    Optimal Process Parameters of Preparing MoS2 Films by RF Magnetron Sputtering

    2023-03-14 13:56:14,,,,,,
    人工晶體學(xué)報(bào) 2023年2期

    , , , , , ,

    (School of Sciences, Henan University of Technology, Zhengzhou 450001, China)

    Abstract:MoS2 films were prepared on quartz substrate by radio frequency (RF) magnetron sputtering. The effect of sputtering time, sputtering temperature, argon flow rate and sputtering power on the structure of MoS2 films was studied by orthogonal test method. The crystallinity, thickness and surface morphology of MoS2 films were analyzed by XRD, Raman, XPS, EDS and SEM, the optimal process parameters for preparing MoS2 films were obtained. It is found that the crystallinity of the sample is poor at higher or lower sputtering temperature, and the XRD diffraction peak of the sample is not obvious at lower sputtering temperature. When the temperature is 250 ℃, the sample has more XRD diffraction peaks and better crystallinity. According to the orthogonal test, sputtering temperature plays a crucial role in the crystallization of MoS2, followed by argon flow rate. When sputtering temperature is 250 ℃, argon flow rate is 6 mL/min, sputtering time is 30 min, and sputtering power is 300 W or 400 W, the crystallinity of MoS2 film is better. The film prepared under this condition is thicker, but it points out the direction for future experiments. In the following experiments, sputtering temperature, sputtering power and argon flow rate can be kept unchanged. By shortening the time, films with a thickness of 58.9 nm have been successfully prepared.

    Key words:MoS2 films; RF magnetron sputtering; two-dimensional material; orthogonal test method; process parameter

    0 Introduction

    In recent years, two-dimensional (2D) materials, for instance, graphene and transition metal dichalcogenides (TMDCs) have attracted enormous research interests[1-4]. Molybdenum disulfide (MoS2), a unique transition-metal disulfide that is abundant in nature[5-7], is supposed to be a two-dimensional material because its thickness can be adjusted from bulk to monolayer[8-11]. MoS2has been broadly used in memory devices, sensors, optoelectronic devices, and biomedical fields due to its excellent physical and chemical properties[12-14]. The main techniques for preparing single-layer or few layer MoS2film materials are: micromechanical exfoliation, solution exfoliation, chemical vapor deposition (CVD)[15], wet chemical method, hydrothermal synthesis, and physical vapor deposition (PVD)[16]. However, the properties of MoS2prepared by different preparation method are significantly different. CVD method has the advantages of fast film forming speed and large area. Still, this method has defects such as high reaction temperature, environmental pollution by residues, and equipment corrosion. Due to the fast film forming speed, and uniform particle size, magnetron sputtering technology can be used to prepare MoS2films with various properties, so the method commonly used in industry[17]. But the crystal structure changes caused by magnetron sputtering process parameters are not clear and there are few literature reports. In terms of substrate, silicon substrates are used more than quartz substrates in most experiments[18]. MoS2films prepared with silicon substrates can be used as field effect transistor and heterojunction, while MoS2films prepared with quartz substrates can be used as photodetector. Therefore, further investigation of preparation technology and performance of MoS2films is indispensable.

    In the literature reports, most of the MoS2films were prepared on silicon substrate by variable-controlling method[19]. However, it is difficult to get optimum process parameters using the variable-controlling method because of the complex preparation conditions. In this paper, optimum process parameters for preparing MoS2films from orthogonal tests were obtained and MoS2films on quartz substrates by radio frequency (RF) magnetron sputtering were successfully prepared.

    1 Experimental section

    1.1 Preparation of MoS2 films

    MoS2films were deposited on quartz substrates by RF magnetron sputtering, argon (Ar, purity 99.99%) was selected as sputtering gas. High-purity MoS2(MoS2, purity 99.99%) was selected as the target material. Quartz substrates were cleaned with absolute ethanol and deionized water. The working pressure is 1.0×10-3Pa. It is found that sputtering time, substrate temperature, argon flow rate, and sputtering power have a significant influence on the experimental results, so these four factors are selected as experimental conditions. Table 1 is the factor level table of the orthogonal experiment design. Sixteen samples were prepared for the experiment. Four factors (A, B, C, and D) represent sputtering time, sputtering temperature, argon flow rate, and sputtering power, respectively. The orthogonal test scheme was obtained in Table 2[20].

    Table 1 Orthogonal test table with 4 factors and 4 levels

    Table 2 Orthogonal test table of 16 samples combined by 4 factors and 4 levels

    1.2 Characterization of MoS2 films

    The microstructures of the deposited films were characterized by 8D Discover X-ray diffraction (XRD) analysis and Renishaw inVia Raman at an excitation light of 532 nm. The chemical composition and bonding of the films were characterized by Multifunctional X-ray photoelectron spectroscope (XPS; Axis ultra dld, Japan). The thickness and morphology of the films were determined by scanning electron microscopy (SEM; S-4800, Hitachi, Tokyo, Japan). The elemental composition and atomic percentage of the films were measured using an X-ray energy spectrometer (EDS; S-4800, Hitachi, Tokyo, Japan).

    2 Results and discussion

    2.1 XRD patterns

    Fig.1 displays different diffraction peaks of 16 samples. The ICSD indicates that the diffraction peaks are 13.5°, 28.1°, 31.9°, 33.5°, and 59.0° correspond to (002), (021), (100), (101), and (110) crystal planes of MoS2. Sharp diffraction peaks indicate prominent MoS2crystals on the surface of the quartz substrate[21]. In Fig.1(a), the 0# is the spectrum of a quartz substrate. All samples have the (101) crystal plane diffraction peak except for samples 1# and 14#, which means that most samples grow preferentially on the (101) crystal plane, followed by (100) crystal plane. In Fig.1(d), samples 15# and 16# have high diffraction peaks at 33.5°.

    Fig. 1 XRD patterns of quartz substrate and sixteen samples

    2.2 Raman spectra

    Fig.2 Raman spectra of quartz substrate and sixteen samples at an excitation light of 532 nm

    Fig.3 Data analysis diagram of Raman and XRD

    2.3 Effect of process parameters on the structure of MoS2 film

    The height and width of XRD peak represent the grain size and crystallinity. The narrower and higher the peak, the larger the grain size, the more perfect the crystallization. On the contrary, the wider and lower the peak, the smaller the grain size, poor crystallization results in relatively small grains. The more the number of diffraction peaks, the better the crystallinity. To study the effect of process parameters on the structure of MoS2films, Table 3 gives the relationship between orthogonal design parameters and the number of XRD peaks. Taking the number of XRD diffraction peaks as the investigation index to investigate the effect of process parameters on the structure of MoS2film, as shown in Table 4.

    Table 3 Relationship between orthogonal design parameters and the number of XRD peaks

    Table 4 Effect of process parameters on the structure of MoS2 film

    In Table 4, it is shown that sputtering temperature plays the essential role in the crystallization effect of MoS2, followed by argon flow rate. And the best combination is A4B3C2D3, or A4B3C2D4(15#),i.e., sputtering temperature is 250 ℃, argon gas flow rate is 6 mL/min, sputtering time is 30 min, and sputtering power is 300 W or 400 W.

    As shown in Table 2 and Table 3, when sputtering temperature is 250 ℃, the crystallinity of samples 3#, 7#, and 11# is relatively good and has two diffraction peaks. There are four diffraction peaks in the spectrum of sample 15# with optimally process parameters. When sputtering temperature is very low, samples 1#, 5#, 9#, and 13# have only one diffraction peak and the intensity is very low. It shows that the lower sputtering temperature is not good for the growth of MoS2films.

    Although sputtering temperature of sample 4# has reached the maximum value, only the (101) crystal plane is crystallized due to the reduction of the mean free path of ions bombarding the substrate caused by the higher argon flow rate, which influences the etching of the film surface and film crystallization. So, argon flow rate is another indispensable influencing factor. When argon flow rate is too large, the number of diffraction peaks of XRD is minimal.

    The third influence is factor sputtering time, which influence the number of layers of MoS2. When sputtering time increases, number of layers increases, which results in the appearance of the (002) and (110) crystal planes of sample 15# and 16#, as shown in Fig.1. It can be seen from the samples 1#, 7#, 12# and 14# that it is not conducive to the growth of the (101) crystal plane when the sputtering power is lower.

    2.4 XPS

    Through the above analysis, samples 1# and 5# with poor crystallization and samples 10# and 16# with better crystallization were selected for further characterization and analysis. Fig.4(a) exhibits the XPS, which verifies the existence of S and Mo elements[26]. As shown in the figure, 531.3eV corresponds to the XPS peak of O 1s and is attributed to the oxidation of the samples before testing. The C 1s peak at 283.8 eV is associated with adventitious carbon in XPS test. The peak positions of S 2p and Mo 3d of sample 1# are shifted relative to other samples. It suggests that there are Mo and S atoms in sample 1# but no MoS2crystals, which is consistent with the results of XRD.

    Fig.4 XPS spectra of four samples: (a) survey scan; (b) Mo 3d elemental scan; (c) S 2p elemental scan

    Fig. 4(b) shows four peaks appearing at 226.5, 229.3, 232.4, and 235.1 eV in the Mo 3d spectrum[27]; these peaks correspond to S 2s, MoS2, and MoO3, respectively[28]. It can be seen that Mo 3d exhibits two spin-orbit characteristic peaks split into 3.10 eV. The high-intensity peaks of Mo 3d3/2at 229.3 eV and Mo 3d5/2at 232.4 eV are consistent with the literature[4,29]. Mo 3d3/2is typical of Mo4+in the MoS2lattice[30]. Furthermore, the peak at 235.1 eV identifies with the Mo—O bond[31], which demonstrates that the film surface is partly oxidized, and the S 2s peak occurs at 226.5 eV, indicating the formation of sulfide.

    Fig.4(c) indicates the two spin-orbit characteristic peaks of the S 2p spectrum at 163.2 eV (S 2p1/2), and 162 eV (S 2p3/2) split into 1.16 eV are consistent with the literature[24,29], reflecting the S2-state in the MoS2lattice. It can be seen from the Fig.4 that sample 16# has a high peak strength, which is due to its good crystallization effect, that is consistent with XRD and Raman results.

    2.5 EDS

    Fig.5 gives the EDS and atomic percentage of the samples 5#, 10#, 15#, and 16#. Table 5 details the atomic percentages of the four elements in four samples. The EDS information indicates that the ratio of Mo to S atoms in samples 15# and 16# is approximately 1∶2[32]. This phenomenon indicates that MoS2exists in the films (and a small number of defects is also present)[33], which is identified with the results of XRD. It shows that with the increase in sputtering temperature and sputtering time, the crystallization of MoS2film is better. Moreover, EDS found the existence of O and Si atoms, the presence of O element is due to the oxidation of the sample before testing, and the presence of Si element is due to the quartz substrates.

    Table 5 Atomic percentages of O, Si, S, and Mo for four samples /%

    Fig.5 EDS (a) and atomic percentage (b) of the samples 5#, 10#, 15# and 16#

    2.6 SEM

    SEM image of samples 5#, 10#, 15#, and 16# are given in Fig. 6. It is observed that the four samples have dense surfaces and the particle size of the last three samples is uniform, but their process parameters are different[34]. Temperature is the most important factor affecting MoS2crystallization, followed by argon flow rate. Fig. 6 shows that the MoS2film prepared at the sputtering temperature of 200 ℃ is thicker. This result is consistent with the Raman test. Although the sputtering time of samples 15# and 16# is longer than that of sample 10#, their thickness is thinner than that of sample 10#. This is because sample 15# has the most suitable temperature and sample 16# has a low argon flow. Fig. 6 (c) shows the optimal process parameters of sample 15#.

    Fig.6 SEM images and cross-section images of samples

    16 samples were prepared by magnetron sputtering, and it can be confirmed that temperature and argon flow rate have great influence. However, the prepared samples are all micron films instead of 2D materials. Next, by keeping sputtering temperature, argon flow rate and sputtering power constant and shortening sputtering time, thinner films can be prepared. Sample 17# with less time was prepared. The optimized process parameters were used for sample 17, but time was reduced, i.e.. The sputtering temperature, argon flow rate, and sputtering power were set to 250 ℃, 6 mL/min, and 300 W, respectively, sputtering time was reduced from 30 min to 1 min. Fig.7 shows the morphology and cross-section images of sample 17#. It can be seen from Fig. 7 that the surface of 17# sample is dense and thickness is 58.9 nm. It shows that the result of orthogonal test is feasible.

    Fig.7 SEM image and cross-section image of samples 17#

    3 Conclusion

    MoS2films were prepared on quartz substrates by RF magnetron sputtering. The sputtering temperature plays an essential role in the crystallization effect of MoS2, followed by argon flow rate. Prepared MoS2films are in better crystallization when sputtering temperature is 250 ℃, argon flow rate is 6 mL/min, sputtering time is 30 min, and sputtering power is 300 or 400 W. As can be seen from XRD, MoS2film grows preferentially at (101) orientation, followed by the (100) crystal plane. XPS tests show that there are typical Mo4+in the prepared films, which prove the existence of MoS2. It can be seen from SEM with the increase in sputtering time, the thickest MoS2films were prepared under 200 ℃. The film prepared under orthogonal test conditions is thicker, by keeping the sputtering temperature, argon flow rate and sputtering power constant and shortening the sputtering time, 2D films were prepared.

    亚洲,欧美,日韩| h日本视频在线播放| 国产黄片美女视频| 久久久精品免费免费高清| 成年人午夜在线观看视频 | 精品久久久久久久久久久久久| 99热这里只有是精品在线观看| 在现免费观看毛片| 国产精品熟女久久久久浪| 国产亚洲最大av| 搡老妇女老女人老熟妇| 卡戴珊不雅视频在线播放| 免费观看的影片在线观看| 人妻少妇偷人精品九色| 一级黄片播放器| 午夜精品国产一区二区电影 | 在线免费观看不下载黄p国产| 国产精品伦人一区二区| 老师上课跳d突然被开到最大视频| 欧美一级a爱片免费观看看| 亚洲不卡免费看| 日韩欧美一区视频在线观看 | 亚洲国产欧美在线一区| 国产精品精品国产色婷婷| 免费看美女性在线毛片视频| 三级毛片av免费| 啦啦啦韩国在线观看视频| 夫妻性生交免费视频一级片| 日本wwww免费看| 91在线精品国自产拍蜜月| 久久久久久久午夜电影| 免费黄色在线免费观看| 人人妻人人看人人澡| 高清午夜精品一区二区三区| 91午夜精品亚洲一区二区三区| 久久热精品热| 九九在线视频观看精品| 成人毛片a级毛片在线播放| 亚洲欧美日韩无卡精品| 爱豆传媒免费全集在线观看| 久久久精品94久久精品| 女人十人毛片免费观看3o分钟| 男人和女人高潮做爰伦理| 韩国av在线不卡| 中文字幕亚洲精品专区| 18禁动态无遮挡网站| 亚洲在线观看片| 欧美+日韩+精品| 亚洲色图av天堂| 午夜福利高清视频| 国产黄色免费在线视频| 最新中文字幕久久久久| 777米奇影视久久| 日本免费a在线| 日本av手机在线免费观看| 欧美精品国产亚洲| 午夜亚洲福利在线播放| 2021少妇久久久久久久久久久| 韩国av在线不卡| 91精品一卡2卡3卡4卡| 亚洲欧美精品自产自拍| 国产一区二区在线观看日韩| 欧美zozozo另类| 亚洲国产最新在线播放| 女人被狂操c到高潮| 日韩在线高清观看一区二区三区| av播播在线观看一区| 淫秽高清视频在线观看| 国产精品久久久久久久久免| 国产伦在线观看视频一区| 亚洲精品aⅴ在线观看| 久久人人爽人人爽人人片va| 国产人妻一区二区三区在| 久久精品熟女亚洲av麻豆精品 | 亚洲精品影视一区二区三区av| 成人亚洲精品av一区二区| 免费少妇av软件| 麻豆成人午夜福利视频| 日本一本二区三区精品| 22中文网久久字幕| 久久综合国产亚洲精品| 国产v大片淫在线免费观看| 小蜜桃在线观看免费完整版高清| av播播在线观看一区| 嫩草影院新地址| 亚洲精品456在线播放app| 欧美激情久久久久久爽电影| 黄片wwwwww| 两个人视频免费观看高清| 99久国产av精品| 亚洲,欧美,日韩| av国产免费在线观看| 最近中文字幕高清免费大全6| 如何舔出高潮| 成年女人看的毛片在线观看| a级毛片免费高清观看在线播放| 在线 av 中文字幕| 免费看不卡的av| 只有这里有精品99| 日韩av在线大香蕉| 国产 一区 欧美 日韩| 成年女人看的毛片在线观看| 狂野欧美激情性xxxx在线观看| 国产精品国产三级国产专区5o| 色5月婷婷丁香| 精品人妻视频免费看| 国产高清有码在线观看视频| 亚洲图色成人| 九九在线视频观看精品| 91久久精品国产一区二区三区| 人妻系列 视频| 国产伦在线观看视频一区| 国产一区二区在线观看日韩| 亚洲四区av| 精品一区二区三卡| 欧美xxⅹ黑人| 亚洲av.av天堂| 乱人视频在线观看| 国产精品久久久久久精品电影小说 | 国产精品人妻久久久久久| 国产午夜精品一二区理论片| 精品酒店卫生间| 国产精品一区二区三区四区免费观看| 国产老妇女一区| 日韩人妻高清精品专区| 日韩中字成人| 久久久久久久午夜电影| 在现免费观看毛片| videos熟女内射| 岛国毛片在线播放| 免费观看a级毛片全部| 精品久久久久久久人妻蜜臀av| 国内精品宾馆在线| 欧美zozozo另类| 亚洲精品日本国产第一区| 久久99热6这里只有精品| 国产日韩欧美在线精品| 国产白丝娇喘喷水9色精品| 欧美+日韩+精品| 亚洲精品乱码久久久久久按摩| 我的女老师完整版在线观看| 亚洲av一区综合| 18禁裸乳无遮挡免费网站照片| 久久99热6这里只有精品| 日韩在线高清观看一区二区三区| 三级国产精品欧美在线观看| 久久精品国产自在天天线| 久久久精品94久久精品| 老司机影院成人| 亚洲人成网站高清观看| 十八禁网站网址无遮挡 | 三级国产精品片| av线在线观看网站| 亚洲,欧美,日韩| 国产乱人视频| 亚洲一级一片aⅴ在线观看| 91久久精品国产一区二区成人| 久久精品国产亚洲网站| 秋霞伦理黄片| 肉色欧美久久久久久久蜜桃 | 亚洲精品乱久久久久久| 男女视频在线观看网站免费| 欧美日韩亚洲高清精品| 18+在线观看网站| 午夜福利高清视频| 最近中文字幕高清免费大全6| 乱码一卡2卡4卡精品| 男女啪啪激烈高潮av片| 一区二区三区免费毛片| 欧美+日韩+精品| 99热网站在线观看| 国产精品国产三级国产专区5o| 网址你懂的国产日韩在线| 亚洲av福利一区| 美女高潮的动态| 欧美区成人在线视频| 国产精品三级大全| 蜜桃久久精品国产亚洲av| 国产免费一级a男人的天堂| 亚洲av电影在线观看一区二区三区 | 欧美日韩亚洲高清精品| 22中文网久久字幕| 精品久久久精品久久久| 日韩在线高清观看一区二区三区| 国产精品人妻久久久影院| 麻豆av噜噜一区二区三区| 成人亚洲精品一区在线观看 | 91久久精品电影网| 啦啦啦中文免费视频观看日本| 午夜久久久久精精品| 午夜福利高清视频| 欧美日韩国产mv在线观看视频 | 真实男女啪啪啪动态图| 国产一区二区三区av在线| 亚洲精品国产av成人精品| 看黄色毛片网站| 男人舔女人下体高潮全视频| 国产成人aa在线观看| 成人毛片a级毛片在线播放| 搡老妇女老女人老熟妇| 日韩欧美一区视频在线观看 | 欧美一级a爱片免费观看看| 国产一区二区三区av在线| 久久国内精品自在自线图片| 99久久九九国产精品国产免费| 亚洲av免费在线观看| 国产精品一二三区在线看| 国产av码专区亚洲av| 国产亚洲最大av| 久久久久久久久久久丰满| 天天躁夜夜躁狠狠久久av| 一区二区三区四区激情视频| 极品少妇高潮喷水抽搐| 亚洲欧美精品专区久久| 久久久色成人| 少妇高潮的动态图| 久久久久久久午夜电影| 亚洲人成网站高清观看| 精品国产三级普通话版| a级毛色黄片| 欧美日韩综合久久久久久| 听说在线观看完整版免费高清| 极品少妇高潮喷水抽搐| 国产一区二区在线观看日韩| 97精品久久久久久久久久精品| 国产伦在线观看视频一区| 黄片wwwwww| 女人十人毛片免费观看3o分钟| 中文字幕免费在线视频6| 亚洲精品一二三| 亚洲精品,欧美精品| 乱人视频在线观看| 三级国产精品片| 国产精品99久久久久久久久| 亚洲欧美精品专区久久| 69人妻影院| 欧美日韩亚洲高清精品| 看十八女毛片水多多多| 亚洲美女视频黄频| 一区二区三区免费毛片| 久久久a久久爽久久v久久| 日本-黄色视频高清免费观看| 麻豆国产97在线/欧美| 国产视频内射| 十八禁网站网址无遮挡 | 久久亚洲国产成人精品v| 亚洲精品乱久久久久久| 国产乱人偷精品视频| av在线观看视频网站免费| 99久久精品国产国产毛片| 亚洲欧美日韩东京热| 国国产精品蜜臀av免费| 国产成人精品一,二区| 男人舔女人下体高潮全视频| 午夜激情福利司机影院| 亚洲欧美一区二区三区黑人 | 老司机影院毛片| 免费看美女性在线毛片视频| 波多野结衣巨乳人妻| 色综合亚洲欧美另类图片| 久久精品国产亚洲网站| 午夜福利高清视频| 一本一本综合久久| 国产精品一区二区在线观看99 | 精品国内亚洲2022精品成人| 七月丁香在线播放| 熟妇人妻不卡中文字幕| 精品久久久久久久久亚洲| 日韩 亚洲 欧美在线| 三级男女做爰猛烈吃奶摸视频| 观看美女的网站| 日韩一区二区视频免费看| 久久99热这里只有精品18| 国产视频内射| 日韩人妻高清精品专区| 亚洲av免费高清在线观看| 国产成人精品福利久久| 青青草视频在线视频观看| 大又大粗又爽又黄少妇毛片口| 精品久久久久久电影网| 午夜精品国产一区二区电影 | 亚洲怡红院男人天堂| 国产中年淑女户外野战色| 欧美日韩一区二区视频在线观看视频在线 | 黑人高潮一二区| 99热这里只有精品一区| 哪个播放器可以免费观看大片| 在线免费观看不下载黄p国产| 国产免费福利视频在线观看| 欧美zozozo另类| av在线亚洲专区| 国产亚洲午夜精品一区二区久久 | 人体艺术视频欧美日本| 欧美激情在线99| 亚洲精华国产精华液的使用体验| 国产精品三级大全| 午夜免费观看性视频| 丰满人妻一区二区三区视频av| 特大巨黑吊av在线直播| 免费播放大片免费观看视频在线观看| 日韩成人av中文字幕在线观看| 国产91av在线免费观看| 三级经典国产精品| 国内揄拍国产精品人妻在线| 性色avwww在线观看| 日韩视频在线欧美| 久久99精品国语久久久| 大片免费播放器 马上看| 成年女人在线观看亚洲视频 | 亚洲精品日韩av片在线观看| 男女视频在线观看网站免费| 免费少妇av软件| 国产一区二区三区av在线| 一区二区三区乱码不卡18| 午夜免费观看性视频| 亚洲成人中文字幕在线播放| 亚洲精品成人av观看孕妇| .国产精品久久| 我要看日韩黄色一级片| 免费看av在线观看网站| 国产成人freesex在线| 国产精品一及| 成人亚洲精品av一区二区| 亚洲欧美日韩无卡精品| 久久草成人影院| 亚洲精品视频女| 日韩亚洲欧美综合| 亚洲欧美精品自产自拍| 国产老妇伦熟女老妇高清| 欧美日韩一区二区视频在线观看视频在线 | 高清av免费在线| 国产色爽女视频免费观看| 久久久久精品久久久久真实原创| 内地一区二区视频在线| 又大又黄又爽视频免费| 亚洲精品乱码久久久v下载方式| 亚洲熟女精品中文字幕| 99久国产av精品| 亚洲自拍偷在线| 青春草国产在线视频| 男人舔奶头视频| 熟女人妻精品中文字幕| 亚洲精品自拍成人| 亚洲精品第二区| 男女啪啪激烈高潮av片| 免费在线观看成人毛片| 自拍偷自拍亚洲精品老妇| 国产片特级美女逼逼视频| 亚洲成人av在线免费| 国产精品久久视频播放| 高清午夜精品一区二区三区| 99久国产av精品国产电影| 九九在线视频观看精品| 亚洲四区av| 天堂中文最新版在线下载 | 国产精品美女特级片免费视频播放器| 一区二区三区高清视频在线| 最近2019中文字幕mv第一页| 2022亚洲国产成人精品| 午夜激情欧美在线| 日本与韩国留学比较| 非洲黑人性xxxx精品又粗又长| 男女啪啪激烈高潮av片| 久久99热6这里只有精品| 免费看a级黄色片| 99热这里只有是精品在线观看| 亚洲真实伦在线观看| 少妇人妻精品综合一区二区| 国产黄色免费在线视频| 亚洲一区高清亚洲精品| 亚洲乱码一区二区免费版| 亚洲精品第二区| 午夜福利在线在线| 一级av片app| 久久99蜜桃精品久久| 美女高潮的动态| 欧美日韩在线观看h| 一级av片app| 亚洲成人中文字幕在线播放| 亚洲美女搞黄在线观看| 精品一区二区免费观看| 又黄又爽又刺激的免费视频.| 国产 亚洲一区二区三区 | 欧美成人午夜免费资源| 国产成人免费观看mmmm| 精品一区二区三卡| 91久久精品国产一区二区三区| 欧美高清成人免费视频www| 亚洲av电影在线观看一区二区三区 | 黄色一级大片看看| 97热精品久久久久久| 看免费成人av毛片| 91久久精品国产一区二区三区| 老师上课跳d突然被开到最大视频| 亚洲自拍偷在线| 禁无遮挡网站| 搞女人的毛片| 又粗又硬又长又爽又黄的视频| 91精品国产九色| 国产永久视频网站| 久久6这里有精品| 成人午夜精彩视频在线观看| 免费电影在线观看免费观看| 超碰97精品在线观看| 国产永久视频网站| 亚洲va在线va天堂va国产| 少妇熟女aⅴ在线视频| 丰满乱子伦码专区| 老师上课跳d突然被开到最大视频| 亚洲熟女精品中文字幕| 精品人妻熟女av久视频| 人人妻人人澡人人爽人人夜夜 | 国产一级毛片在线| 亚洲精品亚洲一区二区| 亚洲精品影视一区二区三区av| 国产精品1区2区在线观看.| 午夜福利在线观看吧| 精品国产一区二区三区久久久樱花 | 麻豆久久精品国产亚洲av| 老司机影院成人| 国产乱人视频| 国产精品伦人一区二区| 菩萨蛮人人尽说江南好唐韦庄| 99久久人妻综合| 日日撸夜夜添| 国产欧美日韩精品一区二区| 免费大片18禁| 久久精品国产亚洲av涩爱| 亚洲成人久久爱视频| 国产高清国产精品国产三级 | 久久精品人妻少妇| av在线天堂中文字幕| 国产综合懂色| 男人舔女人下体高潮全视频| 少妇熟女欧美另类| 身体一侧抽搐| 午夜福利视频精品| 亚洲,欧美,日韩| 综合色av麻豆| 十八禁国产超污无遮挡网站| 久久精品夜夜夜夜夜久久蜜豆| 欧美成人精品欧美一级黄| av播播在线观看一区| 国产69精品久久久久777片| 搞女人的毛片| 舔av片在线| 亚洲av中文字字幕乱码综合| 97超视频在线观看视频| 欧美极品一区二区三区四区| 亚洲自拍偷在线| 免费在线观看成人毛片| 中文天堂在线官网| 在线免费十八禁| 亚洲欧美一区二区三区黑人 | 麻豆国产97在线/欧美| 成人二区视频| 91aial.com中文字幕在线观看| 男插女下体视频免费在线播放| 成人美女网站在线观看视频| 欧美另类一区| 国产亚洲精品av在线| 精品欧美国产一区二区三| 亚洲经典国产精华液单| 免费观看无遮挡的男女| 伊人久久精品亚洲午夜| 青春草亚洲视频在线观看| 久久精品熟女亚洲av麻豆精品 | 亚洲婷婷狠狠爱综合网| 国产精品99久久久久久久久| 男女国产视频网站| 精品久久久噜噜| 亚洲一级一片aⅴ在线观看| 精品亚洲乱码少妇综合久久| 亚洲欧美日韩无卡精品| 韩国高清视频一区二区三区| 国产精品国产三级专区第一集| 在线免费十八禁| 大话2 男鬼变身卡| 丰满少妇做爰视频| 波野结衣二区三区在线| 国产精品久久久久久av不卡| 国产精品一区二区三区四区免费观看| 国产高清有码在线观看视频| 欧美+日韩+精品| 91久久精品国产一区二区三区| a级一级毛片免费在线观看| www.色视频.com| 日日啪夜夜爽| 一级毛片 在线播放| 免费黄网站久久成人精品| av播播在线观看一区| 久久人人爽人人片av| 日韩av在线免费看完整版不卡| 熟女人妻精品中文字幕| 国产女主播在线喷水免费视频网站 | 亚洲人成网站在线播| 欧美日韩精品成人综合77777| 久久草成人影院| 免费观看a级毛片全部| 成人二区视频| 免费观看a级毛片全部| 91精品国产九色| 亚洲成人中文字幕在线播放| 免费看日本二区| 亚洲成人中文字幕在线播放| 99久国产av精品| 日韩中字成人| 中文字幕制服av| 看非洲黑人一级黄片| 蜜桃久久精品国产亚洲av| 亚州av有码| 中文字幕久久专区| 久久精品久久精品一区二区三区| 三级国产精品欧美在线观看| 国产单亲对白刺激| 五月玫瑰六月丁香| 国产成人freesex在线| 亚洲最大成人手机在线| 国产黄频视频在线观看| 久久久a久久爽久久v久久| 青春草亚洲视频在线观看| 久久久久久久久久人人人人人人| 午夜激情福利司机影院| 色综合亚洲欧美另类图片| 亚洲人成网站在线观看播放| 午夜福利视频精品| 日韩av在线免费看完整版不卡| 内地一区二区视频在线| 成人特级av手机在线观看| 三级经典国产精品| 免费黄色在线免费观看| 亚洲综合色惰| 免费看不卡的av| 国模一区二区三区四区视频| 蜜臀久久99精品久久宅男| 极品少妇高潮喷水抽搐| av在线天堂中文字幕| 熟女电影av网| 女人被狂操c到高潮| 国产一区亚洲一区在线观看| 伊人久久精品亚洲午夜| av女优亚洲男人天堂| 97人妻精品一区二区三区麻豆| 十八禁国产超污无遮挡网站| 日本av手机在线免费观看| 亚洲欧美一区二区三区黑人 | 国产成人免费观看mmmm| 亚洲无线观看免费| 亚洲最大成人手机在线| av国产免费在线观看| 久久精品熟女亚洲av麻豆精品 | 人妻一区二区av| 久久国内精品自在自线图片| 日本色播在线视频| 成年女人在线观看亚洲视频 | 亚洲图色成人| 搡老乐熟女国产| 成人亚洲欧美一区二区av| 麻豆精品久久久久久蜜桃| 日韩大片免费观看网站| 一个人看视频在线观看www免费| 精品欧美国产一区二区三| 国产一区二区在线观看日韩| 天堂av国产一区二区熟女人妻| 大片免费播放器 马上看| 国产精品国产三级专区第一集| 国产 一区 欧美 日韩| 国产黄色小视频在线观看| 成人毛片60女人毛片免费| 亚洲久久久久久中文字幕| 淫秽高清视频在线观看| 全区人妻精品视频| 超碰97精品在线观看| 高清av免费在线| 一个人看的www免费观看视频| 麻豆乱淫一区二区| 一级毛片 在线播放| 内射极品少妇av片p| 亚洲欧美中文字幕日韩二区| 日韩精品有码人妻一区| 赤兔流量卡办理| 国产精品久久视频播放| 亚洲乱码一区二区免费版| 精品一区二区三卡| 欧美成人a在线观看| 亚洲欧美清纯卡通| 91av网一区二区| 国产伦精品一区二区三区四那| 欧美成人一区二区免费高清观看| 免费高清在线观看视频在线观看| 亚洲天堂国产精品一区在线| 免费大片18禁| 成人毛片a级毛片在线播放| 亚洲国产精品国产精品| 我要看日韩黄色一级片| 寂寞人妻少妇视频99o| 中文字幕制服av| 噜噜噜噜噜久久久久久91| 在线天堂最新版资源| 女的被弄到高潮叫床怎么办| 夫妻午夜视频| 成人亚洲欧美一区二区av| 免费看日本二区| 国国产精品蜜臀av免费| 国产熟女欧美一区二区| 女的被弄到高潮叫床怎么办| 国产精品爽爽va在线观看网站| 天堂中文最新版在线下载 | 精品一区二区三卡| 18禁在线无遮挡免费观看视频| 欧美日韩在线观看h| 99久久精品一区二区三区| 国产在视频线精品| 在线观看一区二区三区| 久久久久免费精品人妻一区二区|