    Roles of pH in the NH4+-induced corrosion of AZ31 magnesium alloy in chloride environment

    2022-12-30 03:41:00FengGeJiaxuanYinYueLiuWenjunLengXinWangZhongyuCui
    Journal of Magnesium and Alloys 2022年11期

    Feng Ge,Jiaxuan Yin,Yue Liu,Wenjun Leng,Xin Wang,Zhongyu Cui

    School of Materials Science and Engineering,Ocean University of China,Qingdao 266100,China

    Abstract Corrosion behavior of AZ31 magnesium alloy in NH4+-bearing chloride solution with controlled pH was investigated by weight loss experiment,hydrogen collection,and electrochemical test combined with surface morphology and topography observation.The results show that NH4+ and pH of the solution can affect the corrosion of AZ31 magnesium alloy.The existence of NH4+ affects the formation and dissolution of corrosion products,which makes the protective effect of the corrosion product layer weaker.The change of pH value not only affects the corrosion mechanism of AZ31,but also alters the concentration of NH4+ ions in the solution,which further influence the corrosion product layer of AZ31,and finall makes the corrosion of AZ31 change significantl.

    Keywords: NH4+;pH;AZ31 magnesium alloy;Corrosion.

    1.Introduction

    In recent years,air pollution is increasing seriously,especially in some industrial places.Several studies show that the oppressive atmosphere of the environmental problem could cause global environmental deterioration,climatic anomaly,and threats to human health [1,2].Besides,researchers found that air pollution also could influenc the corrosion of the metallic materials [3–5].According to previous reports,content of water-soluble ions (like NO3-,SO42-,NH4+,etc.) increases in the atmosphere due to air pollution [6,7].These ions are proved to influenc the metal corrosion in the atmosphere [8–14].The ammonium salt particles formed by the precipitation of NH3become the main component of haze pollution [15,16].For example,Zhang et al.[15] found that NH4+accounted for 17.7% of the total water-soluble ions in Xiamen.Researchers have studied the effects of NH4+on the corrosion of several kinds of materials and demonstrated its deterioration effect [12,17–22].It is worth noting that watersoluble ions become more aggressive on corrosion in the humid air environment.Especially in the marine atmospheric environment,moist air and more Cl-make corrosion easier than anywhere else [23,24].These ions,which dissolve much more into the thin liquid fil on the material surface,could promote the corrosion more distinctly [25–27].

    Magnesium alloy,as one of the lightest structural material,is an ideal choice for auto lightweight in the future [13].However,it is difficul to avoid the corrosion of automotive magnesium alloys during service in atmospheric environment.Cui et al.[24] and Li et al.[8,9] studied the atmospheric corrosion of Mg alloys in the coastal and polluted air environments and suggested that the corrosion was promoted in these areas because of the abundant presence of Cl-and SO2,respectively.Acharya and Shetty [10] also pointed out that the corrosion rate of AZ31 increases with the increasing concentration of Cl-and SO4-.The energy barrier for the occurrence of corrosion reaction (Ea) decreased from 54.0 to 16.9kJ/mol as the Cl-concentration is increased from 0.02 to 0.25mol/L.Zeng et al.[28] studied the effect of the ions in saline solution on magnesium alloy corrosion,including HCO3-,SO42-,HPO32-,and H2PO3-and showed that these ions exhibited an impact on the corrosion behavior and mechanism.The fact is that the Mg alloy is easy to be corroded and the corrosion process is also easy to be influence by water-soluble ions and the pH [29–31].

    Some researchers investigated the effect of NH4+on the corrosion of magnesium alloy in solution.Battochi et al.[32] found that the corrosion rate of magnesium alloys in dilute Harrison solution (0.05wt.% NaCl+0.35wt.%(NH4)2SO4) was one order higher than that in NaCl(0.1wt.%) solution.Citterio et al.[33] suggested that the NH4+caused the precipitation of Mg(OH)2with dissociation into NH3and H+as local pH increased,which promoted the formation of soluble corrosion products and resulted in the high reactivity of Mg in dilute Harrison solution.Buggio et al.[34] reported that AZ31 magnesium alloy would generate a layer of black corrosion products in the presence of ammonium ions.They declared that the NH4+promoted the formation of magnesium hydride.Cao et al.[35] reported the effect of NH4+on magnesium and demonstrated the accelerated ratio of 30~100 when the NH4+concentration is increased from 0 to 0.8mol/L as well as the corresponding degradation mechanism.They emphasized the enhanced dissolution of relatively protective MgO by NH4+,which resulted in the acceleration effect on Mg corrosion.

    In our previous works [21,22],the corrosion process of magnesium alloy in the NH4+-Cl--NO3-and pure (NH4)2SO4environment was investigated.The results showed that NH4+had a unique effect on the corrosion of magnesium alloy,attributed to the promotion of cathodic reaction and the change of Mg(OH)2.Moreover,the effect of NH4+on the corrosion of magnesium alloy is closely related to the solution pH because of the existence form of NH4+differs with pH.Therefore,in this paper,we designed experiments including the immersion test,hydrogen collection test,polarization curves and surface morphology and topography observation to study the corrosion behavior of magnesium alloy under the various conditions of NH4+and pH values,exploring the effect of pH on the corrosion mechanism of AZ31 in NH4+-containing solution system.

    2.Experimental

    2.1.Material and solution

    The material used in this experiment was the commercial standard AZ31 magnesium alloy plate (3.19wt.% Al,0.81wt.% Zn,0.025wt.% Si,0.006wt.% Fe,0.002wt.% Cu,0.001wt.% Ni,Bal.Mg) with a thickness of 3mm (provided by Shanxi United Magnesium Industry Co.,Ltd).According to the different tests,the samples with different dimensions were prepared by wire cutting.The solutions used in the present work were pure NaCl and NH4Cl with different concentrations (0.001M,0.01M,0.1M) and pH(4.67,7.13,8.85).The NaCl solution was employed to exclude the effect of Cl-in the NH4Cl solution and highlight the special effect of NH4+and pH.To adjust and maintain the solution pH,the buffer solutions including 0.22M CH3COONa+0.3M CH3COOH(for pH 4.67),0.95M H3BO3+0.15M Na2B4O7·10H2O (for pH 7.13) and 0.15M H3BO3+0.05M Na2B4O7·10H2O (for pH 8.85) were used.All the solutions were made with analytical grade reagents and high-quality deionized water.The solution temperature was maintained at 25 ± 1 °C by the water bath during the test.

    2.2.Immersion test and weight loss

    For the immersion test,the samples were cut into pieces with dimensions of 20mm×20mm×3mm.The samples were ground with SiC paper gradually up to 1500 grit and then washed with distilled water,degreased with acetone,and dried with cold air.Before tests,the original weight(w0,mg) of the specimens were recorded by a digital balance with a precision 0.0001g.After immersion with different time intervals,the fina weight of the samples without corrosion products (removed with chromate solution of 200g/L CrO3+10g/L AgNO3+20g/L BaNO3) was obtained(w1,mg).The weight loss (C,mg/cm2) was calculated as follows:

    whereS(cm2) is the surface area of the specimens.

    Besides,during the immersion test for different concentrations of NaCl and NH4Cl,the pH of the solution was monitored.

    2.3.Hydrogen evolution test (HE)

    The samples used in hydrogen gas collection and their pretreatment were the same as those in Section 2.2.The evolved hydrogen in different solutions was collected during the immersion.A set of devices assembled by a burette and funnel were used to collect the hydrogen generated by the cathodic reaction.The change of solution volume in the burette displayed the volume of released hydrogen.The ratio of solution volume to sample area was controlled at 40:1 [36].The burette was fille with the initial solution before the test.

    2.4.Electrochemical tests

    A size of 10mm×10mm×3mm pieces were sealed into epoxy resin with 1 cm2surface exposed for electrochemical tests.CHI 660E electrochemical workstation with a threeelectrode cell was used for measuring potentiodynamic polarization curves.A platinum sheet was used as a counter electrode,and a saturated calomel electrode (SCE) as a reference electrode.For the polarization curves,the potential was scanned from open circuit potential (OCP) to anodic and cathodic directions separately with a rate of 0.333mV/s.For the cathodic curves,the potential was scanned from +50 mVOCPto ?500 mVOCP.In the case of anodic curves,the potential was scanned from ?50 mVOCPto positive direction until the anodic current density reached 10mA/cm2.

    2.5.Surface morphology and topography observation

    Fig.1.Weight loss (a) and average corrosion rate (b) of AZ31 alloy during immersion in solutions with different concentrations of NaCl and NH4Cl.

    The surface of the samples after immersion test without corrosion products was observed by scanning electron microscope (SEM,Quanta 250) and confocal laser scanning microscope (CLSM,VK-250X).

    3.Results and discussion

    3.1.Corrosion of Mg in NH4+-Cl- solution environment without pH buffer

    3.1.1.Weight loss,hydrogen evolution,and corrosion rate

    Fig.1 shows the weight loss and corrosion rate of AZ31 alloy during immersion in solutions with different concentrations of NaCl and NH4Cl.The results display that the weight loss in all solutions increases rapidly during the 24 h immersion.After that,the corrosion rate decreases slowly as the soaking time increases.In Fig.1a,the weight loss curve certifie that the presence of ammonium ions greatly promotes the corrosion of the AZ31 samples despite the NH4+concentration is low.

    In Fig.1b,the average corrosion rate is calculated by the following equation:

    Fig.2.Hydrogen evolution volume (a) and the corresponding corrosion rate(b) of AZ31 magnesium alloy during immersion in solutions with different concentrations of NaCl and NH4Cl.

    wherePw(mm/year) is average corrosion rate,C(mg/cm2) is the weight loss,t(h) is the immersion time.Fig.1b demonstrates that the increase of NaCl and NH4Cl concentration increases the corrosion rate of magnesium alloy.However,NH4+can promote the corrosion rate more significantl.Besides,the average corrosion rate of all the samples reduces with extending immersion time.In the 0.1M NH4Cl,the reduction of the corrosion rate is the most remarkable.After 120 h immersion,the corrosion rate of AZ31 samples in 0.001,0.01 and 0.1M NaCl and NH4Cl are 0.18,0.27,0.70,0.35,1.44,and 8.46mm/year.The presence of NH4+increases the corrosion rate of AZ31 magnesium alloy by 1.9,5.3,and 12.1 times when the concentration is 0.001,0.01,and 0.1M,respectively.

    Fig.2 shows the dependence of hydrogen evolution volume(a) and the corresponding corrosion rate (b) on the immersion time in the solutions with different concentrations of NaCl and NH4Cl.The hydrogen evolution takes place on Mg surface according to the following reaction equation:

    The reaction indicates that corrosion of 1mol Mg (24.31g)will produce 1mol H2(22.4L).Therefore,the average corrosion rate (VH,ml/cm-2·d-1) was calculated by the following equation [37]:

    whereVn(mL) is the change of the released hydrogen during immersion,S(mm2) is the surface area,tis the immersion time.PHis the regular corrosion rate inferred by the Faraday’s law.The results show that the samples in all corrosive media continuously evolve hydrogen during the immersion but the hydrogen evolution rate differs from different solutions.The hydrogen evolution is rapid during the initial immersion period,and the increasing degree gradually attenuates with the immersion time in all six solutions,which is consistent with the results of the weight loss.When the concentration of NH4Cl is 0.1M,the detected hydrogen gas volume is much more than the other fi e conditions.After 12h immersion,the hydrogen evolution volume has exceeded the range of hydrogen collection device.In general,the addition of NH4+significantl increases the hydrogen evolution volume.The gas volume is relatively close in 0.001M NaCl,0.01M NaCl,and 0.001M NH4Cl.When the NaCl concentration is 0.1M,the evolved hydrogen volume and corrosion rate of the AZ31 samples are lower than those in 0.01M NH4Cl.During the 120h immersion,the average corrosion rate of AZ31 samples obtained by hydrogen evolution test in 0.001,0.01,and 0.1M NaCl are 0.02,0.03,and 0.30mm/year.The average corrosion rate in 0.001M,0.01M NH4Cl was 0.01 and 0.58mm/year,while it was 42.78mm/year for AZ31 samples in 0.1M NH4Cl during the 12h immersion.

    The above results suggest that the presence of NH4+remarkably promotes the corrosion of AZ31 magnesium alloy especially in the solution with high NH4+concentration.Generally,NH4+can be hydrolyzed in the solution as follow reaction equation:resulting in the acidificatio of the solution.Table 1 shows that the initial (0h) pH of different concentrations of NH4Cl solution is slightly acidic.Many studies have proved that acid medium could promote the corrosion of AZ31 alloy[22,32,33].

    Table 1 Variation of solution pH during the immersion test.

    Table 2 Extrapolated parameters from polarization curves of AZ31 specimens in solutions with different concentrations of NaCl and NH4Cl.

    By monitoring the pH value of the solution,it is found that the pH value increases with prolonging immersion time.However,at the same concentration,the pH of NH4Cl is always lower than that of NaCl.It means that the change of pH in solution caused by NH4+is a continuous process.That is to say,the reduction of pH is permanent for the promotion of corrosion.It is also important to note that the higher the concentration of NH4+ions,the more significan the change of pH value during the soaking process.It shows that the pH change of the solution caused by the presence of NH4+ions is critical for Mg.

    Fig.3.The polarization curves of AZ31 alloys before (a) and after (b) IRcompensation in solutions with different concentrations of NaCl and NH4Cl.

    3.1.2.Electrochemical behavior

    Fig.3 displays the polarization curves of AZ31 alloy before and after IR-compensation in different solutions.As the polarization curve is tested by separate scanning to the cathodic and anodic directions from the OCP,the corrosion potential is statistically analyzed,and the results are shown in Table 2.Since the cathodic interference is avoided by separate scanning,the corrosion potential is equal to short-term OCP [21].With NaCl concentration increasing from 0.001M to 0.1M,the corrosion potential shows little change but the slope of the anodic and cathode branches is altered.However,in the NH4Cl solution,with increasing NH4+concentration,the cathodic curves are shifted to the right side,indicating the expedition of the cathodic reactions.Even so,the shape of curves does not change,indicating that the reaction mechanism does not change except for the promoted reaction rates.In addition,no limiting current and passivation tendency can be identifie in the polarization curves,suggesting that the corrosion process is controlled by the charge transfer process.The deviation of the anodic polarization curves from the Tafel law in some cases is attributed to the generation of the corrosion products on the magnesium surface [38].

    The fitte corrosion current density and Tafel slopes by Tafel extrapolation are listed in Table 2.It should be noted that only the cathodic branch is fitte because the anodic branch does not meet the strict prerequisites for the Tafel fittin [39].By comparing the polarization curves in NH4Cl and NaCl solution with the same concentration,the promotion effect of NH4+on the anodic and cathodic reactions can be found.The acceleration of cathodic reaction kinetics results in the positive shift of the corrosion potential [40],while the facilitation of anodic reactions leads to the negative shift of corrosion potential.In the solution containing 0.01M NH4+,the cathodic reaction process is more heavily promoted,and the corrosion potential rises from ?1.535 to ?1.494 VSCEand corrosion current density increases from 20.6 to 81.7 μA/cm2.As the NH4+concentration is increased to 0.1M,the anodic process is significantl accelerated,and the corrosion potential declines from ?1.545 to ?1.599 VSCEaccompanied by increase of corrosion current density from 78.6 to 827.1 μA/cm2.The change of NH4+concentration determines the dynamic trend of anodic and cathodic reactions of AZ31 alloy.

    3.1.3.Corrosion morphology

    The corrosion morphologies after removing corrosion products and the corresponding surface topographies of AZ31 alloy after immersion in NaCl and NH4Cl for different time are shown in Figs.4 and 5,respectively.It is seen that more serious localized corrosion appears with increasing NH4+concentration.Under the same concentration of Cl-,the corrosion is more severe in the NH4Cl than that in the NaCl.Also,the corrosion is aggravated with extending immersion time in all the solutions.It is worth noting that the white Al-Mn phase can be observed on the surface,which is served as the cathodic phase that accelerates the dissolution of anodicα-Mg during the corrosion process.When the NaCl concentration is 0.001M,the sample surface shows slight pitting corrosion after 6h immersion (Fig.4a1).With 0.001M NH4+,corrosion becomes more serious as indicated by the enhanced dissolution area in Fig.4b.In 0.01M NaCl solution,corrosion pits begin to transfer from pitting to filifor corrosion as the immersion time prolongs to 120h (Fig.4c3).The addition of 0.01M NH4+increases the occurrence rate of pitting and changes the corrosion morphology after 24 and 120h immersion (Fig.4d2–d3).Pitting and filifor corrosion (Fig.4e1-f1)appear at the same time after 6h immersion in 0.1M NaCl solution.After 120h immersion,corrosion propagates laterally and gradually and becomes uniform corrosion with isolated cavities (Fig.4e3).With 0.1M NH4+,typical uniform corrosion morphology can be observed,especially when the immersion time is more than 24 h.The serious corrosion caused by the high concentration of NH4+erases the occurrence of localized corrosion (Fig.4f2,f3).

    The topography results shown in Fig.5 clearly illustrate the evolution of the corrosion process.With increasing of NH4+content,Mg alloy not only has a higher probability of pitting(Fig.5d1,f1) during the initial immersion stage,but also has a more serious uniform corrosion (Fig.5d2,f2,d3,f3).

    3.1.4.Effect of NH4+on corrosion of Mg

    The aforementioned results show that NH4+promotes the corrosion of magnesium alloy in the NH4+-Cl-system.It is affected by two ways: one is the hydrolysis of NH4+,which affects the pH of the solution.The other is the influenc of NH4+on the corrosion product layer on the surface of magnesium alloy.

    It is generally believed that the main corrosion products on magnesium alloy surface are the outer porous Mg(OH)2and inner protective MgO layer,and the presence of NH4+can accelerate the dissolution rate of the two products.It has been proved that the NH4+-induced dissolution rate of MgO is three times higher than that of Mg(OH)2[35].In this case,the corrosion mechanism of Mg in the NH4+-Cl-system can be summarized.NH4+affects the corrosion of Mg alloy through hydrolysis and the change of dissolution rate of corrosion products.But there is a limit between the two actions.In this study,when the concentration of NH4+is small(less than 0.01M),the solution shows weak acidity,and the presence of H+in the solution promotes the cathodic reaction of magnesium alloy.However,the weak acidity is not enough to encourage the anodic reaction,so the corrosion potential shows a positive shift.Yet,when the NH4+concentration is high (0.1M),the pH change of solution due to hydrolysis has a more significan effect on corrosion,and the corrosion potential has a significan negative shift.The impact of NH4+on corrosion products is positively correlated with its concentration.Under the combined action of NH4+and Cl-in the solution,the local corrosion depth and size of the pits on magnesium alloy surface increase significantl and evolve to uniform corrosion quickly.

    3.2.Roles of pH in the NH4+-induced corrosion of AZ31

    3.2.1.Weight loss and corrosion rate

    Fig.6 shows the weight loss and average corrosion rate of samples in 0.01M and 0.1M pure NaCl and pure NH4Cl solution with different pH.It should be noted that the immersion period is 24h for the solution with pH 8.85 and 7.13.In comparison,it is 6 h for the solution with pH 4.67 because of the relatively high corrosion rate in this environment.6a and c reveal that when the NH4+concentration is 0.01M,pH of the solution has a little influenc on Mg corrosion.Differently,when the NH4+concentration is 0.1M,the weight loss and corrosion rate is increased with the presence of NH4+(6b and d).In addition,the weight loss and corrosion rate increase distinctly with decreasing pH.

    Fig.4.Corrosion morphologies of AZ31 alloy samples after immersion for 6 (a1-f1),24 (a2-f2) and 120 (a3-f3) hours in solutions with different concentrations of NaCl and NH4Cl.

    These results once again prove that the effect of NH4+on corrosion of magnesium is related to pH.At the same time,the reason for the limit value caused by NH4+hydrolysis alone cannot be well explained here.Especially when the pH is fi ed to a particular value,the effect of pH by hydrolysis is weak.It shows that the existence of this limit also affects the role of NH4+.

    3.2.2.Potentiodynamic polarization curves

    Fig.7 shows the polarization curves of the specimens in 0.01M and 0.1M pure NaCl and pure NH4Cl with different pH.Similar to the results shown in Fig.3,the corrosion is controlled by charge transfer process without limiting current and passivation phenomenon.In the solution containing 0.01M Cl-,cathodic reaction is enhanced with addition of NH4+as the buffered pH is controlled at 8.85 (Fig.7a).However,no visible changes can be distinguished between the NH4+-bearing and Na+-bearing solutions when the buffered pH is kept at 7.13 and 4.67 (Fig.7b and c).This phenomenon is consistent with the weight loss results in which only slight increase in corrosion rate caused by NH4+is observed in the pH 8.85 solution when the Cl-concentration is 0.01M.As the Cl-concentration is increased to 0.1M,the reaction rates difference cannot be distinguished.However,the variations of the anodic and cathodic reaction rates differ from solution pH values.When the buffered solution is controlled at 8.85 and 7.13,cathodic reactions are expedited,while the anodic reaction is stimulated at pH 4.67.

    Fig.5.3D profile of AZ31 alloy samples after immersion for 6 (a1-f1),24 (a2-f2) and 120 (a3-f3) hours in solutions with different concentrations of NaCl and NH4Cl.

    The Tafel fittin results including the corrosion current density and cathodic Tafel slopes are listed in Table 3.The results show that the presence of NH4+does not affect the electrochemical reaction of magnesium alloy when its concentration is low.At the same pH of NH4Cl and NaCl solution,the shifting trend of polarization curves is the same with the increase of solution concentration and the corrosion current density exhibits little change.So it means that pH controls the corrosion kinetics of Mg alloy in this environment.However,the corrosion rate extrapolated from polarization curves cannot be used to compare the corrosion rate of magnesium because the differences cannot be distinguished when the cathodic branch is fitted As compared with the weight loss data,the acceleration of the anodic reactions especially in the solution with 0.1M NH4+is responsible for the slight increase in weight loss.

    Fig.6.Weight loss and average corrosion rate of AZ31 alloy in solution under different pH conditions: (a,b) weight loss in 0.01M NaCl and NH4Cl solution,(c,d) average corrosion rate in 0.1M NaCl and NH4Cl solution.

    Table 3 Extrapolated parameters from polarization curves of AZ31 specimens in NH4+-bearing and Na+-bearing chloride solution with different pH.

    3.2.3.Corrosion morphology and topography observation

    The SEM and CLSM morphologies of the samples after immersion in the solution with different pH are shown in Figs.8 and 9,respectively.In solution with pH 7.13,the surface morphology of the samples is almost the same.But in the solution with pH 8.85 and 4.67,the corrosive degree is different between the samples in NH4Cl and NaCl.It should be noted that the NH4+causes corrosion aggravation in these two solutions.The 0.01M NaCl and NH4Cl solution only slightly corrode the surface of magnesium alloy at pH 8.85 (Figs.8a1,b1,and 9a1,b1).But there is no pitting,which could influenc the protection and stability of the corrosion product layer under this condition.With increasing concentration,pitting occurs in NaCl solution and pitting turns into uniform corrosion in the NH4Cl solution.In pH 7.13 environment,the probability of shallow dish pitting is high,and uniform corrosion tends to cover the metal surface in a large area.When the pH value is 4.67,AZ31 samples in 0.01M NaCl and NH4Cl contains corrosion pits that connects into shallow dish.When the concentration is increased to 0.1M,dense pitting morphology with larger pit diameter can be found (Fig.8c3,d3).Under the same pH value,the addition of NH4+does not change the corrosion morphology.Still,it promotes the occurrence of uniform corrosion morphology which may be transformed from the early pitting corrosion.It also can be found that in the solution with low pH value and high concentration,the localized corrosion is easier to appear and is more obvious.

    Fig.7.The polarization curves of AZ31 alloys before (a,c,d) and after (b,e,f) IR-compensation in different concentrations of NaCl and NH4Cl solution under different pH conditions.

    The corrosion morphology still shows that pH controls the corrosion surface morphology of Mg alloy.Under the condition of pH control,NH4+did not show the same effect as a result in Section 3.1.In the alkaline and neutral environment,the presence of NH4+only shows an impact on the increase of pitting corrosion.However,under the condition of pH value being 4.67,7.13,and 8.85,the pitting density and size become smaller than those under the same NaCl condition,attributed to the accelerated corrosion process that promotes the evolution from pitting corrosion to uniform corrosion.

    3.2.4.Effect of pH on the corrosion of Mg induced by NH4+

    According to Pan et al.[21],the effect of the initial pH value of the solution due to NH4+hydrolysis is negligible.Through the above results,it can be concluded that pH can not only control the corrosion of Mg alloy,but also control the action of NH4+.First of all,it should be noted that pH can control the proportion of NH4+in solution.The percentage of NH4+in solution can be obtained by the following formula[41]:

    whereKhis the hydrolysis constant of NH4+.According to the different pH values (8.85,7.13,and 4.67),the proportion of NH4+is 71.1%,99.2%,and 99.9% in the alkaline,neutral,and acidic solutions,respectively.The lower the pH value is,the higher the percentage of NH4+.Even so,both NH4+and NH4OH can affect the corrosion of Mg [22].

    In this study,the effect of pH induced by NH4+is mainly attributed to the fact that pH controls the hydrolysis of NH4+,affecting the proportion of NH4+,and thus influencin the state of corrosion product layer on Mg surface.It is worth mentioning that the different corrosion products layers generating in different solution could change the corrosion process and mechanism of Mg alloys [42].In the solutions with different pH,the model of the NH4+-induced corrosion of AZ31 magnesium alloy is shown in Fig.10.

    When the pH is 8.85,the presence of OH-in the solution promotes the formation of Mg(OH)2.Although Mg(OH)2is porous with partially protection [34],it still plays a vital role in the corrosion process of magnesium alloy.Therefore,the corrosion loss of Mg alloy is the smallest and the corrosion degree is the lightest.Under this condition,the proportion of NH4+in the solution is the lowest.However,the enrichment of OH-can still attract the NH4+,but the same electricity will exclude Cl-.Therefore,NH4+can still improve the dissolution of Mg(OH)2,which increases weight loss and corrosion rate.

    Fig.8.Corrosion morphologies of AZ31 alloys after immersion for 6 (a3-c3) or 24 (a1-d1,a2-d2) hours in 0.01M and 0.1M NaCl and NH4Cl solution with solution pH of 8.85 (a1-d1),7.13 (a2-d2),and 4.67 (a3-d3).(The immersion test lasts 6 h in the acidic environment because of the high corrosion rate.).

    When the pH is 7.13,NH4+has the least effect on the corrosion of Mg alloy.Under this condition,because the pH value of the solution is neutral,the anodic and cathodic reactions are also in equilibrium during the dissolution of magnesium alloy.Therefore,the corrosion potential of the polarization curve is not shifted with changing solution concentration.In this case,some NH4+is hydrolyzed to produce H+.This part of H+promotes the cathodic reaction,and the anodic reaction is also facilitated to keep the balance,resulting in the formation of thicker corrosion product layer.When the concentration of NH4+is low,the effect is not significant As the concentration of NH4+increases,the effect of NH4+on the dissolution of Mg(OH)2becomes more significant At this time,the amount of H+produced by NH4+hydrolysis also increases,which can make the local environment more acidic and the cathodic reaction is promoted,resulting in the positive shift of the corrosion potential.

    When the pH is 4.67,the formation and dissolution rate of Mg(OH)2and MgO on the alloy surface are enhanced by excessive H+,resulting in the acceleration of the anodic reactions and the negative shift of the corrosion potential.At this time,99%of NH4+is in the form of ions,so the H+produced by hydrolysis is very little.Therefore,the increase of NH4+on the dissolution of corrosion product fil is the reason for the negative shift of corrosion potential at the same concentration of NH4Cl and NaCl.In this case,the pitting corrosion is accelerated.In addition,the falling off of the corrosion product layer is enhanced in this environment,which further accelerates the corrosion rate.

    Therefore,it can be concluded that the pH of the solution plays an important role in controlling the corrosion of Mg in NH4+-Cl-system.On the one hand,pH controls the kinetics of the corrosion reaction of Mg alloy.On the other hand,pH can control the hydrolysis of NH4+,which makes the content of NH4+significantl related to the pH of the solution.When the concentration of NH4+is low,the pH plays a significan role,and the presence of NH4+will affect the corrosion of Mg.When the concentration of NH4+is high,the effect of NH4+on the corrosion product fil of the Mg surface becomes significant and the promotion effect of NH4+on the corrosion of Mg alloy becomes more apparent.

    Fig.9.3D profile of AZ31 alloys after immersion for 6 or 24 h in 0.01M,0.1M NaCl and NH4Cl solution under different pH conditions.

    Fig.10.Schematic diagram of the NH4+-induced corrosion of AZ31 alloy in the solutions with different pH.

    4.Conclusion

    (1) NH4+can affect the corrosion of Mg alloy in two aspects.One is that NH4+can affect the formation and dissolution of corrosion products on the magnesium alloy surface,and the other is that NH4+can promote the cathodic hydrogen evolution reaction.However,NH4+does not change the electrochemical corrosion reactions of magnesium alloy in the chloride solution.

    (2) The pH of the solution can affect the corrosion process of NH4+on Mg.There is no synergistic effect between NH4+and solution pH on the corrosion of Mg alloy,and the mechanism between them is independent.

    (3) In the presence of NH4+,the pitting corrosion is accelerated especially during the initial immersion stage,which may be attributed to the partial destruction of NH4+on the corrosion product layer.

    Declaration of Competing Interest

    None.

    Acknowledgement

    The authors wish to acknowledgement the financia support of the National Natural Science Foundation of China (Nos.51601182),the Fundamental Research Funds for the Central Universities (No.201762008) and Shandong Provincial Key R &D plan (No.2019GHY112050).

    日本欧美国产在线视频| .国产精品久久| 大型黄色视频在线免费观看| 日韩三级伦理在线观看| 久久天躁狠狠躁夜夜2o2o| 午夜激情福利司机影院| 精品国内亚洲2022精品成人| 国产精品久久久久久久电影| 日日撸夜夜添| 中国美女看黄片| 韩国av在线不卡| 成人综合一区亚洲| 全区人妻精品视频| 国产精品一及| 最近手机中文字幕大全| 国产综合懂色| av.在线天堂| 亚洲美女视频黄频| 欧美zozozo另类| 国产精品一二三区在线看| 成人一区二区视频在线观看| 国产精品综合久久久久久久免费| 99在线人妻在线中文字幕| 嫩草影院入口| 又爽又黄a免费视频| 国产成人freesex在线 | 亚洲图色成人| 精品福利观看| 久久婷婷人人爽人人干人人爱| 搡老妇女老女人老熟妇| 国产91av在线免费观看| 网址你懂的国产日韩在线| 亚洲精品日韩av片在线观看| 精品免费久久久久久久清纯| 亚洲av不卡在线观看| 亚洲欧美成人精品一区二区| 婷婷精品国产亚洲av在线| 国产成人福利小说| 午夜精品在线福利| 国产成人a区在线观看| 国产老妇女一区| 男人舔女人下体高潮全视频| 亚洲精品影视一区二区三区av| 如何舔出高潮| 老熟妇乱子伦视频在线观看| 久久婷婷人人爽人人干人人爱| 丝袜美腿在线中文| 亚洲图色成人| 精品不卡国产一区二区三区| 久久精品国产清高在天天线| 禁无遮挡网站| 久久久a久久爽久久v久久| 人人妻人人澡人人爽人人夜夜 | 最近2019中文字幕mv第一页| 亚洲av中文字字幕乱码综合| 人人妻,人人澡人人爽秒播| 色哟哟·www| 欧美色视频一区免费| 日本一本二区三区精品| 国产高潮美女av| 亚洲18禁久久av| 高清毛片免费观看视频网站| 成人综合一区亚洲| 麻豆久久精品国产亚洲av| 国产精品,欧美在线| 精品久久久久久久末码| 一本精品99久久精品77| 日本黄大片高清| 久久久久久久久久黄片| 国产人妻一区二区三区在| 天堂网av新在线| 欧美三级亚洲精品| 有码 亚洲区| 国产淫片久久久久久久久| 午夜精品一区二区三区免费看| 国产精品久久久久久久电影| 国产精品三级大全| 熟女人妻精品中文字幕| 亚洲性久久影院| 亚洲精品亚洲一区二区| 听说在线观看完整版免费高清| 日韩 亚洲 欧美在线| 99精品在免费线老司机午夜| 自拍偷自拍亚洲精品老妇| a级毛片免费高清观看在线播放| 三级毛片av免费| 国产精品人妻久久久久久| 国产精品久久久久久亚洲av鲁大| 狠狠狠狠99中文字幕| 亚洲精品456在线播放app| 色5月婷婷丁香| 村上凉子中文字幕在线| 国产高清有码在线观看视频| 亚洲精品亚洲一区二区| 69人妻影院| 成年av动漫网址| 黄色日韩在线| 日韩制服骚丝袜av| 一级毛片我不卡| 国产在视频线在精品| 国产老妇女一区| 日韩三级伦理在线观看| 秋霞在线观看毛片| 黄色一级大片看看| 国产高清激情床上av| 久久韩国三级中文字幕| 亚洲人成网站高清观看| 亚洲一区二区三区色噜噜| 亚洲内射少妇av| 国产精品美女特级片免费视频播放器| 内射极品少妇av片p| 成人三级黄色视频| 国产精品久久久久久av不卡| 午夜精品一区二区三区免费看| 亚洲成人久久性| 床上黄色一级片| 熟女人妻精品中文字幕| 少妇熟女aⅴ在线视频| 国产不卡一卡二| 欧美成人a在线观看| 别揉我奶头 嗯啊视频| 波野结衣二区三区在线| 国产精品人妻久久久影院| 精品欧美国产一区二区三| 国产伦精品一区二区三区四那| av在线观看视频网站免费| 搡老妇女老女人老熟妇| 最近最新中文字幕大全电影3| 精品一区二区三区人妻视频| 天美传媒精品一区二区| 日本一本二区三区精品| 亚洲精品日韩av片在线观看| 最近手机中文字幕大全| 成人永久免费在线观看视频| 一进一出好大好爽视频| 麻豆乱淫一区二区| 精品福利观看| 91久久精品国产一区二区三区| 免费看av在线观看网站| 成年女人看的毛片在线观看| 国产精品爽爽va在线观看网站| 国产69精品久久久久777片| 欧美激情久久久久久爽电影| 日本精品一区二区三区蜜桃| 成人二区视频| 免费在线观看影片大全网站| 国产精品爽爽va在线观看网站| 亚洲欧美精品综合久久99| 亚洲精品一卡2卡三卡4卡5卡| 亚洲18禁久久av| 99热全是精品| av在线亚洲专区| 日产精品乱码卡一卡2卡三| 2021天堂中文幕一二区在线观| 老熟妇乱子伦视频在线观看| 日韩人妻高清精品专区| 丰满人妻一区二区三区视频av| 久久国内精品自在自线图片| 成人一区二区视频在线观看| 国产精品一区二区性色av| 亚洲美女黄片视频| 亚洲成人av在线免费| 99热只有精品国产| 六月丁香七月| 国产v大片淫在线免费观看| 搞女人的毛片| 亚洲av中文av极速乱| 免费不卡的大黄色大毛片视频在线观看 | 色av中文字幕| 三级男女做爰猛烈吃奶摸视频| 国产亚洲91精品色在线| 成年女人毛片免费观看观看9| 婷婷亚洲欧美| 91av网一区二区| 九九久久精品国产亚洲av麻豆| 国产成人影院久久av| 看黄色毛片网站| 99国产极品粉嫩在线观看| 免费人成视频x8x8入口观看| 久久久久久久久久久丰满| 成人毛片a级毛片在线播放| 欧美一区二区国产精品久久精品| 精品无人区乱码1区二区| 欧美激情国产日韩精品一区| av在线观看视频网站免费| 天天躁日日操中文字幕| 免费观看精品视频网站| 一a级毛片在线观看| 性插视频无遮挡在线免费观看| 免费观看精品视频网站| 免费看a级黄色片| 中国美女看黄片| 亚洲在线自拍视频| 日韩精品有码人妻一区| 最近手机中文字幕大全| 天天一区二区日本电影三级| 亚州av有码| 最新在线观看一区二区三区| .国产精品久久| 丰满乱子伦码专区| 亚洲av不卡在线观看| 人妻夜夜爽99麻豆av| 国产一区二区在线av高清观看| 国产成人aa在线观看| 少妇高潮的动态图| 男女边吃奶边做爰视频| 日韩欧美国产在线观看| 国内少妇人妻偷人精品xxx网站| 最近中文字幕高清免费大全6| 中文字幕免费在线视频6| 身体一侧抽搐| 最近视频中文字幕2019在线8| 晚上一个人看的免费电影| 白带黄色成豆腐渣| 色哟哟·www| 夜夜夜夜夜久久久久| 九九在线视频观看精品| 精品久久久久久久久av| 蜜桃久久精品国产亚洲av| 小说图片视频综合网站| 国产一区二区三区在线臀色熟女| 欧美高清性xxxxhd video| 日本免费一区二区三区高清不卡| 日日干狠狠操夜夜爽| 成人综合一区亚洲| 国产一区二区三区av在线 | 欧美色欧美亚洲另类二区| 亚洲欧美成人精品一区二区| 精品久久久久久久久av| 欧美中文日本在线观看视频| 国产精品99久久久久久久久| 国产午夜精品久久久久久一区二区三区 | 又爽又黄无遮挡网站| 亚洲国产精品合色在线| 亚洲国产欧美人成| 色av中文字幕| 亚洲欧美日韩无卡精品| 最近手机中文字幕大全| 久久久久国产网址| 亚洲无线在线观看| 大又大粗又爽又黄少妇毛片口| 97碰自拍视频| 午夜精品在线福利| 欧美+日韩+精品| 日韩三级伦理在线观看| 晚上一个人看的免费电影| 日本免费一区二区三区高清不卡| 国产精品久久视频播放| 两性午夜刺激爽爽歪歪视频在线观看| 久久中文看片网| 极品教师在线视频| 插逼视频在线观看| 国产黄色小视频在线观看| 国内久久婷婷六月综合欲色啪| 亚洲精品日韩在线中文字幕 | 欧美在线一区亚洲| 亚洲人成网站在线观看播放| 婷婷六月久久综合丁香| 国产中年淑女户外野战色| h日本视频在线播放| 99国产极品粉嫩在线观看| 亚洲精品国产成人久久av| 欧美国产日韩亚洲一区| 1000部很黄的大片| 亚洲精品国产av成人精品 | 俄罗斯特黄特色一大片| 免费黄网站久久成人精品| 国产高清视频在线播放一区| 日本a在线网址| 啦啦啦韩国在线观看视频| 午夜福利高清视频| 观看美女的网站| 午夜久久久久精精品| 五月伊人婷婷丁香| 日韩 亚洲 欧美在线| 国产白丝娇喘喷水9色精品| 亚州av有码| 一卡2卡三卡四卡精品乱码亚洲| 免费av不卡在线播放| 中文字幕熟女人妻在线| 亚洲国产精品国产精品| 亚洲成人精品中文字幕电影| 插阴视频在线观看视频| 国内精品一区二区在线观看| 综合色av麻豆| 成人美女网站在线观看视频| 日韩制服骚丝袜av| 一级av片app| 又粗又爽又猛毛片免费看| 听说在线观看完整版免费高清| 最新在线观看一区二区三区| 欧美日韩国产亚洲二区| 日韩av不卡免费在线播放| 麻豆国产97在线/欧美| 99riav亚洲国产免费| 国产又黄又爽又无遮挡在线| 身体一侧抽搐| 亚洲熟妇中文字幕五十中出| 别揉我奶头~嗯~啊~动态视频| 免费一级毛片在线播放高清视频| 成年女人看的毛片在线观看| 国产精品一区二区三区四区久久| 亚洲国产精品成人久久小说 | 欧美另类亚洲清纯唯美| 又黄又爽又免费观看的视频| 日韩制服骚丝袜av| 午夜福利在线观看吧| 久久久久久久久久成人| 深夜精品福利| 淫妇啪啪啪对白视频| 五月伊人婷婷丁香| 性欧美人与动物交配| 不卡一级毛片| 最近在线观看免费完整版| 日韩欧美在线乱码| 97超视频在线观看视频| 丝袜喷水一区| 亚洲一级一片aⅴ在线观看| 国产精品美女特级片免费视频播放器| 国产熟女欧美一区二区| 亚洲aⅴ乱码一区二区在线播放| 在线播放无遮挡| 床上黄色一级片| 亚洲国产精品久久男人天堂| 最新中文字幕久久久久| 又爽又黄无遮挡网站| 国产成人精品久久久久久| 69av精品久久久久久| 亚洲性久久影院| 久久人人爽人人爽人人片va| 国内精品久久久久精免费| 精品人妻视频免费看| 在线观看美女被高潮喷水网站| 日韩中字成人| 激情 狠狠 欧美| 欧美3d第一页| 人妻制服诱惑在线中文字幕| 日本与韩国留学比较| 观看美女的网站| av专区在线播放| 99国产极品粉嫩在线观看| 91在线精品国自产拍蜜月| 最近的中文字幕免费完整| 看免费成人av毛片| 99热只有精品国产| 99riav亚洲国产免费| 成人综合一区亚洲| 日本与韩国留学比较| 久久午夜福利片| 尾随美女入室| 菩萨蛮人人尽说江南好唐韦庄 | 91精品国产九色| 你懂的网址亚洲精品在线观看 | 白带黄色成豆腐渣| 色综合亚洲欧美另类图片| 欧美激情在线99| 日韩在线高清观看一区二区三区| 色噜噜av男人的天堂激情| 嫩草影院入口| 天堂av国产一区二区熟女人妻| 一进一出好大好爽视频| 亚洲成a人片在线一区二区| 色哟哟哟哟哟哟| 69av精品久久久久久| 国产亚洲精品av在线| 国产精品国产三级国产av玫瑰| 午夜福利成人在线免费观看| 国产爱豆传媒在线观看| 高清毛片免费观看视频网站| 搡老熟女国产l中国老女人| 国产av不卡久久| 亚洲av不卡在线观看| 亚洲成人av在线免费| 搡老妇女老女人老熟妇| 天堂网av新在线| 九九久久精品国产亚洲av麻豆| 成人性生交大片免费视频hd| 在线a可以看的网站| 日本五十路高清| 毛片女人毛片| 日韩,欧美,国产一区二区三区 | 亚洲人成网站在线播| 成人亚洲欧美一区二区av| 美女黄网站色视频| 国产成人aa在线观看| 国产白丝娇喘喷水9色精品| 国产精品国产三级国产av玫瑰| 别揉我奶头~嗯~啊~动态视频| 搞女人的毛片| 国产蜜桃级精品一区二区三区| 热99re8久久精品国产| 日韩国内少妇激情av| 国产蜜桃级精品一区二区三区| 一级黄片播放器| 黄色一级大片看看| 草草在线视频免费看| 狂野欧美白嫩少妇大欣赏| 搡老熟女国产l中国老女人| 深夜精品福利| 夜夜夜夜夜久久久久| av天堂中文字幕网| 亚洲av熟女| 欧美日韩国产亚洲二区| 亚洲18禁久久av| 久久久国产成人精品二区| 亚洲专区国产一区二区| 日本精品一区二区三区蜜桃| 乱系列少妇在线播放| 国产精品国产高清国产av| 免费电影在线观看免费观看| 能在线免费观看的黄片| 黄色配什么色好看| 亚洲av.av天堂| 日本黄色片子视频| 九九在线视频观看精品| 综合色av麻豆| 中文字幕人妻熟人妻熟丝袜美| 国产高清视频在线播放一区| 欧美成人a在线观看| 欧美最黄视频在线播放免费| 91av网一区二区| av女优亚洲男人天堂| 日日摸夜夜添夜夜添av毛片| 成人国产麻豆网| 国产麻豆成人av免费视频| 国产伦在线观看视频一区| 久久综合国产亚洲精品| 日韩国内少妇激情av| 性插视频无遮挡在线免费观看| 黄色一级大片看看| 国产精华一区二区三区| 亚洲一区二区三区色噜噜| 最近在线观看免费完整版| 亚洲精品亚洲一区二区| 麻豆乱淫一区二区| avwww免费| 桃色一区二区三区在线观看| 寂寞人妻少妇视频99o| 亚洲av中文av极速乱| 男人舔女人下体高潮全视频| 久久天躁狠狠躁夜夜2o2o| 少妇的逼水好多| 99久久中文字幕三级久久日本| 女人被狂操c到高潮| 全区人妻精品视频| 91久久精品国产一区二区三区| 亚洲人成网站高清观看| 男人舔女人下体高潮全视频| 在线免费观看不下载黄p国产| 欧美区成人在线视频| 日本免费a在线| 最近最新中文字幕大全电影3| 2021天堂中文幕一二区在线观| 午夜精品在线福利| 天天一区二区日本电影三级| 久久精品综合一区二区三区| 国产乱人偷精品视频| 欧美日韩在线观看h| 午夜精品在线福利| 少妇高潮的动态图| 一级毛片我不卡| 亚洲电影在线观看av| 狂野欧美白嫩少妇大欣赏| 国产 一区精品| 啦啦啦啦在线视频资源| 日韩制服骚丝袜av| 国产一区亚洲一区在线观看| 无遮挡黄片免费观看| 两个人视频免费观看高清| 国产av麻豆久久久久久久| 搡女人真爽免费视频火全软件 | 91久久精品国产一区二区成人| 尤物成人国产欧美一区二区三区| ponron亚洲| 俄罗斯特黄特色一大片| 欧洲精品卡2卡3卡4卡5卡区| 国产高清视频在线播放一区| 中文字幕熟女人妻在线| 观看免费一级毛片| 五月伊人婷婷丁香| 亚洲国产色片| 永久网站在线| 少妇猛男粗大的猛烈进出视频 | 插阴视频在线观看视频| 一个人看视频在线观看www免费| 亚洲性夜色夜夜综合| 淫妇啪啪啪对白视频| 日韩欧美三级三区| 日本三级黄在线观看| 国产高清激情床上av| 亚洲一区高清亚洲精品| 波多野结衣高清无吗| 99久国产av精品国产电影| 国产精品久久久久久久电影| 女人十人毛片免费观看3o分钟| 中文字幕av在线有码专区| 男女边吃奶边做爰视频| 国产探花在线观看一区二区| 国产国拍精品亚洲av在线观看| 亚洲av成人精品一区久久| 精品乱码久久久久久99久播| 亚洲图色成人| www.色视频.com| 国产精品久久电影中文字幕| 在线观看一区二区三区| 国产单亲对白刺激| 美女免费视频网站| 又爽又黄无遮挡网站| 美女大奶头视频| 成年免费大片在线观看| 村上凉子中文字幕在线| 99在线视频只有这里精品首页| 亚洲欧美精品自产自拍| 久久韩国三级中文字幕| 亚洲国产日韩欧美精品在线观看| 国产一区亚洲一区在线观看| 蜜桃久久精品国产亚洲av| 午夜福利在线在线| 亚洲人成网站高清观看| 亚洲精品日韩在线中文字幕 | 国产精品女同一区二区软件| 国产探花在线观看一区二区| 五月玫瑰六月丁香| 别揉我奶头 嗯啊视频| 精品国产三级普通话版| 成年女人毛片免费观看观看9| 国产精品美女特级片免费视频播放器| 永久网站在线| 一边摸一边抽搐一进一小说| 国产伦在线观看视频一区| 俄罗斯特黄特色一大片| 啦啦啦观看免费观看视频高清| 亚洲av美国av| 国产在视频线在精品| 色吧在线观看| 蜜桃久久精品国产亚洲av| 免费av毛片视频| 高清毛片免费看| 丰满的人妻完整版| 欧美成人免费av一区二区三区| 3wmmmm亚洲av在线观看| 亚洲av不卡在线观看| 最新中文字幕久久久久| 国产人妻一区二区三区在| 女的被弄到高潮叫床怎么办| 亚洲第一电影网av| 久久欧美精品欧美久久欧美| 99久国产av精品国产电影| 欧美绝顶高潮抽搐喷水| а√天堂www在线а√下载| 日韩在线高清观看一区二区三区| 免费大片18禁| 亚洲无线观看免费| 日韩欧美免费精品| 91狼人影院| 亚洲熟妇熟女久久| 亚洲丝袜综合中文字幕| 丰满人妻一区二区三区视频av| 亚洲欧美精品综合久久99| 身体一侧抽搐| 女生性感内裤真人,穿戴方法视频| 国产成人a区在线观看| 九九热线精品视视频播放| 日韩欧美在线乱码| 日本a在线网址| 久久久欧美国产精品| 亚洲av第一区精品v没综合| 黄色一级大片看看| 日韩欧美三级三区| 亚洲在线观看片| 亚洲最大成人av| 又黄又爽又刺激的免费视频.| 搡女人真爽免费视频火全软件 | 99精品在免费线老司机午夜| 丰满人妻一区二区三区视频av| 亚洲欧美日韩高清在线视频| 我的女老师完整版在线观看| 最近最新中文字幕大全电影3| 精品一区二区免费观看| 男女那种视频在线观看| 日韩制服骚丝袜av| 久久久久久久亚洲中文字幕| 我的女老师完整版在线观看| 久久久久久久亚洲中文字幕| 色综合亚洲欧美另类图片| 亚洲不卡免费看| 国产精品,欧美在线| 天堂影院成人在线观看| 日日撸夜夜添| 精品人妻一区二区三区麻豆 | 亚洲av熟女| av福利片在线观看| 中国美女看黄片| 人妻夜夜爽99麻豆av| 男人的好看免费观看在线视频| 国产极品精品免费视频能看的| 久久午夜福利片| 三级男女做爰猛烈吃奶摸视频| 91久久精品国产一区二区成人| 成年女人看的毛片在线观看| 国产精品一区www在线观看| 国产精品久久久久久亚洲av鲁大| 精品人妻熟女av久视频| 国产爱豆传媒在线观看| 美女 人体艺术 gogo| 波多野结衣高清无吗| 亚洲成人久久爱视频| 国产三级中文精品| 晚上一个人看的免费电影| 在线观看一区二区三区| 老师上课跳d突然被开到最大视频| 免费av毛片视频| 啦啦啦观看免费观看视频高清| 女生性感内裤真人,穿戴方法视频| 亚洲国产日韩欧美精品在线观看|