    An Investigation of Creep Resistance in Grade 91 Steel through Computational Thermodynamics

    2020-09-05 07:41:38AndrewSmithMohmmdAsdikiyMeiYngJiuhuChenYuZhong
    Engineering 2020年6期

    Andrew Smith, Mohmmd Asdikiy,, Mei Yng, Jiuhu Chen, Yu Zhong,,*

    a Department of Mechanical and Materials Engineering, Florida International University, Miami, FL 33174, USA

    b Mechanical Engineering Department, Worcester Polytechnic Institute, Worcester, MA 01609, USA

    Keywords:

    Grade 91 steel Creep resistance Ferritic-martensitic steels Welding microstructure Computational thermodynamics Secondary phase Alloy composition

    A B S T R A C T

    This study was conducted to understand the relationship between various critical temperatures and the stability of the secondary phases inside the heat-affected-zone (HAZ) of welded Grade 91 (Gr.91) steel parts. Type IV cracking has been observed in the HAZ, and it is widely accepted that the stabilities of the secondary phases in Gr.91 steel are critical to the creep resistance,which is related to the crack failure of this steel.In this work,the stabilities of the secondary phases,including those of the M23C6,MX,and Z phases, were simulated by computational thermodynamics. Equilibrium cooling and Scheil simulations were carried out in order to understand the phase stability in welded Gr.91 steel.The effect of four critical temperatures—that is, Ac1 (the threshold temperature at which austenite begins to form), Ac3 (the threshold temperature at which ferrite is fully transformed into austenite), and the M23C6 and Z phase threshold temperatures—on the thickness of the HAZ and phase stability in the HAZ is discussed.Overall, the simulations presented in this paper explain the mechanisms that can affect the creep resistance of Gr.91 steel,and can offer a possible solution to the problem of how to increase creep resistance at elevated temperatures by optimizing the steel composition, welding, and heat treatment process parameters. The simulation results from this work provide guidance for future alloy development to improve creep resistance in order to prevent type IV cracking.

    1. Introduction

    Grade 91(Gr.91)steel is a high-chromium(Cr)ferritic-martensitic structural steel that was originally produced by Oak Ridge National Laboratory in the 1970s, and that has been extensively utilized by the power industries, most notably for thick-section boiler components [1]. This alloy steel has high creep resistance,due to the formation of fine secondary-phase M23C6and MX particles in the matrix and grain boundaries. However, past studies have established that there are two possible mechanisms of premature creep failure, which cause the formation of type IV cracks along the heat-affected-zone (HAZ) that can be observed under short-term or long-term creep tests. Short-term creep tests are performed at higher temperatures and under high stresses, while long-term creep tests are optimized for longer periods of time with lower temperatures and low stresses. The first mechanism of premature creep failure is the coarsening of M23C6at high temperature and high stress,which occurs during short-term creep testing [2-4]. M23C6is viewed as a beneficial phase in the initial microstructure, due to its fine particle size. However, volume percentage increase and particle size coarsening of M23C6are typically observed during or after heat treatment, changing M23C6into a secondary phase that is detrimental for creep resistance. The second mechanism is the precipitation of the detrimental Z phase;this occurs under the low temperature and low stress of long-term tests [3,5-7], and ‘‘eats” away the fine MX particles.

    Decades of research on the issue of creep failure in Gr.91 steel have involved extensive thermodynamic, kinetic, and crystallographic investigations, most of which have focused on direct simulations of creep failure[3,8,9].However, very few fundamental investigations have been conducted on the stabilities of the critical secondary phases,which are directly linked to the creep resistance of this steel, even though computational thermodynamics is widely accepted as an extremely useful means of providing predictions and guidance for the design of new alloys—and especially of steels. To address this issue, a thermodynamic investigation of Gr.91 steel was carried out in order to examine the relationship between various critical temperatures and the stabilities of the M23C6,MX,and Z phases within the HAZ,which can be used to predict and improve the creep resistance under both short-term and long-term applications. This investigation paves the way for a comprehensive understanding of how to optimize the alloy composition to improve the creep resistance.

    2. Literature review

    2.1. Type IV cracks and creep resistance in Gr.91 steel

    Creep resistance degradation is considered to be the main reason for type IV cracks in welded Gr.91 steel, which occurs under repeated cyclic loading.These cracks are mostly observed to occur along the outer edge of the HAZ—more specifically, in the finegrain HAZ (FGHAZ) and intercritical HAZ (ICHAZ) (Fig.1), which are created by the welding process and will be explained in further detail below. Various works have been carried out in order to understand the formation mechanism of type IV cracks and to propose a method to suppress these cracks. However, the exact mechanism leading to critical failure along the HAZ is still unknown, although many suggestions have been made [10-15].From a thermodynamic viewpoint, it has been observed that secondary phases, such as the M23C6, MX, and Z phases, not only change the microstructure of the HAZ, but also directly affect the alloys’ failure under long-term and short-term applications. The formation and stability of secondary phases are determined by the alloy composition, welding process parameters such as the temperature gradient, and the alloy’s application conditions.Therefore, thermodynamic simulations are an effective approach to investigate the formation and stability of the secondary phases,which could lead to the determination of the underlying mechanism of type IV cracks.

    2.2. Microstructure of the HAZ

    The HAZ is considered to be the most likely place for premature creep failure, since it has been widely observed to form type IV cracks.Three main factors affect the microstructure evolution of the HAZ and its subzones: ①the peak welding temperatures, ②the Ac1 and Ac3 temperatures (defined below), and ③the formation and dissolution of M23C6carbides [15,16]. The MX phase is not considered during the formation of the HAZ because it does not dissolve or destabilize during welding[17].Studies have shown that its changes are much smaller,due to its high thermal stability,small coarsening,and fine distribution within the microstructure[17,18].Therefore, the phase stability and coarsening of M23C6are the primary focus in most studies on the HAZ formation.

    Fig.1. Schematic microstructure of the HAZ and its three subzones formed during the welding process: the coarse-grain HAZ (CGHAZ), FGHAZ, and ICHAZ.

    Fig.1 shows the schematic microstructure of the HAZ and the location of its three subzones in Gr.91 steel. After the welding process, Gr.91 steel has been observed to form three subzones within the HAZ:the coarse-grain HAZ(CGHAZ),FGHAZ,and ICHAZ.It is widely accepted that the microstructure of the HAZ is closely related to the two Ac temperatures,Ac1 and Ac3.The Ac1 temperature is defined as the temperature at which austenite begins to form, whereas the Ac3 temperature is the temperature at which austenite transformation is completed. The first zone next to the weld metal is the CGHAZ, which is located near the fusion line.In this zone, the peak temperature during welding is above Ac3,and is also higher than the M23C6stability temperature region. In the CGHAZ, M23C6particles on the grain boundary dissolve into the matrix,which reduces the pinning force,leading to coarsening of the grains. In the FGHAZ, which is next to the CGHAZ, the peak temperature is also above the Ac3, but lies within the M23C6stability temperature region. Therefore, the M23C6particles on the grain boundary cannot dissolve into the matrix.Thus,very fine grain size is observed in the FGHAZ due to the grain boundary pinning effect from M23C6.

    The ICHAZ, which is the smallest of the three zones, is located furthest from the fusion line and has a peak temperature between Ac1 and Ac3. This zone differs from the other two zones in that upon cooling, a mixture of fresh martensite and ferrite forms,whereas the CGHAZ and the FGHAZ contain mostly martensite upon cooling. Hence, from a thermodynamic perspective, the M23C6stability region and the Ac temperatures are considered to be the critical factors determining the microstructure of the HAZ subzones. The Ac3 temperature determines the boundary location between the CGHAZ and FGHAZ, and the Ac1 temperature determines the boundary location between the ICHAZ and the over-tempered region.

    2.3. Long-term creep failure

    Long-term creep tests of Gr.91 steel are defined as tests of a material’s creep life expectancy that last for 100 000 h or more,with the preferred stresses for testing being below 100 MPa[5,7,18-20]. In these tests, the testing temperature will be as low as 550 °C [5,7]. It has been observed that the Z phase will eventually form and reduce the creep resistance of the material[21].The Z phase has been particularly studied in the last few decades,and it has been found that its formation can lead to a decrease of the fine MX carbonitrides (M(C,N)) and to the disappearance of niobium(Nb)-rich (NbX) MX phases [22,23], both of which are considered to be beneficial to the material’s creep strength within the HAZ.It is believed that the formation of the Z phase within the steel determines the premature creep resistance damage during longterm operations.

    2.4. Short-term creep failure

    To investigate the creep resistance mechanism over a short time period, speed-up failure creep tests were designed. For example,the total creep life resulting in short-term failure can vary from 100 to 1000 h at temperatures between 575 and 650 °C [24] and under high stresses between 100 and 200 MPa, depending on the heat-treatment conditions prior to testing [3,24]. The main observation is that the increase and coarsening of M23C6particles influence the microstructure in the HAZ, and can lower the creep resistance.

    Many factors have been observed to affect the coarsening of M23C6, including the presence of creep voids in the HAZ [25-27]and neutron irradiation [28-31]. However, the mechanism of the coarsening of M23C6has been best described based on the Ostwald ripening effect [20,32-35], which is considered to be the last stage of precipitation and is mainly dependent on the working temperature of the material. Higher temperatures correspond to a higher coarsening rate of M23C6.

    2.5. Elements pertaining to Gr.91 secondary phases

    Understanding the composition of the secondary phases and the role of each element in contributing to the formation of secondary phases such as the M23C6,MX,and Z phases is necessary in order to study the different mechanisms of creep resistance degradation in Gr.91 steel at various operation temperatures. The typical concentration of each element and their tolerances under the American Society of Mechanical Engineers (ASME) standards[36] in the material are provided in Table 1. The ‘‘M” in M23C6carbides represents the metals Cr, iron (Fe), or molybdenum (Mo),while the ‘‘M” in MX represents vanadium (V) or Nb. The ‘‘X” in MX represents carbon (C) or nitrogen (N), and has been observed to vary throughout the material, making these phases carbides(MC), nitrides (MN), or carbonitrides (M,(C,N)) [37]. The Z phase forms at lower temperatures over the long-term usage of the material[5].Its crystal structure has three different sites—(Fe,Cr)(Mo,V,Nb)(N,Va)—where Va stands for vacancies. This paper adapts the notation of Cr(V,Nb)N for the Z phase for ease of comprehension,since the Fe and Mo concentrations are extremely low.

    In general, the elements in Gr.91 steel can be grouped into two categories—ferrite (α-Fe) stabilizers and austenite (γ-Fe)stabilizers—which affect both the Ac temperatures and the stability of the secondary phases.α-Fe stabilizers are elements added to the steel alloy that have a large solubility in the α-Fe phase, thereby increasing the alloy’s Ac temperatures;in contrast,γ-Fe stabilizers have a large solubility in the γ-Fe phase,thereby decreasing the Ac temperatures. C and N are both γ-Fe stabilizers [38], and are both essential to the stabilities of the MX and M23C6precipitates that form and coarsen during the normalization and tempering process of the heat treatment. Cr, which is an α-Fe stabilizer [38], is the most important element in the alloy. At sufficiently large concentrations, Cr can prevent oxidation and corrosion under aqueous conditions.Cr is the essential element in the creation of the carbide M23C6that makes up most of the secondary phases that form during the initial stages of heat treatment. Other precipitates also form, such as the M7C3(Cr7C3) and M2X (Cr2N) precipitates, if changes are made to the composition[38,39].Mo is an α-Fe stabilizer that provides a solid solution for the M23C6(Mo23C6)carbides[38]. A limited amount needs to be added in order to prevent an abundance of both Laves phase(Fe,Cr)2(Mo,W)and δ-phase formation[37].At low amounts of Cr,M2C(Mo2C)can form[39].Lastly,V and Nb(which are γ-Fe stabilizers[38])are strong suppliers to the formation of MX, especially in Gr.91 steel. MX precipitates are extremely stable even at temperatures higher than the normalization process temperature, which makes them difficult to produce but beneficial in improving the creep resistance.

    3. Thermodynamic investigation

    To determine the stability of the critical secondary phases in Gr.91—that is, the M23C6, MX, and Z phases—the calculation of phase diagrams (CALPHAD) approach based on computational thermodynamics was utilized by using Thermo-Calc and its corresponding TCFE8 database. The CALPHAD approach was first developed by Kaufman [40] to model complex multicomponent materials and their corresponding equilibrium phases. The basic concept of CALPHAD is to gather and analyze thermodynamic data from individual phases and use this data to predict the properties of materials under a wide range of temperatures, pressures, and compositional conditions [41-48].

    The chemical composition of the Gr.91-based system is shown in Table 1. Here, the weight percentage of each element under ASME standards [36] is compared with the composition chosen for the current simulations. The alloy consists of more than 13 elements; however, only the most critical elements were selected in the current thermodynamic simulations, especially for the prediction of the stability of the secondary phases. Therefore, an Fe-Cr-C-V-Nb-Mo-N (Gr.91-based system) alloy was chosen as the base material for the investigation.

    3.1. Isopleth diagrams of the Gr.91-based system

    Fig.2 shows the isopleth diagrams of the Gr.91-based system with changes in the carbon concentration. More specifically,Fig.2(a)is the isopleth diagram for a C concentration ranging from 0 to 0.2 wt% at temperatures between 600 and 1600 °C, whereas Fig.2(b)is the diagram for 0-0.15 wt%of C at 700-1000°C.The isopleth diagrams show the phase stability region for the α and γ matrix phases along with the critical secondary phases, including the MX phase, M23C6phase, and Z phase.

    It is worth noting that the MX phase has the same facecentered cubic (fcc) crystal structure as the matrix γ phase. However, the Gibbs energy of the MX has a miscibility gap, which means that two fcc MX phases with different compositions can be formed within a specific temperature region.This finding agrees well with the experimental observations for this particular family of alloys [49-53]. A more detailed discussion on the Gibbs energy of the MX phases and the matrix γ phase is provided in the subsection below. The MX phase can be described as a solid solution phase with two sublattices: (V,Nb)(C,N). The first sublattice is mainly occupied with V and Nb, while C and N occupy the second sublattice. In the current work, MX1 is used to describe the MX phase, which has a higher site fraction of N than C in the second sublattice.MX2 is used to describe the phase in which the site fraction of C is higher than that of N in the second sublattice.

    Detailed simulations have been done to show that the composition of the M23C6phase—that is, (Cr,Fe,Mo)23C6—does not change much in this steel alloy;this phase has Cr as the dominant element in the first sublattice, and forms in the lower temperature region[38]. The Z phase—that is, (Fe,Cr)(Mo,V,Nb)(N,Va)—forms at even lower temperatures; its composition does not change much, and Cr and V are always the dominant elements in the first and the second sublattices, respectively [23].

    At 0.05 wt% of C, the first secondary phase that is precipitated out during the temperature change from 1243 to 896 °C is the MX1 phase. When the temperature drops to the Ac3 temperature(896 °C), the γ phase starts to transform into the α phase. As the temperature decreases further, the other two secondaryphases—that is, the M23C6phase and Z phase—become stable. It should be noted that in regions with a carbon concentration higher than 0.1 wt%, two types of MX phases—MX1 and MX2—become stable due to the miscibility gap. For example, with an increase in carbon concentration, the stable phases change from γ + MX1 to γ + MX1 + MX2 around 0.155 wt% of C at 1000 °C, as shown in Fig.2(a).

    StatusElements (wt%)CrCVNbMoNMnPSSiAlTiZr ASME standard 0.01(max)Simulation8.750.100.2150.080.950.05——7.90-9.60 0.06-0.15 0.16-0.27 0.05-0.11 0.80-1.10 0.025-0.080 0.25-0.66 0.025(max)0.012(max)0.18-0.56 0.02(max)0.01(max)

    Fig.2. Phase diagrams of the Gr.91-based system, with the Ac1 (blue) and Ac3 (red) temperatures highlighted. (a) Overall phase diagram of the Gr.91-based system for temperature ranges of 600-1600 °C at a range of 0-0.2 wt% of C; (b) close-up of the phase diagram at temperature ranges of 700-1000 °C and 0-0.15 wt% of C.

    3.2. Gibbs energy of the fcc structure (γ phase and MX phase)

    In the CALPHAD approach, a single Gibbs energy description is typically used to describe the phases that share the same crystal structure [23]. As mentioned above, the γ, MX1, and MX2 phases all have the fcc structure. The MX phase is considered to be beneficial for creep resistance because it is thermodynamically more stable and has a very low coarsening rate in comparison with M23C6under short-term applications [38]. Therefore, it is worthwhile to take a closer look at this phase. Fig.3 shows the Gibbs energies of the γ, MX1, and MX2 phases at 1000 °C. It can be seen that the Gibbs energies of these three phases are very different,even though the phases share the same crystal structure. In the region with less than 0.15 wt%of C,γ and MX1 are the only stable phases, while MX2 becomes stable in the region with a higher C concentration. This result clearly explains the phase transformation shown at 1000 °C in Fig.2(a).

    Fig.3. Gibbs energy of the γ, MX1, and MX2 phases in the Gr.91-based system at 1000 °C from 0 to 0.20 wt% of C.

    3.3. Ac1 minimum austenite transformation temperature and Ac3 threshold ferrite temperature

    The two Ac temperatures—Ac1 and Ac3—are critical in understanding the phase stabilities and the microstructure evolution in the HAZ. In particular, the Ac3 temperature determines the boundary between the FGHAZ and ICHAZ,and the Ac1 temperature determines the boundary between the ICHAZ and the overtempered region, as discussed above (Fig.1). Therefore, these two Ac temperatures are closely linked with the formation of type IV cracks, making it worthwhile to investigate the factors that affect them. Fig.4 shows the change of the Ac1 and Ac3 temperatures in the Gr.91-based system (solid lines) in comparison with a Fe-C binary system (dashed lines).

    With an increase in the carbon concentration, as shown in Fig.4(a), the Ac1 temperature of the Gr.91-based system drops from 890 to 830 °C, with the biggest difference happening in the beginning, up to 0.01 wt% of C, and then gradually decreasing afterwards. Similar behavior is seen for the Fe-C binary system;however, the sudden change happens at a slightly higher carbon concentration and drops from 910 to 738 °C. This sudden change in both systems is due to the phase transformation. The Ac1 temperature from the Gr.91-based system is generally much higher than that from the Fe-C system. This major difference indicates that the alloying elements in Gr.91 greatly increase the Ac1 temperature. Fig.4(b) shows the Ac3 temperature vs. the carbon concentration. The temperature drops from 954 °C for 0 wt% of C to 850 °C for 0.2 wt% of C for the Gr.91-based system,whereas it drops from 910 to 837 °C for the Fe-C system. Similar to Fig.4(a), the slope change in the curve for the Gr.91-based system at around 0.08 wt%of C represents a phase transformation from α+γ+MX1+MX2+M23C6to α+γ+MX1+M23C6.A linear relationship is observed for the Fe-C binary system,because there is no phase transformation—that is,α and γ are the only two stable phases in this temperature range.Overall,these findings show that Gr.91 shares similar Ac3 temperatures with the Fe-C binary system in the typical C concentration range for Gr.91—that is, for about 0.1 wt% of C.

    Fig.4. (a)Ac1 and(b)Ac3 temperatures(°C)vs.weight percentage of C for the Gr.91-based system simulation(solid line)in comparison with the Ac temperatures of the Fe-C binary system (dashed line).

    3.4. Mole/site fraction of secondary phases under the equilibrium condition

    Fig.5 shows the mole fraction of the secondary phases—that is, the M23C6, MX, and Z phases—in the temperature range between 600 and 1400 °C for the Gr.91-based steel. It can be seen that the MX1 phase is stable between 770 and 1260 °C, while a very limited amount of the fcc MX2 phase shows up briefly between 847 and 890 °C. Fig.6 shows the changes in the site fraction in the first and second sublattices for the MX1 and MX2 phases. For MX1, it shows that the dominant species in the first sublattice changes from Nb to V with the decrease in temperature, while N is always the dominant species in the second sublattice. For the MX2 phase, Nb is always the dominant species for the first sublattice, while C has a slightly higher site fraction than N in the second sublattice. Therefore, V is an important element in MX1 at lower temperatures.

    M23C6becomes stable when the temperature is lower than 870 °C, and quickly becomes the dominant secondary phase with a decrease in temperature. Its dramatic concentration increase is due to the γ to α matrix phase transformation in that temperature range,which corresponds to the sudden carbon solubility decrease in the matrix.

    Fig.5. Mole fraction of the secondary phases in the Gr.91-based system.

    Fig.5 also shows that the Z phase is stable at temperatures below 790 °C, when MX1 becomes unstable. The formation of the Z phase takes V from the MX1 phase and causes the decomposition of the MX1 phase. This likely to be the reason why it has been experimentally observed that the Z phase ‘‘eats” away the MX phase during low-temperature long-term creep tests [54].

    3.5. Equilibrium cooling and Scheil simulations

    The above equilibrium cooling simulation can be used to understand the phase stability change during the ideal slow cooling.However,a real sample does not always reach equilibrium at each temperature under typical cooling conditions. Therefore, both equilibrium cooling and Scheil simulations were carried out in order to obtain a basic understanding of the phase stabilities under real cooling conditions.

    The equilibrium simulation,shown in Fig.5,predicts the formation of secondary phases under equilibrium cooling conditions—that is,the sample reaches global equilibrium at each temperature.It is used to simulate the phase stabilities for an extremely slow cooling rate.Meanwhile,the Scheil simulation predicts the formation of secondary phases under conditions similar to the quench condition. There are three major assumptions for Scheil simulations:①No diffusion occurs in solid phases once they are formed;②the liquid phase is homogeneous all the time; and ③the local equilibrium exists at the interface of the liquid and solid phases.It has been widely accepted that the equilibrium cooling and Scheil simulations can be adopted as the two boundary conditions. In other words,equilibrium cooling corresponds to an extremely slow cooling rate,while the Scheil simulation corresponds to a quenching process. Therefore, the quantity of the solid phases under real conditions should fall between what is predicted by the equilibrium cooling and Scheil simulations. In addition, using these two simulations may provide guidance regarding phase stability changes under various processing conditions, such as normalization, tempering, welding, and post-welding heat treatment. Under these conditions, the phase stability of the system will change toward the equilibrium condition as the time increases.

    Fig.6. Site fraction of Nb, V, C, and N (a,b) the MX1 and (c,d) the MX2 phases of the Gr.91-based system.

    Fig.7 shows the formation of the secondary phases—the M23C6,MX1, Z, and MX2 phases—during the solidification process of the Gr.91-based steel from the equilibrium cooling (solid line) and Scheil (dashed line) simulations. As shown in Fig.7(a), the M23C6phase precipitates out at 870 °C under equilibrium cooling conditions, but forms at 1225 °C during the Scheil simulation. In addition,much less of the M23C6phase will form during the Scheil simulation than during equilibrium cooling. This result indicates that the concentration of the M23C6phase formed during the real cooling process may be less than that formed during the equilibrium simulations. Therefore, Gr.91 steel has a tendency to form much more of the M23C6phase under annealing/operation conditions at elevated temperatures. This finding explains very well why much more of the M23C6phase has been observed in Gr.91 samples under high-temperature short-term creep testing conditions[24].

    On the other hand, the MX1 phase will form at 1260 °C during equilibrium cooling, as shown in Fig.7(b), but will disappear at temperatures below 770 °C. Under fast cooling conditions, the MX1 phase will form at 1410 °C; however, its maximum content is much lower than that resulting from equilibrium cooling. This finding indicates that the observed MX phase is a metastable phase at typical operation temperatures, that its formation is due to the fast cooling speed, and that it has a tendency to disappear under high-temperature short-term creep testing conditions. The observations in Figs. 7(a) and (b) explain very well the increased molar volume of the M23C6phase and the disappearance of the MX phase under high-temperature short-term creep test conditions [3].

    Furthermore, Fig.7(c) shows that the Z phase is a stable phase under equilibrium cooling conditions, and its formation temperature is lower than those of the M23C6and MX phases. However,the Z phase does not form during the Scheil simulation,indicating that formation of the Z phase is prohibited by the fast cooling rate.This finding explains very well why the Z phase is not observed in the initial microstructure,and why it gradually shows up and eats away the MX phase under low-temperature long-term creep test conditions [54]. For the MX2 phase, only a small fraction forms during equilibrium simulations in a short temperature range, as shown in Fig.2(b) and Fig.5, while the MX2 phase is not stable at all during the Scheil simulations.Its stability will greatly depend on the cooling rate and alloy compositions.

    3.6. Alloy composition effects on creep resistance

    Based on the systematic thermodynamic simulations, it was found that the stabilities of various secondary phases are imperative to the creep resistance of Gr.91 alloys. The simulation results also show that the alloy composition affects the stabilities of the secondary phases.To improve the creep resistance of Gr.91 alloys,the alloy composition needs to be optimized in order to obtain the desired microstructure in the HAZ after the welding process.

    As shown in Fig.8,there are four different critical temperatures for Gr.91 alloys. Ac1 (the blue line) is the boundary between the ICHAZ and the over-tempered region, while Ac3 (the red line) is the boundary between the FGHAZ and the ICHAZ during welding.The M23C6threshold temperature (the black solid line) is defined as the maximum temperature at which M23C6is thermodynamically stable. In welded alloys, this corresponds to the boundary between the FGHAZ and the CGHAZ. As mentioned above, type IV cracks only occur inside the FGHAZ and ICHAZ [55]. Many suggestions have been made to explain why it is possible for type IV cracks to be located within this region of the material [3,15];however, from a thermodynamic point of view, two secondary phases—M23C6coarsening and Z phase formation—have been observed and theorized to decrease the creep resistance between the FGHAZ and the ICHAZ [20,23,56].

    Fig.7. Results of the equilibrium cooling (solid line) and Scheil (dashed line) simulations for the Gr.91-based system. Molar fractions for (a) the M23C6 phase, (b) the MX1 phase, (c) the Z phase, and (d) the MX2 phase. The Z phase and MX2 phase were not stable during the Scheil simulations.

    Fig.8. Gr.91 M23C6 (black solid line) and Z phase (dashed line) threshold diagram,along with the Ac1 (blue solid line) and Ac3 (red solid line) temperatures.

    Assuming that the temperature gradient inside the HAZ during the welding process is not changing, adjusting the Ac1,Ac3, and M23C6threshold temperature will have a large impact on the thickness of the FGHAZ and ICHAZ. To reduce the whole thickness of the FGHAZ and ICHAZ, it is necessary to reduce the temperature difference between the Ac1 and M23C6threshold temperatures. As shown in Fig.8, reducing the carbon concentration of Gr.91 should be helpful in reducing the chance of type IV cracking.

    High-temperature short-term creep resistance is related to the coarsening of the M23C6phase [20,32-35]. Therefore, the creep resistance can be improved by reducing the thermodynamic stability of M23C6.Based on Fig.8,the M23C6threshold temperature will greatly decrease with a decrease in carbon concentration,which will decrease the stability of the M23C6at high temperatures and thereby increase the high-temperature short-term creep resistance.

    Low-temperature long-term creep resistance is related to the formation of the detrimental Z phase. Based on previous observations, the N-rich MX phase will eventually disappear through Cr diffusion from the grain matrix into MX, eventually transforming the MX phase into the Z phase [23]. From this observation, the assumption is that by reducing the Z phase threshold temperature,which is the maximum temperature at which the Z phase is thermodynamically stable,it should be possible to greatly improve the long-term creep resistance.As illustrated in Fig.8,a higher carbon concentration will be helpful in improving the short-term creep resistance.

    Similar thermodynamic simulations could be performed for the alloying elements, in order to investigate the effects of alloy composition on creep resistance. The approach used in the current work paves the way for the alloy composition optimization of Gr.91 in order to improve the creep resistance of this alloy under various applications.

    4. Summary and future work

    This work establishes a fundamental thermodynamic understanding using the CALPHAD approach by analyzing and simulating the relationship among the Ac temperatures, M23C6, and Z phase threshold temperatures, and stability and compositional change of the M23C6, MX, and Z phases in the HAZ of Gr.91 steel.

    Two different thermodynamic creep mechanisms under different application conditions contributing to a decrease in creep resistance and,eventually,type IV cracks in the HAZ were discussed:①M(fèi)23C6coarsening under low stress and high temperatures for short-term testing conditions through the Ostwald ripening effect[20,32-35]; and ②Z phase formation under high stress and low temperatures for long-term application conditions, which eventually decreases the overall MX phase stability within Gr.91 [22,23].

    Equilibrium cooling and Scheil simulations were carried out to show the phase stabilities under two extreme cooling conditions—that is, extremely slow cooling and quench conditions. The Scheil simulations showed the formation of a limited amount of the M23C6and MX1 phases under fast cooling conditions and above 1200 °C. In comparison, the equilibrium cooling simulations indicated that much more of the M23C6and Z phases form at low temperatures. Meanwhile, the MX phase is thermodynamically unstable and may disappear at operation temperatures. This finding successfully explains the experimental observations of the formation of more M23C6, the formation of the Z phase, and the disappearance of the MX phase under creep test conditions.

    In addition, effort was initiated to investigate the elements’effects on creep resistance by using carbon as a case study. To be specific,the effect of carbon on the four critical temperatures—that is,Ac1,Ac3,the M23C6threshold temperature, and the MX threshold temperature—was investigated. The findings show that the addition of carbon may have various effects on the microstructure and phase stabilities. It may increase the overall thickness of the FGHAZ and ICHAZ during the welding process, which in turn may increase the likelihood of type IV cracking. Furthermore, the addition of carbon may increase the stability of M23C6and decrease the stability of the Z phase,which may be detrimental to the shortterm creep resistance but beneficial to the long-term creep resistance. However, based on the thermodynamic model of the secondary phases—that is, the M23C6and Z phases—in Gr.91, it cannot be concluded that there is a specific carbon concentration that can change the overall stability of the secondary phases. The model highlights the overall trend of the threshold phase stability,while the mechanical properties can be altered depending on the welding conditions, which can in turn affect the HAZ microstructure. Therefore, the alloy composition needs to be optimized through both specific heat treatment conditions and creep experiments. In addition, similar simulations can reveal the role of various alloying elements in type IV cracking in the HAZ and in the creep resistance of Gr.91 steel, and will be carried out in future studies.

    Acknowledgements

    This material is based upon work supported by the US Department of Energy (DOE) (DE-FE0027800). The authors would like to thank the DOE National Energy Technology Laboratory program managers, Dr. Karol Schrems and Dr. Jessica Mullen, and Dr. Wei Zhang from Ohio State University, for their support and guidance.

    Disclaimer

    This paper was prepared as an account of work sponsored by an agency of the United States government.Neither the United States government nor any agency thereof, nor any of their employees,makes any warranty, express or implied, or assumes any legal liability or responsibility for the accuracy, completeness, or usefulness of any information, apparatus, product, or process disclosed,or represents that its use would not infringe upon privately owned rights. Reference herein to any specific commercial product, process,or service by trade name,trademark, manufacturer,or otherwise does not necessarily constitute or imply its endorsement,recommendation, or favoring by the United States government or any agency thereof. The views and opinions of the authors expressed herein do not necessarily state or reflect those of the United States government or any agency thereof.

    Compliance with ethics guidelines

    Andrew Smith, Mohammad Asadikiya, Mei Yang, Jiuhua Chen,and Yu Zhong declare that they have no conflict of interest or financial conflicts to disclose.

    国产精品自产拍在线观看55亚洲 | 久久99热这里只频精品6学生| 欧美亚洲 丝袜 人妻 在线| 国产极品粉嫩免费观看在线| 亚洲色图综合在线观看| 女人被躁到高潮嗷嗷叫费观| av有码第一页| 狠狠狠狠99中文字幕| 久久精品人人爽人人爽视色| 两人在一起打扑克的视频| 亚洲一区二区三区欧美精品| 亚洲精品乱久久久久久| 国产亚洲欧美精品永久| svipshipincom国产片| 高潮久久久久久久久久久不卡| 99国产精品一区二区三区| 99久久人妻综合| 亚洲国产日韩一区二区| 国产欧美日韩综合在线一区二区| 亚洲中文日韩欧美视频| 十八禁高潮呻吟视频| 日韩熟女老妇一区二区性免费视频| 两性夫妻黄色片| 欧美黄色淫秽网站| 美女国产高潮福利片在线看| 国产成人精品久久二区二区91| 香蕉丝袜av| 99国产精品一区二区蜜桃av | 日韩欧美一区视频在线观看| 天天操日日干夜夜撸| a在线观看视频网站| 一级片'在线观看视频| 日韩免费高清中文字幕av| 久久人人97超碰香蕉20202| 99热网站在线观看| 免费在线观看视频国产中文字幕亚洲 | 精品少妇久久久久久888优播| 亚洲精品第二区| 欧美在线黄色| a级毛片在线看网站| 国产男女内射视频| 97精品久久久久久久久久精品| 青春草视频在线免费观看| 久久人妻熟女aⅴ| 最新在线观看一区二区三区| 色婷婷久久久亚洲欧美| 国产日韩欧美在线精品| 伊人亚洲综合成人网| 亚洲国产欧美在线一区| 9热在线视频观看99| 亚洲国产看品久久| 高清黄色对白视频在线免费看| 欧美黄色淫秽网站| 亚洲午夜精品一区,二区,三区| 国产日韩欧美在线精品| 1024视频免费在线观看| 亚洲欧美日韩高清在线视频 | 男女午夜视频在线观看| 久久国产精品大桥未久av| 欧美亚洲 丝袜 人妻 在线| 97精品久久久久久久久久精品| 亚洲国产看品久久| 丰满人妻熟妇乱又伦精品不卡| 亚洲少妇的诱惑av| 欧美激情高清一区二区三区| 久久国产亚洲av麻豆专区| 久久国产精品影院| 久久亚洲国产成人精品v| 这个男人来自地球电影免费观看| 50天的宝宝边吃奶边哭怎么回事| 欧美日韩国产mv在线观看视频| 欧美精品亚洲一区二区| 满18在线观看网站| 老司机影院毛片| 成人免费观看视频高清| 国产精品 国内视频| 亚洲熟女精品中文字幕| 极品人妻少妇av视频| 日本猛色少妇xxxxx猛交久久| 国产99久久九九免费精品| 9热在线视频观看99| 亚洲av成人不卡在线观看播放网 | 亚洲av欧美aⅴ国产| 视频在线观看一区二区三区| 日韩中文字幕视频在线看片| 亚洲国产欧美网| av不卡在线播放| 黄色视频在线播放观看不卡| 国产精品99久久99久久久不卡| 日韩 亚洲 欧美在线| www.自偷自拍.com| 两个人免费观看高清视频| 久久久水蜜桃国产精品网| 狠狠婷婷综合久久久久久88av| 波多野结衣一区麻豆| av福利片在线| 大片电影免费在线观看免费| 国产人伦9x9x在线观看| 国产成人av激情在线播放| 两个人看的免费小视频| 水蜜桃什么品种好| 天天影视国产精品| 久久久水蜜桃国产精品网| 国产av国产精品国产| 久久久欧美国产精品| 色婷婷av一区二区三区视频| 中文字幕av电影在线播放| 丝瓜视频免费看黄片| 老司机影院毛片| 爱豆传媒免费全集在线观看| √禁漫天堂资源中文www| 中文字幕最新亚洲高清| 一区二区三区四区激情视频| 又黄又粗又硬又大视频| 中文字幕高清在线视频| 国产视频一区二区在线看| 国产真人三级小视频在线观看| 日韩三级视频一区二区三区| 国产免费福利视频在线观看| 青草久久国产| 又大又爽又粗| 国产熟女午夜一区二区三区| 国产伦人伦偷精品视频| 成年人免费黄色播放视频| 亚洲少妇的诱惑av| 久久久久久久国产电影| 男女无遮挡免费网站观看| 99re6热这里在线精品视频| 中文字幕人妻丝袜制服| 三级毛片av免费| 婷婷丁香在线五月| 午夜日韩欧美国产| 飞空精品影院首页| 人妻 亚洲 视频| 美女脱内裤让男人舔精品视频| av福利片在线| 国产精品一区二区免费欧美 | 亚洲精品美女久久久久99蜜臀| 天堂中文最新版在线下载| 18禁黄网站禁片午夜丰满| 国产精品一区二区在线不卡| 欧美日韩精品网址| 精品国产一区二区三区四区第35| 最近中文字幕2019免费版| 少妇裸体淫交视频免费看高清 | 满18在线观看网站| 国产欧美日韩综合在线一区二区| 亚洲欧洲日产国产| 久久久久久免费高清国产稀缺| 亚洲国产日韩一区二区| 大码成人一级视频| 丝袜在线中文字幕| 国产伦人伦偷精品视频| 久久久久久久精品精品| 男人添女人高潮全过程视频| 男人操女人黄网站| 久久久久网色| 国产精品九九99| 最新在线观看一区二区三区| 国产视频一区二区在线看| 国产欧美亚洲国产| 日本猛色少妇xxxxx猛交久久| 建设人人有责人人尽责人人享有的| 久久久水蜜桃国产精品网| 亚洲免费av在线视频| 欧美精品亚洲一区二区| 午夜福利免费观看在线| 欧美精品av麻豆av| av在线app专区| 国产福利在线免费观看视频| 久久99热这里只频精品6学生| 涩涩av久久男人的天堂| 日韩大码丰满熟妇| 夜夜骑夜夜射夜夜干| 人妻 亚洲 视频| 99香蕉大伊视频| 一本大道久久a久久精品| 午夜免费观看性视频| 后天国语完整版免费观看| 亚洲av片天天在线观看| 日本91视频免费播放| 欧美激情极品国产一区二区三区| 国产一区二区三区av在线| 国产精品一区二区免费欧美 | 高清av免费在线| 建设人人有责人人尽责人人享有的| 午夜福利免费观看在线| 国产精品欧美亚洲77777| 国产精品久久久久久精品古装| 国产精品av久久久久免费| 亚洲精品国产色婷婷电影| 国产欧美日韩一区二区三区在线| 国产亚洲av片在线观看秒播厂| 亚洲七黄色美女视频| 久久热在线av| 日本欧美视频一区| 制服诱惑二区| 老司机深夜福利视频在线观看 | 国产免费一区二区三区四区乱码| 最新在线观看一区二区三区| 国产精品一二三区在线看| 成在线人永久免费视频| 亚洲精品国产色婷婷电影| 成人国产一区最新在线观看| a级毛片在线看网站| 精品国内亚洲2022精品成人 | 欧美激情久久久久久爽电影 | 日韩有码中文字幕| 国产亚洲av高清不卡| 午夜福利在线免费观看网站| 青春草亚洲视频在线观看| www.自偷自拍.com| 中文欧美无线码| 大片免费播放器 马上看| 久热这里只有精品99| 亚洲天堂av无毛| 免费在线观看视频国产中文字幕亚洲 | 国产精品成人在线| 欧美日韩国产mv在线观看视频| 他把我摸到了高潮在线观看 | 在线观看舔阴道视频| 欧美变态另类bdsm刘玥| 爱豆传媒免费全集在线观看| 成人国产一区最新在线观看| 制服诱惑二区| 精品少妇一区二区三区视频日本电影| 啦啦啦 在线观看视频| av又黄又爽大尺度在线免费看| 在线观看www视频免费| 国内毛片毛片毛片毛片毛片| 国产99久久九九免费精品| 日本欧美视频一区| 日本vs欧美在线观看视频| 一级黄色大片毛片| 亚洲久久久国产精品| 爱豆传媒免费全集在线观看| 日本精品一区二区三区蜜桃| 免费观看人在逋| 黑丝袜美女国产一区| 久久久久久亚洲精品国产蜜桃av| 久久热在线av| 自线自在国产av| a级片在线免费高清观看视频| 老鸭窝网址在线观看| 欧美另类亚洲清纯唯美| av不卡在线播放| 国产真人三级小视频在线观看| 纵有疾风起免费观看全集完整版| 日本撒尿小便嘘嘘汇集6| 又黄又粗又硬又大视频| 热99久久久久精品小说推荐| av网站在线播放免费| 老熟妇仑乱视频hdxx| 啪啪无遮挡十八禁网站| 一本大道久久a久久精品| 亚洲精品美女久久av网站| 午夜激情久久久久久久| 亚洲成人免费av在线播放| 高潮久久久久久久久久久不卡| 男女无遮挡免费网站观看| 精品国产一区二区久久| 欧美 日韩 精品 国产| 69av精品久久久久久 | 日韩 欧美 亚洲 中文字幕| 啦啦啦在线免费观看视频4| 80岁老熟妇乱子伦牲交| 成人三级做爰电影| 久久精品国产a三级三级三级| 免费高清在线观看视频在线观看| 9热在线视频观看99| 黑丝袜美女国产一区| 50天的宝宝边吃奶边哭怎么回事| 亚洲精品一二三| 日韩中文字幕视频在线看片| 精品人妻1区二区| 国产av又大| 丝袜脚勾引网站| 美女脱内裤让男人舔精品视频| 精品国产乱子伦一区二区三区 | 久久 成人 亚洲| 久久久欧美国产精品| 18禁裸乳无遮挡动漫免费视频| 热re99久久精品国产66热6| 国产免费现黄频在线看| 中文精品一卡2卡3卡4更新| 免费久久久久久久精品成人欧美视频| 欧美大码av| 日本五十路高清| 日韩熟女老妇一区二区性免费视频| 日本vs欧美在线观看视频| 一级a爱视频在线免费观看| 成年人免费黄色播放视频| 国产97色在线日韩免费| 一级a爱视频在线免费观看| 男女床上黄色一级片免费看| 亚洲精品中文字幕一二三四区 | 黄色视频,在线免费观看| 桃花免费在线播放| 亚洲中文字幕日韩| 亚洲欧美精品自产自拍| 黄色怎么调成土黄色| 国产日韩欧美在线精品| 欧美xxⅹ黑人| 黄片播放在线免费| 国产亚洲av片在线观看秒播厂| 国产精品 国内视频| 日本av手机在线免费观看| 日本欧美视频一区| 久久性视频一级片| 国产精品免费大片| 日韩一区二区三区影片| 久久久精品免费免费高清| 免费在线观看黄色视频的| 9热在线视频观看99| 亚洲中文av在线| 大码成人一级视频| 国产一级毛片在线| 美女脱内裤让男人舔精品视频| 成人影院久久| 国产亚洲av高清不卡| 国产免费现黄频在线看| www.精华液| 天天躁夜夜躁狠狠躁躁| 欧美午夜高清在线| 精品久久久久久电影网| 久久国产精品影院| 日韩欧美免费精品| 日日摸夜夜添夜夜添小说| 婷婷色av中文字幕| 国产成人精品久久二区二区91| 窝窝影院91人妻| 国产主播在线观看一区二区| 中国美女看黄片| 午夜福利影视在线免费观看| 亚洲,欧美精品.| 免费人妻精品一区二区三区视频| 天天影视国产精品| 国产亚洲精品久久久久5区| 久久久久久久久免费视频了| 涩涩av久久男人的天堂| 免费观看a级毛片全部| 欧美 亚洲 国产 日韩一| kizo精华| 777米奇影视久久| 在线亚洲精品国产二区图片欧美| 国产成人精品久久二区二区91| 国产av国产精品国产| 在线观看免费视频网站a站| 日本wwww免费看| 国产视频一区二区在线看| 成在线人永久免费视频| 亚洲精品国产一区二区精华液| 黄网站色视频无遮挡免费观看| 亚洲精品美女久久av网站| 免费不卡黄色视频| 超碰成人久久| 搡老岳熟女国产| 黄频高清免费视频| 多毛熟女@视频| 999精品在线视频| 91av网站免费观看| 中文字幕最新亚洲高清| 亚洲 国产 在线| 国产有黄有色有爽视频| 亚洲综合色网址| 亚洲欧美精品综合一区二区三区| 亚洲视频免费观看视频| 性少妇av在线| 一二三四在线观看免费中文在| 欧美黄色片欧美黄色片| 欧美日韩一级在线毛片| 欧美性长视频在线观看| 欧美老熟妇乱子伦牲交| 精品国产一区二区三区久久久樱花| 成年人黄色毛片网站| 亚洲精品久久午夜乱码| 亚洲全国av大片| 美女高潮到喷水免费观看| 欧美在线一区亚洲| 国产精品一区二区在线不卡| 女人爽到高潮嗷嗷叫在线视频| 97在线人人人人妻| 女警被强在线播放| 国产无遮挡羞羞视频在线观看| 大型av网站在线播放| 99久久99久久久精品蜜桃| 日本精品一区二区三区蜜桃| 亚洲avbb在线观看| av在线app专区| 操出白浆在线播放| 亚洲成人免费电影在线观看| 最近最新中文字幕大全免费视频| 黄色毛片三级朝国网站| 国产精品香港三级国产av潘金莲| 欧美日韩福利视频一区二区| 少妇 在线观看| 亚洲九九香蕉| xxxhd国产人妻xxx| 一区福利在线观看| 操美女的视频在线观看| 黄色 视频免费看| 欧美精品一区二区大全| 国产精品亚洲av一区麻豆| 一区二区三区激情视频| cao死你这个sao货| 啦啦啦视频在线资源免费观看| 精品视频人人做人人爽| 免费观看a级毛片全部| 国产精品一区二区精品视频观看| 欧美激情极品国产一区二区三区| 午夜成年电影在线免费观看| 日本91视频免费播放| 日韩 欧美 亚洲 中文字幕| 国产极品粉嫩免费观看在线| 水蜜桃什么品种好| 一个人免费在线观看的高清视频 | 99久久精品国产亚洲精品| 一级a爱视频在线免费观看| 女性生殖器流出的白浆| 久久国产精品人妻蜜桃| 精品一区二区三卡| 女警被强在线播放| 一边摸一边做爽爽视频免费| 在线永久观看黄色视频| 日韩有码中文字幕| 无限看片的www在线观看| 18禁国产床啪视频网站| 免费不卡黄色视频| 亚洲精品国产av蜜桃| 69精品国产乱码久久久| 欧美成人午夜精品| 亚洲国产欧美一区二区综合| 欧美 亚洲 国产 日韩一| 久久国产精品大桥未久av| 久久久国产欧美日韩av| 精品一区二区三区四区五区乱码| 亚洲熟女毛片儿| 伊人亚洲综合成人网| 欧美成人午夜精品| 美女扒开内裤让男人捅视频| 一个人免费看片子| 汤姆久久久久久久影院中文字幕| 91老司机精品| 国产深夜福利视频在线观看| 高清黄色对白视频在线免费看| 一级毛片女人18水好多| 精品国产一区二区三区四区第35| 亚洲一卡2卡3卡4卡5卡精品中文| 下体分泌物呈黄色| 精品久久久久久久毛片微露脸 | 久久久久久久久免费视频了| 亚洲国产毛片av蜜桃av| 青草久久国产| 一二三四在线观看免费中文在| 91精品三级在线观看| 日本一区二区免费在线视频| 久久精品亚洲熟妇少妇任你| 久久亚洲国产成人精品v| 女人精品久久久久毛片| 久久国产精品影院| 丝袜美腿诱惑在线| 男女高潮啪啪啪动态图| 国产深夜福利视频在线观看| 国产成人精品无人区| 窝窝影院91人妻| 国产主播在线观看一区二区| 在线观看免费日韩欧美大片| 亚洲av片天天在线观看| 另类亚洲欧美激情| 久久这里只有精品19| 午夜激情av网站| 国产成人精品无人区| 又黄又粗又硬又大视频| 欧美日韩中文字幕国产精品一区二区三区 | 亚洲激情五月婷婷啪啪| 国产亚洲精品一区二区www | 精品少妇久久久久久888优播| 久久久国产欧美日韩av| 国产熟女午夜一区二区三区| 热99国产精品久久久久久7| 日本黄色日本黄色录像| svipshipincom国产片| 日本五十路高清| 91国产中文字幕| 9热在线视频观看99| 亚洲欧美精品自产自拍| 黄色a级毛片大全视频| 午夜免费成人在线视频| 欧美日韩视频精品一区| 亚洲专区国产一区二区| 中亚洲国语对白在线视频| 一边摸一边抽搐一进一出视频| 在线看a的网站| 亚洲自偷自拍图片 自拍| 俄罗斯特黄特色一大片| 久久精品国产综合久久久| 国产精品一区二区在线观看99| 91精品伊人久久大香线蕉| 午夜福利免费观看在线| 在线观看舔阴道视频| 亚洲欧美一区二区三区黑人| a级毛片黄视频| 亚洲精华国产精华精| 久热爱精品视频在线9| 亚洲精品自拍成人| videos熟女内射| 在线av久久热| 午夜影院在线不卡| 国产精品免费大片| 91麻豆精品激情在线观看国产 | 动漫黄色视频在线观看| 日韩有码中文字幕| 亚洲伊人色综图| 热99re8久久精品国产| 少妇粗大呻吟视频| 成年人黄色毛片网站| 欧美 日韩 精品 国产| 免费观看a级毛片全部| 狠狠精品人妻久久久久久综合| 美女主播在线视频| 成年av动漫网址| 国产成人一区二区三区免费视频网站| 亚洲精品国产区一区二| 如日韩欧美国产精品一区二区三区| 天堂俺去俺来也www色官网| 汤姆久久久久久久影院中文字幕| 女性被躁到高潮视频| 国产精品av久久久久免费| 亚洲 欧美一区二区三区| 久久av网站| 一级毛片电影观看| 精品国产一区二区三区四区第35| 中文字幕色久视频| 亚洲少妇的诱惑av| 一区二区av电影网| 欧美日韩亚洲高清精品| tocl精华| 不卡一级毛片| 国产黄色免费在线视频| 五月天丁香电影| 香蕉丝袜av| 一本综合久久免费| 美女脱内裤让男人舔精品视频| 国产成人a∨麻豆精品| 欧美黑人精品巨大| 久久久久国产一级毛片高清牌| 天天躁夜夜躁狠狠躁躁| 伊人亚洲综合成人网| 少妇猛男粗大的猛烈进出视频| 深夜精品福利| av又黄又爽大尺度在线免费看| 亚洲伊人色综图| 人人妻人人澡人人看| 国产亚洲一区二区精品| 国产色视频综合| 久久人人爽人人片av| 久久天躁狠狠躁夜夜2o2o| 一区二区三区激情视频| 这个男人来自地球电影免费观看| 亚洲三区欧美一区| 在线观看免费日韩欧美大片| 侵犯人妻中文字幕一二三四区| 日韩视频一区二区在线观看| 男男h啪啪无遮挡| 国产三级黄色录像| 99久久综合免费| 99国产精品免费福利视频| 国产成人av教育| 国产一级毛片在线| 69av精品久久久久久 | 美女主播在线视频| 狠狠精品人妻久久久久久综合| 热99re8久久精品国产| 亚洲少妇的诱惑av| 欧美黄色淫秽网站| 亚洲国产看品久久| svipshipincom国产片| kizo精华| 精品一区在线观看国产| 亚洲av美国av| 看免费av毛片| videosex国产| 色婷婷久久久亚洲欧美| 亚洲av欧美aⅴ国产| 久热爱精品视频在线9| 中文欧美无线码| 亚洲精品国产av蜜桃| 菩萨蛮人人尽说江南好唐韦庄| 91成人精品电影| 日韩有码中文字幕| tocl精华| 99热全是精品| 中亚洲国语对白在线视频| 亚洲国产精品成人久久小说| 亚洲七黄色美女视频| 久久人人爽人人片av| 国产熟女午夜一区二区三区| 亚洲精品一区蜜桃| 亚洲精品乱久久久久久| 国产欧美日韩一区二区三 | 亚洲精品成人av观看孕妇| 亚洲一卡2卡3卡4卡5卡精品中文| 久久精品国产a三级三级三级| 国产亚洲欧美精品永久| 国产又色又爽无遮挡免| 美女福利国产在线| 电影成人av| 亚洲精品国产区一区二| 国产成人欧美在线观看 | 两性午夜刺激爽爽歪歪视频在线观看 | 1024香蕉在线观看| 搡老乐熟女国产| 啦啦啦 在线观看视频| 91九色精品人成在线观看| 久久精品国产亚洲av高清一级|