-containing groups and defects of ONCs play important roles in selective synthesis of H2O2with high activity.For example,Luet al[9]used strong acid to oxidize nanocarbons to realize the regulation of the surface oxidation state, significantly improving the activity and selectivity (~90%) for generating H2O2.However, oxidation of nanocarbons with strong acid is a wet chemical process, requiring a large number of chemical reagents and a relatively long processing time(in hour scale).Kimet al[13]employed thermally reduced graphene oxide as an electrocatalyst to synthesize H2O2with high selectivity and stability at low overpotential in alkaline condition.Nevertheless, the preparation of graphene oxide is cumbersome and requires a large number of purification steps to remove the impurities of metal ions introduced in the synthesis process.As such, it is meaningful but urgent to develop an efficient and environmentally friendly approach to obtain ONCs with enhanced activity and selectivity for electrocatalytic synthesis of H2O2.

    Plasma activation technology is a low-temperature,timeefficient, and dry method to realize surface modification of carbon materials.Plasma contains a large number of ions,excited molecules, metastable particles, photons and other active particles.The energy of most of these particles is higher than that of C=C and C–C, which means that these particles can destroy the original chemical bonds on the surface of carbon materials and form new bonds [30, 31], thus endowing the surface of materials with new characteristics.In Ar/O2plasma, a large amount of Ar+ions and oxygencontaining excited species exist.The Ar+ions will etch the surface of carbon materials to generate defects and surfacebound radicals [32].On the other hand, the oxygen-containing species in Ar/O2plasma can interact with the dangling bonds to form corresponding functional groups [33].

    Herein, we develop an O2/Ar plasma activation strategy instead of the traditional chemical activation technology, and it was experimentally proved that this strategy is applicable for commercial carbon nanomaterials with various morphologies (multiwalled carbon nanotubes (MWCNTs), singlewalled carbon nanotube (SWCNT), graphene (G), and super P carbon black(SP)).O2/Ar plasma can effectively introduce oxygen-containing functional groups (C–O and C=O) and defects onto the surface of nanocarbons in 5 min without using any chemicals.In addition, the amount of oxygencontaining groups and defects can be easily controlled by the plasma parameters.Compared with raw commercial nanocarbons, the potential at 1 mA cm?2is positively shifted and the selectivity for H2O2is greatly improved in a wide voltage window.Most importantly, possible active sites (oxygen functional groups and defects) during the electrocatalytic synthesis of H2O2are identified byex situx-ray photoelectron spectroscopy andin situRaman measurements.

    Figure 1.Schematic diagram of plasma activation of nanocarbons.

    2.Experimental

    2.1.Materials

    MWCNTs (purity >95%, length: 0.5–2 μm, diameter:8–15 nm), SWCNT (purity >95%, diameter: 1–2 nm, length:1–3 μm), and G powder synthesized with a physical method(sheet diameter: 0.5–5 μm, thickness: around 0.8 nm, single layer rate: 80%) were provided by Nanjing XFNANO Materials Tech Co., Ltd.SP was purchased from Shenzhen Ruiheda Technology Co., Ltd.Nafion solution (5 wt%) was provided by Sigma-Aldrich.Potassium hydroxide (KOH),perchloric acid (HClO4), H2O2(30%), sodium dihydrogen phosphate, and disodium hydrogen phosphate were provided by Sinopharm Chemical Reagent Co., Ltd.Potassium titanium oxalate and phenol were purchased from Macklin Inc.Hydrophobic carbon paper was provided by Shanghai Hesen Electric Co., Ltd.

    2.2.Preparation of ONCs

    The specific preparation process of ONCs is shown in figure 1; 30 mg of nanocarbons were evenly spread onto a quartz glass dish and put into the plasma enhanced chemical vapor deposition (PECVD) equipment with a RF plasma source (13.56 MHz, 0–500 W) for plasma oxidation.The plasma oxidation process was carried out at room temperature.Up to about 0.5 g of nanocarbons can be processed per hour.The ratio of O2to Ar was 9:1, 3:7, and 5:5.The gas pressure was 40 Pa, 50 Pa, and 60 Pa.The RF plasma power was 150 W, 250 W, and 350 W, and the activation time(3 min,5 min,and 10 min)was varied.MWCNTs were stirred with nitric acid (12 M) at 80 °C for 48 h to realize traditional chemical oxidation and the obtained sample is denoted as O-MWCNTs.

    2.3.Physio-chemical characterizations

    Transmission electron microscopy(TEM)and high-resolution TEM (HRTEM) images were measured by FEI Tecnai G2 F20.HRTEM images with spherical aberration correction were taken by FEI Titan G2 60–300.X-ray diffraction(XRD)patterns in the 2θ range from 5° to 80° were obtained by PANAlytical X’Pert PRO instrument.The x-ray photoelectron spectroscopy (XPS) was measured by Thermo Fischer ESCALAB 250 Xi.Fourier transform infrared (FT-IR)spectra were obtained from the Nicolet 5700 spectrometer.A LabRam HRUV ultraviolet laser Raman spectrometer was used to obtain Raman spectra.A confocal microscopy(Confotec?MR 520)using 532 nm laser was used to collectin situRaman spectra.The concentration of H2O2was determined by MAPADA-P4CP UV spectrophotometer.Before the above-mentioned characterizations, the obtained samples were kept in sealed conditions, except for the unavoidable contact with air.

    2.4.Electrode preparation and electrochemical characterizations

    First, 5 mg of carbon material was dispersed in 950 μl of alcohol and 50 μl of Nafion,and the slurry(0.5 mg ml?1)was obtained by ultrasound for about 30 min.Then, 10 μl of the catalyst ink was dropped onto the surface of a glassy carbon electrode with an area of 0.2475 cm2as the working electrode.A CHI 760E electrochemical workstation was used to perform the electrochemical measurements.A saturated calomel electrode and a carbon rod were employed as reference electrode and counter electrode, respectively.Three electrolytes (0.1 M KOH with pH ~ 13, 0.1 M phosphate buffered saline (PBS) with pH ~ 7 and 0.1 M HClO4with pH ~ 1) were used for testing.A rotating ring disk electrode(RRDE)was employed to evaluate the activity and selectivity for ORR in oxygen saturated electrolyte [19, 34, 35].

    To investigate the ORR activity, linear sweep voltammogram (LSV) curves were recorded in the range of 0.4–1.1 V versus reversible hydrogen electrode (RHE).The scan rate in the LSV test was 5 mV s?1.The electrochemically active surface area (ECSA) was assessed by the electrochemical double-layer capacitance (Cdl) of the electrocatalysts.A series of cyclic voltammetry(CV)curves were measured at various scan rates(5,10,15,20 and 25 mV s?1).At 0.115 V versus RHE, theCdlcan be obtained from the function between disk current density (j) and scan rates.

    According to equation (1) and the relationship between the ring current and the disk current of the rotating ring disk electrode, the 2e?ORR selectivity of the catalysts was obtained easily.During the testing process, the speed of rotation was controlled at 1600 rpm and the potential on the ring of the working electrode was set at 1.2 V versus RHE.

    whereIRis the ring current,IDrepresents the disk current,andNstands for the collection efficiency.In our workN= 0.37.

    2.5.Measurement of H2O2 concentration

    The Teflon-treated carbon fiber paper (CP) was cut into a proper size, and the catalyst slurry (Valcohol:Vdeionizedwater:VNafion= 470: 470: 60) was painted uniformly onto CP(1×1 cm2) with controlled loading of about 0.5 mg cm?2.Then, the CP loaded with catalyst was used as the working electrode and the accumulation of electrochemically synthetized H2O2was performed in an H-cell in 0.1 M KOH solution, using Nafion?117 membrane as a separator.In the two compartments, the volume of electrolyte was controlled at 25 ml and O2was continuously supplied at a flow rate of 200 ml min?1to ensure that the electrolyte reaches oxygen saturation state.

    The H2O2concentration was measured by a titanium salt spectrophotometry method [36].The color depth of the complex is directly proportional to the content of H2O2in the sample.The specific operation process is as follows: an appropriate amount of electrolyte in the compartment of ORR was added to the 0.05 M potassium-titanium oxalate K2TiO(C2O4)2solution.After that,the pH value was adjusted by adding deionized water and sulfuric acid and the sample was placed stably for 10 min.The absorption coefficient at 400 nm wavelength was observed by spectrophotometer and the concentration of H2O2was determined by comparing with the standard curve.

    Based on the equation(2),the current efficiency of H2O2generated can be calculated:

    wherenis the number of electrons in reducing O2to H2O2(n= 2),Fis the Faraday constant,Cis the concentration of H2O2,Vrepresents the volume of electrolyte,andQstands for the amount of passed charge.

    2.6.Degradation of phenol

    The degradation device is similar to the H2O2generation device and only the electrolyte was changed into an acid solution with pH = 3 regulated by sulfuric acid.Phenol was added into the electrolyte as an organic pollutant with a concentration of 50 mg l?1.The concentration of phenol was analyzed by high-performance liquid chromatography(HPLC, DGU20A3R, Shimadzu, Japan).

    3.Results and discussion

    3.1.Characterization of the MWCNTs and PO-MWCNTs

    We first employ MWCNTs as a typical nanocarbon to demonstrate the role of plasma activation in promoting the selectivity and activity for H2O2production.The optimized plasma-oxidized MWCNTs (denoted as PO-MWCNTs) are obtained at the plasma power of 250 W,gas pressure of 40 Pa,O2/Ar ratio of 9/1, and activation time of 5 min.TEM images (figures 2(a) and (b)) and XRD patterns (figure 2(f))show that no obvious changes in structure and phase after plasma oxidation can be found, confirming that plasma activation is a mild process without destroying the original structure of carbon nanotubes.However, HRTEM images demonstrate that a coarse and irregular defect layer with a thickness of about 2 to 3 nm is generated on the surface of PO-MWCNTs (figures 2(c) and (d)) due to the etching effect of plasma.The introduction of defects can also be verified by the Raman spectrum with slightly increased intensity ratio of D band to G bandfrom 1.09 to 1.16 after plasma oxidation (figure 2(e)), and the amount of defects can be tuned by the plasma processing time (figure S1 available online at stacks.iop.org/PST/23/025502/mmedia).

    From the above analysis,it can be concluded that plasma oxidation mainly occurs on the surface of the MWCNTs.To further explore the effect of plasma activation on elements and chemical states of the MWCNTs and PO-MWCNTs,XPS measurement is performed.As shown in figure 3(a), the intensity of O 1s peak is significantly enhanced in POMWCNTs and the oxygen content is increased from 1.6% to 8.4%.The C 1s spectrum can be fitted by C–C in graphite at 284.5 eV, defects (carbon atoms lose their regular arrangement) at 285.4 eV, C–O at 286.1 eV, O–C=O at 288.7 eV(such as –COOH), and π-π*transition at 290.5 eV corresponding to the shakeup line of carbon in aromatic compounds.Meanwhile, the O 1s spectrum can be fitted by O–C at 533.2 eV and O=C at 531.6 eV.The introduction of C–O and C=O can also be confirmed by FT-IR(figure S2).Comparing the C 1s and O 1s spectra of MWCNTs and PO-MWCNTs(figures 3(b)–(f)), it can be seen that after plasma oxidation the defect proportion and the ratio of C–O to C=O increase obviously.The ratio of C–O/C=O and the content of surface defects achieve the maximum at the oxidation time of 5 min(figure S3,tables S1 and S2).The above results evidence that the Ar/O2plasma can effectively introduce controllable defects and oxygen-containing functional groups onto nanocarbons.

    3.2.Electrochemical performance of MWCNTs and POMWCNTs

    RRDE is employed to evaluate the effect of plasma activation on the electrochemical properties of the electrocatalysts.As mentioned above, ORR can follow the 4-electron or 2-electron pathways, of which the 2-electron pathway is the focus of this work, because H2O2is the target product.The oxygen reduction currents are measured on the disk electrode(solid lines), while the H2O2oxidation currents are measured on the platinum ring electrode(dashed lines).The potential on the platinum ring (1.2 V versus RHE) ensures that only the oxidation of H2O2can be allowed rather than ORR.

    Figure 3.(a) XPS survey spectra of MWCNTs and PO-MWCNTs.High-resolution C 1s XPS spectra of (b) MWCNTs and (c) POMWCNTs.High-resolution O 1s XPS spectra of (d) MWCNTs and (e) PO-MWCNTs.

    The LSV curves demonstrate that the activity of MWCNTs is significantly improved after plasma oxidation(figure 4(a)).The potential corresponding to the current density of 1 mA cm?2is increased from 0.71 to 0.75 V versus RHE and the limiting current is raised obviously.As can be seen from figure 4(b),the selectivity is greatly enhanced after plasma oxidation.In the voltage interval of 0.5–0.75 V versus RHE, the selectivity is nearly doubled.Remarkably, at 0.7 V versus RHE,a high selectivity up to 95% is obtained by POMWCNTs.In addition,the Tafel slope is decreased from 59.8 to 38.2 mV dec?1, demonstrating the faster ORR kinetics(figure 4(c)).Cdlmeasurement demonstrates that the ECSA of PO-MWCNTs (3.07 mF cm?2) is about ten times that of MWCNTs(0.303 mF cm?2)(figures 4(d)and S4(a)and(b)),revealing that more active sites are exposed by POMWCNTs.The above results demonstrate that plasma activation can enhance both the activity and selectivity of MWCNTs for H2O2synthesis.For comparison,the traditional chemical oxidation method is also employed to oxidize MWCNTs (denoted as O-MWCNTs).As can be seen, the activity and selectivity of O-MWCNTs are inferior to those of PO-MWCNTs,further demonstrating that the plasma method is more effective (figures S5(a) and (b)).Apart from high activity and selectivity, long-term stability over 10 h is also displayed by PO-MWCNTs with no significant changes in the ring and disk current (figure 4(e)).In addition to excellent activity and selectivity in alkaline electrolyte, the POMWCNTs also exhibit high activity and selectivity under acidic (0.1 M HClO4) and neutral (0.1 M PBS) conditions(figures 5(a) and (b)).The selectivities of PO-MWCNTs under these two conditions are higher than 80%(figure 5(c)).

    Figure 4.(a)Polarization curves and (b)H2O2 selectivity of MWCNTs and PO-MWCNTs in 0.1 M KOH.(c)Tafel and(d) ECSA plots of MWCNTs and PO-MWCNTs in 0.1 M KOH.(e) Stability of PO-MWCNTs in 0.1 M KOH.

    To obtain the optimal plasma parameters, the oxidation time,plasma power,pressure,Ar/O2ratio,and electrocatalyst loading is optimized to 5 min, 250 W, 40 Pa, 1/9, and 0.2 mg cm?2, respectively (figures S5–S7(a), (b)).With the increase of plasma time(figure S5(c)–(h)),the oxygen content(table S1) increases and the H2O2production performance of MWCNTs is greatly improved, indicating that oxygen functional groups play an important role in improving the selectivity and activity of nanocarbons.Previous theoretical calculations have revealed that all the oxygen-containing functional groups may act as the active sites for H2O2production and–COOH and C–O–C groups may be more active[9].In our work, the selectivity of the plasma-oxidized MWCNTs is positively correlated to the ratio of C–O/C=O and surface defects, as confirmed by XPS analysis (tables S1 and S2).Therefore, the C–O site may be more active than C=O for 2e?ORR.

    3.3.In-situ Raman spectroelectrochemical analysis

    Figure 5.(a),(b)Polarization curves and(c)H2O2 selectivity of MWCNTs and PO-MWCNTs in(a)neutral and(b)acid electrolyte.(d),(e)In-situ Raman spectra with calculated Voigt deconvolutions of PO-MWCNTs at various potentials.ORR occurs below 0.84 V.(f), (g)FWHM and D/(G + D′ + D″) ratio of PO-MWCNTs as a function of applied potentials.0.1 M oxygen-saturated KOH is used as the electrolyte.

    As shown in the XPS results, the density of defects in nanocarbons after plasma activation is significantly increased.As such,it is worth exploring what role the defects generated by plasma play in H2O2production.The Raman spectra of nanocarbons are usually composed of five major Raman bands.In terms of the location of their existence, they are defined as D band at ~1350 cm?1, D″ band at ~1500 cm?1,G band at ~1580 cm?1, D′ band at ~1620 cm?1, and 2D band at ~2680 cm?1.However, the 2D band mainly reflects the graphene sheet stacks and layer number changes.Therefore,the influence of the 2D band can be excluded during the analysis.Additionally, the D″ band, which is ascribed to amorphous carbon,should be excluded,as amorphous carbon is unavoidable in commercial carbon materials.Therefore,the D and D′ bands corresponding to certain defects which may interact with the intermediates in the ORR process are investigated.The difference between the D and D′ bands is that the D band mostly represents the defects at the edge of the graphene layer, while the D′ band mainly reveals the defects on the sp2basal plane of graphene layer.For the convenience of analysis,the Raman spectra collected between 1.01 and 0.71 V versus RHE are selected as the investigated object(figures 5(d)–(f)).The onset potential of PO-MWCNTs for ORR is around 0.83 V versus RHE, indicating that the ORR cannot happen when the applied voltage is higher than 0.83 V versus RHE.Therefore, no obvious changes are observed on the D and D′ bands at the voltage above 0.83 V versus RHE(figures 5(d)and(e)).However,when the voltage is lower than 0.83 V versus RHE,the intensity of these peaks and full-width at half peak maximum (FWHM) change significantly (figures 5(f) and (g)).As can be observed from figure 5(f), the relative content of the D band (D/D′ + G + D) increases significantly, evidencing possible interaction between the ORR intermediate and the defects related to the D band(edge defect sites).However,the growth rate of the D band between 0.91 and 0.81 V versus RHE is lower than that between 0.81 and 0.71 V versus RHE, suggesting that there may be other active sites interacting with the intermediates to drive the ORR process at lower overpotential.The FWHM value of the D′ band increases obviously from 39.2 cm?1to 142.4 cm?1at the overpotential of 0.91–0.71 V versus RHE,while the FWHM value of the D band only exhibits a more notable increase below 0.81 V versus RHE.It can be concluded that with the increase of defect concentration both edge defect and sp2basal planar defect may be the active sites of 2e?ORR.However, the dominance is highly dependent on the applied voltages [13].

    3.4.Characterization and electrochemical performance of other ONCs

    Importantly, the plasma activation strategy is universal and can be extended to promote the activity and selectivity of other nanocarbons including SWCNT, G, and SP (figures 6 and S8–S16).The same plasma oxidation method can also maintain the morphology and phase of other nanocarbons and introduce oxygen functional groups (figures 6(a)–(f) and S8,S9,S11,S12,S14,S15).Similarly,the activity and selectivity of these nanocarbons can also be improved after plasma activation.At the same time,the ECSA and Tafel slopes also further reflect the improvement of exposed active sites and reaction kinetics(figures S10,S13,and S16).Remarkably,all the plasma-ONCs in this work exhibit comparable/better selectivity to/than the reported electrocatalysts for H2O2production (table S3) [9, 35–43].

    Figure 6.(a),(b)HRTEM images of SP before(a)and after(b)plasma oxidation.(c),(d)HRTEM images of G before(c)and after(d)plasma oxidation.(e), (f) HRTEM images of SWCNT before (e) and after (f) plasma oxidation.(g) Polarization curves and (h) H2O2 selectivity of SP, G, SWCNT and their plasma-oxidized derivatives in 0.1 M KOH.(i) Ring current (at 0.6 V) comparison of G, PO-G, SP, PO-SP,SWCNT, and PO-SWCNT.

    3.5.H2O2 production with large electrode and phenol degradation

    To verify the practical application of plasma-ONCs, POMWCNTs inked on CP is used as working electrode for demonstration (figures S17 and S18).In order to explore the appropriate voltage range for H2O2generation, the produced H2O2concentration at various voltages for 20 min is shown in figure S17(a).The H2O2yield and current efficiency under different voltages are also calculated (figure S17(b)).At the voltage of 0.5 V versus RHE, high production rate of 54.5 mmol l?1h?1and current efficiency of almost 100%are achieved (figure S17(b)), outperforming most reported electrocatalysts (table S4) [40, 43–46].Strikingly, after 5 h of operation, the electrode performance presents no obvious attenuation, demonstrating good durability (figure S17(c)).Due to the strong oxidation capability of H2O2, the electrochemically synthesized H2O2can be used for on-site degradation of organic pollutants.As such, phenol with a concentration of 50 mg l?1is employed as a model organic pollutant.Only in 3 h, the concentration of phenol can be reduced to 80% (figures S17(d) and S18), verifying the potential real application of plasma-ONCs.

    4.Conclusions

    In summary,we have developed a rapid and dry O2/Ar plasma activation method to realize the mild oxidation of various nanocarbons and replace the complex and long-term traditional chemical treatment methods.Due to the introduction of oxygencontaining functional groups and defects on the surface of nanocarbons during the plasma activation process,the selectivity and activity for H2O2generation by 2e?ORR have been significantly improved.The possible active sites are revealed byex situXPS andin situRaman tests.The production rate of H2O2reaches as high as 54.5 mmol l?1h?1and the on-site organic pollutant degradation is also demonstrated.This work provides a new strategy to construct ONCs for electrocatalytic H2O2production.Thein situRaman method can be also extended to characterize the active sites of carbon materials in other electrolysis process.

    Acknowledgments

    This work is supported by National Natural Science Foundation of China(No.12075002),the Outstanding Youth Fund of Anhui Province (No.2008085J21), the Anhui Provincial Supporting Program for Excellent Young Talents in Universities (No.gxyqZD2019005), and the Innovation and Entrepreneurship Project of Overseas Returnees in Anhui Province(No.2019LCX018).Hao Bin Wu acknowledges the funding support from the ‘Hundred Talents Program’ of Zhejiang University.The authors also acknowledge the help of Prof.Zhijuan Hai at Anhui University for HPLC measurement and Miss Ying Yang at Anhui University forin situRaman measurement.

    猜你喜歡
    長山王燕
    Optical simulation of CsPbI3/TOPCon tandem solar cells with advanced light management
    英語學(xué)習(xí)活動(dòng)觀在高中英語閱讀課堂的實(shí)踐與思考
    Clinical observation on acupoint injection for back pain in patients w ith primary osteoporosis
    駕駛黃昏的人
    詩林(2019年4期)2019-11-15 05:59:54
    智取“私了協(xié)議”
    Stratigraphy of late Quaternary deposits in the mid-western North Yellow Sea*
    醫(yī)學(xué)論文英文摘要中否定的對(duì)比研究
    卷宗(2016年5期)2016-08-02 02:50:18
    漫畫
    智珠
    基于原生植被的長山群島植被退化分析
    免费观看人在逋| 国产精品,欧美在线| 中国美女看黄片| 亚洲国产精品sss在线观看| 午夜免费成人在线视频| 夜夜看夜夜爽夜夜摸| 老司机在亚洲福利影院| 在线观看66精品国产| 黑人操中国人逼视频| 久久久精品大字幕| 夜夜躁狠狠躁天天躁| 淫妇啪啪啪对白视频| 精品一区二区三区av网在线观看| 国产精品1区2区在线观看.| 午夜免费成人在线视频| 日韩欧美免费精品| 99热6这里只有精品| 特大巨黑吊av在线直播| 淫妇啪啪啪对白视频| 久久国产精品影院| 国产欧美日韩一区二区三| 亚洲欧美日韩卡通动漫| 国产成人av教育| 99热这里只有是精品50| 999精品在线视频| 久久久成人免费电影| 亚洲av第一区精品v没综合| 免费在线观看成人毛片| 日韩大尺度精品在线看网址| 精品不卡国产一区二区三区| 五月伊人婷婷丁香| 91久久精品国产一区二区成人 | 三级毛片av免费| 色噜噜av男人的天堂激情| 色在线成人网| 国产一区在线观看成人免费| 国产男靠女视频免费网站| 身体一侧抽搐| 特级一级黄色大片| 亚洲av片天天在线观看| 欧美高清成人免费视频www| 欧美最黄视频在线播放免费| 可以在线观看毛片的网站| 99精品在免费线老司机午夜| 亚洲人成网站高清观看| 两个人看的免费小视频| 中文字幕久久专区| 国产伦精品一区二区三区四那| 国产精品99久久久久久久久| 色老头精品视频在线观看| 久久欧美精品欧美久久欧美| 久久久国产精品麻豆| 国产成人av教育| 真人做人爱边吃奶动态| 最好的美女福利视频网| 18禁美女被吸乳视频| 美女高潮的动态| 久久久久久久久中文| 一区二区三区高清视频在线| 19禁男女啪啪无遮挡网站| 亚洲成av人片免费观看| 美女被艹到高潮喷水动态| 午夜福利在线观看免费完整高清在 | 99久久无色码亚洲精品果冻| 熟女少妇亚洲综合色aaa.| 免费在线观看视频国产中文字幕亚洲| 亚洲国产精品999在线| 国产精品精品国产色婷婷| 非洲黑人性xxxx精品又粗又长| 亚洲av中文字字幕乱码综合| 老熟妇仑乱视频hdxx| 老汉色av国产亚洲站长工具| 国产欧美日韩一区二区精品| 日韩大尺度精品在线看网址| 两个人的视频大全免费| 久久久久久大精品| 成年免费大片在线观看| 日韩精品中文字幕看吧| 免费av毛片视频| a级毛片在线看网站| 精品99又大又爽又粗少妇毛片 | 精品欧美国产一区二区三| 真实男女啪啪啪动态图| 黄色 视频免费看| www.999成人在线观看| 欧美成狂野欧美在线观看| 两个人看的免费小视频| 国产乱人视频| 免费大片18禁| 熟女少妇亚洲综合色aaa.| 手机成人av网站| 久久精品夜夜夜夜夜久久蜜豆| 亚洲七黄色美女视频| 久久久久国产一级毛片高清牌| 欧美绝顶高潮抽搐喷水| 美女午夜性视频免费| 久久久久久久精品吃奶| 色尼玛亚洲综合影院| 亚洲欧美精品综合一区二区三区| 国产精品久久久久久精品电影| 国产精品久久视频播放| 精品一区二区三区av网在线观看| 国内少妇人妻偷人精品xxx网站 | 免费一级毛片在线播放高清视频| 波多野结衣高清无吗| 嫩草影院精品99| xxxwww97欧美| 网址你懂的国产日韩在线| 久久久成人免费电影| 午夜免费激情av| 真实男女啪啪啪动态图| 午夜免费成人在线视频| 亚洲精品中文字幕一二三四区| 色综合欧美亚洲国产小说| 婷婷亚洲欧美| 色吧在线观看| 99久久国产精品久久久| 曰老女人黄片| 日本精品一区二区三区蜜桃| 在线观看免费午夜福利视频| 亚洲av成人一区二区三| 午夜免费成人在线视频| 亚洲aⅴ乱码一区二区在线播放| 欧美日韩亚洲国产一区二区在线观看| 日本成人三级电影网站| 成年女人永久免费观看视频| 在线看三级毛片| 一本综合久久免费| 少妇丰满av| 在线观看午夜福利视频| 久久久久久久久中文| 日韩欧美精品v在线| 亚洲av第一区精品v没综合| 真人一进一出gif抽搐免费| 99在线视频只有这里精品首页| 巨乳人妻的诱惑在线观看| 一个人免费在线观看的高清视频| 19禁男女啪啪无遮挡网站| 99久久国产精品久久久| 色老头精品视频在线观看| 久久中文看片网| 男人和女人高潮做爰伦理| xxx96com| 午夜福利在线在线| 狠狠狠狠99中文字幕| 国产av一区在线观看免费| 日本黄色视频三级网站网址| 亚洲国产欧洲综合997久久,| 亚洲成av人片免费观看| 欧美绝顶高潮抽搐喷水| 欧美黑人欧美精品刺激| 国产97色在线日韩免费| 国产精品国产高清国产av| 国产精品久久久人人做人人爽| 男人的好看免费观看在线视频| 中文字幕久久专区| 男女午夜视频在线观看| 国产亚洲欧美在线一区二区| 亚洲黑人精品在线| 在线观看午夜福利视频| 国产精品乱码一区二三区的特点| 变态另类成人亚洲欧美熟女| 99国产极品粉嫩在线观看| 国产精品一及| 国产亚洲精品久久久com| 久久国产精品人妻蜜桃| 国产精品久久久久久久电影 | 亚洲欧美日韩东京热| 成年女人看的毛片在线观看| 色综合亚洲欧美另类图片| 欧美激情在线99| 桃红色精品国产亚洲av| 天堂影院成人在线观看| 免费无遮挡裸体视频| 人人妻人人澡欧美一区二区| www.999成人在线观看| 性色avwww在线观看| 美女高潮的动态| 男女那种视频在线观看| 天堂影院成人在线观看| 9191精品国产免费久久| 久久精品aⅴ一区二区三区四区| 两性夫妻黄色片| 午夜日韩欧美国产| 免费av毛片视频| 精品熟女少妇八av免费久了| 免费看光身美女| 精品乱码久久久久久99久播| 两人在一起打扑克的视频| 国产精品一区二区三区四区免费观看 | 日本黄色视频三级网站网址| 国产又色又爽无遮挡免费看| a级毛片a级免费在线| 999久久久精品免费观看国产| 人妻丰满熟妇av一区二区三区| 国产精品1区2区在线观看.| 久久精品影院6| 国产亚洲欧美98| 婷婷精品国产亚洲av| 国产欧美日韩精品亚洲av| 久久久久性生活片| 夜夜看夜夜爽夜夜摸| 最近视频中文字幕2019在线8| 蜜桃久久精品国产亚洲av| 两个人的视频大全免费| 国产精品久久视频播放| 久久草成人影院| 小蜜桃在线观看免费完整版高清| av天堂中文字幕网| 又粗又爽又猛毛片免费看| 国产 一区 欧美 日韩| xxx96com| 婷婷亚洲欧美| 亚洲真实伦在线观看| 丰满的人妻完整版| 免费观看的影片在线观看| 真实男女啪啪啪动态图| 午夜福利在线观看免费完整高清在 | 我的老师免费观看完整版| 99久久精品热视频| 亚洲精品中文字幕一二三四区| 成人三级做爰电影| 手机成人av网站| 热99在线观看视频| 中亚洲国语对白在线视频| 国产久久久一区二区三区| 欧美精品啪啪一区二区三区| 午夜影院日韩av| 他把我摸到了高潮在线观看| 成人午夜高清在线视频| 老司机午夜十八禁免费视频| 99久久99久久久精品蜜桃| 亚洲美女黄片视频| 久久亚洲真实| 亚洲第一电影网av| 精品一区二区三区视频在线观看免费| 国产欧美日韩一区二区三| 香蕉国产在线看| 精品国产乱子伦一区二区三区| 成人av一区二区三区在线看| 亚洲熟妇熟女久久| 亚洲国产色片| 国产激情欧美一区二区| 黑人巨大精品欧美一区二区mp4| 一a级毛片在线观看| 久久亚洲真实| 在线播放国产精品三级| 亚洲av五月六月丁香网| 亚洲自拍偷在线| 91在线精品国自产拍蜜月 | 免费在线观看亚洲国产| 真人做人爱边吃奶动态| 色哟哟哟哟哟哟| 国产欧美日韩精品亚洲av| а√天堂www在线а√下载| 国产久久久一区二区三区| 欧美日韩国产亚洲二区| 97超视频在线观看视频| 国产久久久一区二区三区| 久久久久亚洲av毛片大全| 99riav亚洲国产免费| 一本综合久久免费| 亚洲无线在线观看| 一级毛片女人18水好多| 男女下面进入的视频免费午夜| 国产麻豆成人av免费视频| 在线观看免费视频日本深夜| 男女之事视频高清在线观看| 成人精品一区二区免费| 国产精品久久久久久精品电影| 亚洲成a人片在线一区二区| 欧美三级亚洲精品| av视频在线观看入口| 波多野结衣巨乳人妻| 九九久久精品国产亚洲av麻豆 | 亚洲欧美精品综合一区二区三区| 在线观看美女被高潮喷水网站 | 18禁黄网站禁片午夜丰满| 又紧又爽又黄一区二区| 欧美激情在线99| 在线国产一区二区在线| 国产高清视频在线观看网站| 色尼玛亚洲综合影院| 久久国产乱子伦精品免费另类| 麻豆成人午夜福利视频| 九九在线视频观看精品| 亚洲aⅴ乱码一区二区在线播放| 色综合婷婷激情| 国产成年人精品一区二区| 99热这里只有精品一区 | 久久九九热精品免费| 又黄又爽又免费观看的视频| 噜噜噜噜噜久久久久久91| 亚洲在线自拍视频| 欧美在线黄色| 久久这里只有精品19| 欧美三级亚洲精品| 俺也久久电影网| 亚洲欧美日韩东京热| a级毛片a级免费在线| 淫妇啪啪啪对白视频| 热99在线观看视频| 欧美日韩亚洲国产一区二区在线观看| 五月伊人婷婷丁香| 国产亚洲欧美98| 国产精品综合久久久久久久免费| 两性夫妻黄色片| 在线a可以看的网站| 两个人视频免费观看高清| 91九色精品人成在线观看| 亚洲精品粉嫩美女一区| 啦啦啦韩国在线观看视频| 在线观看一区二区三区| 一本久久中文字幕| 国产精品野战在线观看| 国产野战对白在线观看| cao死你这个sao货| 中文字幕最新亚洲高清| 18禁观看日本| 久久久久久大精品| 后天国语完整版免费观看| 夜夜躁狠狠躁天天躁| 九九在线视频观看精品| 国产高清视频在线观看网站| 一进一出抽搐动态| 精品一区二区三区av网在线观看| 91字幕亚洲| 最近视频中文字幕2019在线8| 夜夜夜夜夜久久久久| 国产乱人伦免费视频| 一进一出好大好爽视频| 在线观看日韩欧美| 99久久精品一区二区三区| 最好的美女福利视频网| 高清毛片免费观看视频网站| 麻豆一二三区av精品| 99re在线观看精品视频| 国产亚洲精品久久久com| 国产欧美日韩精品一区二区| 999精品在线视频| 久久久久久久精品吃奶| 久久久精品大字幕| 久久久国产欧美日韩av| 免费搜索国产男女视频| 精品久久久久久久人妻蜜臀av| 村上凉子中文字幕在线| 久久久久国内视频| 亚洲欧美日韩高清在线视频| 悠悠久久av| 日韩欧美免费精品| xxx96com| 国产野战对白在线观看| 嫩草影院入口| 看黄色毛片网站| 午夜福利欧美成人| 欧美日韩一级在线毛片| 久久久久国产精品人妻aⅴ院| 国产一区在线观看成人免费| 麻豆av在线久日| 网址你懂的国产日韩在线| 精品国产乱码久久久久久男人| 亚洲av中文字字幕乱码综合| 香蕉av资源在线| 成年免费大片在线观看| 色综合婷婷激情| 天堂√8在线中文| 亚洲在线自拍视频| 久久香蕉国产精品| 久久精品国产综合久久久| 90打野战视频偷拍视频| 久久精品国产综合久久久| 听说在线观看完整版免费高清| 国产人伦9x9x在线观看| 久久这里只有精品中国| 久久国产精品人妻蜜桃| 亚洲精品美女久久久久99蜜臀| 色综合欧美亚洲国产小说| 日韩 欧美 亚洲 中文字幕| 亚洲人与动物交配视频| 午夜影院日韩av| 男插女下体视频免费在线播放| 日韩中文字幕欧美一区二区| 国产黄色小视频在线观看| 看黄色毛片网站| 九九热线精品视视频播放| 真实男女啪啪啪动态图| 亚洲国产欧洲综合997久久,| 国内久久婷婷六月综合欲色啪| 久久久成人免费电影| 国内精品久久久久久久电影| 久久久国产欧美日韩av| x7x7x7水蜜桃| 嫩草影视91久久| 欧美色欧美亚洲另类二区| 亚洲中文字幕一区二区三区有码在线看 | 亚洲,欧美精品.| 男女之事视频高清在线观看| 久久久久性生活片| 成人亚洲精品av一区二区| 两性夫妻黄色片| 97超级碰碰碰精品色视频在线观看| 久久久久久久久中文| АⅤ资源中文在线天堂| 成人av在线播放网站| 午夜日韩欧美国产| 国产不卡一卡二| 国产欧美日韩一区二区精品| 国内精品一区二区在线观看| 色在线成人网| 亚洲黑人精品在线| 国产伦在线观看视频一区| 1024香蕉在线观看| 亚洲精品456在线播放app | 老司机在亚洲福利影院| 丝袜人妻中文字幕| 老汉色∧v一级毛片| 天堂影院成人在线观看| 91九色精品人成在线观看| 免费看美女性在线毛片视频| 亚洲av电影不卡..在线观看| 色吧在线观看| 亚洲av中文字字幕乱码综合| 99国产综合亚洲精品| 成人高潮视频无遮挡免费网站| 亚洲国产欧美一区二区综合| 不卡一级毛片| 国产日本99.免费观看| 午夜影院日韩av| 午夜福利成人在线免费观看| 村上凉子中文字幕在线| 亚洲精品乱码久久久v下载方式 | 精品久久久久久,| 欧美一级毛片孕妇| 黄色女人牲交| 亚洲精品456在线播放app | 国产日本99.免费观看| 三级国产精品欧美在线观看 | 久久久久国产精品人妻aⅴ院| 国产精品久久久久久人妻精品电影| 小蜜桃在线观看免费完整版高清| 国产精品免费一区二区三区在线| 亚洲 欧美一区二区三区| 国产又色又爽无遮挡免费看| 两个人看的免费小视频| 女同久久另类99精品国产91| 午夜亚洲福利在线播放| 美女被艹到高潮喷水动态| 久久精品人妻少妇| 两人在一起打扑克的视频| 99re在线观看精品视频| 黄色丝袜av网址大全| 午夜a级毛片| 国产高清三级在线| 中文字幕熟女人妻在线| 一级毛片女人18水好多| 日韩欧美免费精品| 国产午夜精品论理片| 国产精品av视频在线免费观看| av女优亚洲男人天堂 | x7x7x7水蜜桃| 国产黄片美女视频| 久久精品91蜜桃| 欧美午夜高清在线| 69av精品久久久久久| 日本撒尿小便嘘嘘汇集6| 黄色日韩在线| 九九热线精品视视频播放| 亚洲成a人片在线一区二区| 国产伦一二天堂av在线观看| www.自偷自拍.com| 国产精品日韩av在线免费观看| 久久久久国产一级毛片高清牌| 精品国产超薄肉色丝袜足j| 男女下面进入的视频免费午夜| www.www免费av| svipshipincom国产片| 久久国产精品影院| 免费看美女性在线毛片视频| 级片在线观看| 日韩精品青青久久久久久| 亚洲欧美一区二区三区黑人| 欧美一级a爱片免费观看看| 又紧又爽又黄一区二区| 久久久久久久久久黄片| 久久九九热精品免费| 国产av麻豆久久久久久久| 亚洲美女视频黄频| 久久草成人影院| 亚洲熟女毛片儿| 91在线精品国自产拍蜜月 | 国产高清激情床上av| 嫁个100分男人电影在线观看| 怎么达到女性高潮| 午夜福利欧美成人| 国产真实乱freesex| 又黄又粗又硬又大视频| 男人舔女人的私密视频| 嫩草影院精品99| 亚洲精品乱码久久久v下载方式 | 久久亚洲真实| 精品一区二区三区四区五区乱码| 欧美日本视频| 美女大奶头视频| 午夜福利在线观看吧| 91在线观看av| 90打野战视频偷拍视频| 好男人在线观看高清免费视频| 99热这里只有是精品50| 精品电影一区二区在线| 母亲3免费完整高清在线观看| 亚洲国产日韩欧美精品在线观看 | 后天国语完整版免费观看| 日本在线视频免费播放| 欧美乱码精品一区二区三区| 在线视频色国产色| 亚洲七黄色美女视频| 在线观看午夜福利视频| 国产av一区在线观看免费| 婷婷精品国产亚洲av在线| 18禁国产床啪视频网站| 91麻豆精品激情在线观看国产| 国产精品一及| 亚洲国产欧美人成| 嫩草影院入口| 欧美中文综合在线视频| 99国产极品粉嫩在线观看| 日日干狠狠操夜夜爽| 99riav亚洲国产免费| 黄色片一级片一级黄色片| 国产伦人伦偷精品视频| 国产成+人综合+亚洲专区| 啦啦啦免费观看视频1| 99久久综合精品五月天人人| 色老头精品视频在线观看| 变态另类成人亚洲欧美熟女| 男女做爰动态图高潮gif福利片| 丝袜人妻中文字幕| 看片在线看免费视频| 日韩欧美国产一区二区入口| 丰满人妻一区二区三区视频av | 免费观看人在逋| 久久国产精品人妻蜜桃| 1024香蕉在线观看| 欧美成人一区二区免费高清观看 | 亚洲乱码一区二区免费版| 热99在线观看视频| 久久精品夜夜夜夜夜久久蜜豆| 亚洲无线在线观看| 别揉我奶头~嗯~啊~动态视频| 中文字幕精品亚洲无线码一区| 日本成人三级电影网站| 国产精品,欧美在线| 免费看十八禁软件| 最近最新中文字幕大全电影3| 身体一侧抽搐| 国产av不卡久久| 搡老岳熟女国产| 欧美日韩乱码在线| 天堂av国产一区二区熟女人妻| 久久天堂一区二区三区四区| 国产成人一区二区三区免费视频网站| 欧美乱色亚洲激情| 波多野结衣高清作品| 一进一出抽搐动态| 一区二区三区国产精品乱码| 99国产精品一区二区蜜桃av| 久久草成人影院| 亚洲最大成人中文| 欧美在线黄色| 日韩有码中文字幕| 在线十欧美十亚洲十日本专区| 99re在线观看精品视频| 国产精品精品国产色婷婷| 成人三级做爰电影| 国产亚洲精品av在线| 一级a爱片免费观看的视频| 亚洲五月天丁香| 国产高清videossex| 婷婷精品国产亚洲av| 亚洲av美国av| aaaaa片日本免费| 亚洲欧美日韩高清在线视频| 亚洲美女视频黄频| 给我免费播放毛片高清在线观看| 中文字幕av在线有码专区| 91av网一区二区| 国产成人精品久久二区二区91| av黄色大香蕉| 精品电影一区二区在线| 国产亚洲精品久久久com| 亚洲av片天天在线观看| 精品国产美女av久久久久小说| 免费看十八禁软件| 精品国产乱子伦一区二区三区| 亚洲av成人不卡在线观看播放网| 少妇裸体淫交视频免费看高清| 亚洲精品乱码久久久v下载方式 | 国产精品美女特级片免费视频播放器 | 成人高潮视频无遮挡免费网站| 色综合亚洲欧美另类图片| 热99re8久久精品国产| 国产毛片a区久久久久| 美女大奶头视频| 首页视频小说图片口味搜索| 一级黄色大片毛片| 中文字幕熟女人妻在线| 日韩欧美国产在线观看| 宅男免费午夜| 亚洲欧美激情综合另类| 亚洲专区国产一区二区| 色综合站精品国产| 成人亚洲精品av一区二区| 午夜日韩欧美国产| 搡老岳熟女国产| 久久午夜亚洲精品久久|