    軋制壓下量對連擠連軋銅排組織和性能的影響

    2015-06-26 13:03:54運新兵王聰田甜趙穎裴久揚
    精密成形工程 2015年4期
    關(guān)鍵詞:壓下量銅排銅板

    運新兵,王聰,田甜,趙穎,裴久揚

    (大連交通大學(xué)連續(xù)擠壓教育部工程研究中心,遼寧大連116028)

    軋制壓下量對連擠連軋銅排組織和性能的影響

    運新兵,王聰,田甜,趙穎,裴久揚

    (大連交通大學(xué)連續(xù)擠壓教育部工程研究中心,遼寧大連116028)

    目的 連擠連軋是一種帶材生產(chǎn)新技術(shù),它結(jié)合連續(xù)擠壓與熱軋工藝的特點,研究軋制壓下量對連擠連軋銅排組織、性能的影響。方法 利用光學(xué)顯微鏡、萬能材料實驗機、布氏硬度儀對銅排連擠連軋的組織、性能進行試驗研究。結(jié)果 經(jīng)連續(xù)擠壓的銅排為等軸再結(jié)晶組織,平均晶粒尺寸為60μm左右,抗拉強度為220 MPa,延伸率為66%,沿銅排寬度方向的硬度分布不均勻。連擠連軋后的銅排晶粒沿軋制方向被拉長成扁平狀,隨著軋制壓下量的增加,相鄰晶界間距減小,最終形成纖維組織,沿銅排寬度方向的硬度分布較連續(xù)擠壓排坯均勻。當壓下量由2 mm增加到8 mm時,銅排的抗拉強度由250 MPa增加到400 MPa,延伸率由48%降低到13%,硬度由72HB左右增加到119HB。結(jié)論 得到了軋制壓下量對連擠連軋銅排組織和性能的影響規(guī)律。

    銅排;連擠連軋;軋制壓下量;組織與性能

    銅加工業(yè)是我國國民經(jīng)濟發(fā)展與國防建設(shè)的重要支柱產(chǎn)業(yè)之一,當前銅產(chǎn)品向高精度、高表面光潔度、性能高度一致性方向發(fā)展;工藝向節(jié)能、環(huán)保、短流程化方向發(fā)展[1—4]。隨著電子、信息、汽車工業(yè)的發(fā)展,銅及銅合金板帶尤其是高精度銅板帶的需求日益旺盛。高精度銅板帶的關(guān)鍵品種為電子材料、接插件、汽車端子、同軸電纜帶、變壓器帶、引線框架用銅板等[5]。

    傳統(tǒng)的銅板帶加工方法存在能耗高、含氧量高、材料利用率低以及板形難控制等困擾學(xué)術(shù)和工程界的問題[6—7]。連續(xù)擠壓因工藝簡單、產(chǎn)品長度不限、生產(chǎn)率高、性能好、尺寸精度高、節(jié)能環(huán)保等優(yōu)勢,廣泛應(yīng)用于有色金屬加工。目前銅及銅合金連續(xù)擠壓電磁線、母線到異型材已經(jīng)發(fā)展得較為成熟[8—10],并可將連續(xù)擠壓的銅板帶坯冷軋制造銅板帶[11],但板帶冷軋過程中因加工硬化需要退火處理,增加了加工成本和能耗。為此,文中提出了一種新的板帶加工方法——連擠連軋技術(shù)。連擠連軋技術(shù)結(jié)合了連續(xù)擠壓以及熱軋工藝的優(yōu)點。連擠連軋是以上引無氧鑄桿為坯料,在冷態(tài)下,經(jīng)連續(xù)擠壓輪槽對桿坯的摩擦驅(qū)動進入模腔產(chǎn)生劇烈的塑性變形,銅在連續(xù)擠壓過程中溫度急劇升高,最高甚至達到800℃左右,隨后完成連續(xù)擠壓熱塑性變形,擠出模具口處的材料帶有余溫,直接利用此余熱進行軋制,實現(xiàn)連擠連軋工藝,其成形原理如圖1所示。連擠連軋工藝無須加熱即可實現(xiàn)連續(xù)熱擠壓和熱軋,與傳統(tǒng)工藝對比具有較大的優(yōu)勢,是一種節(jié)能、節(jié)材、環(huán)保的有色金屬加工技術(shù),具有廣泛的應(yīng)用前景。

    圖1 連擠連軋工藝原理Fig.1 Principle of continuous extrusion and rolling

    2013年大連交通大學(xué)開始對純銅連擠連軋工藝的理論進行研究,通過理論計算確定連擠連軋咬入條件,建立了連擠連軋過程的速度協(xié)調(diào)方程,并應(yīng)用DEFORM-3D軟件對連擠連軋過程進行了有限元模擬[12—13]。劉富東針對連擠連軋工藝過程的 TLJ400連續(xù)擠壓機以及與之匹配的軋機速度匹配問題進行控制以及編程,成功解決了連續(xù)擠壓機與軋機的速度匹配[14]。

    文中采用金相顯微分析、拉伸實驗和硬度測量,通過實驗研究軋制壓下量對連擠連軋銅排組織、性能的影響規(guī)律,為連擠連軋成形銅排生產(chǎn)實際提供理論指導(dǎo)。

    1 實驗

    實驗原材料采用TU2純銅上引鑄造桿料,桿坯直徑為φ20 mm。實驗在TLJ400連續(xù)擠壓機和TRZ250熱軋機組成的實驗臺上進行。連續(xù)擠壓出的銅排直接進入軋機,軋制后水冷至室溫。擠壓出的銅排尺寸為80 mm×10 mm,進行軋制壓下量分別為2,4,6,8 mm的軋制實驗。

    用線切割機切割制成金相試樣和拉伸試樣,然后進行磨、拋、腐蝕,腐蝕劑為三氯化鐵鹽酸水溶液,用OLYMPUS-BX41M金相顯微鏡對連擠連軋銅排的顯微組織進行觀察;用AG-IC100kN電子萬能高溫材料實驗機測試抗拉強度和延伸率,用EQUOTIP2布氏硬度儀測試硬度。

    2 結(jié)果及討論

    2.1 原材料的顯微組織

    圖2 坯料截面顯微組織Fig.2 Microstructure of feedstock

    圖2為原材料的顯微組織照片。桿坯采用上引鑄造成形,由于純銅的導(dǎo)熱能力很強,桿坯在整個斷面的冷卻速度較快,且凝固比較均勻,柱狀晶發(fā)達,中心組織為等軸晶,周圍組織為柱狀晶[15],存在縮松、縮孔缺陷。

    2.2 經(jīng)連續(xù)擠壓的銅排顯微組織和性能

    圖3所示為經(jīng)連續(xù)擠壓后銅排坯的顯微組織。從圖3可以看出,連續(xù)擠壓后銅排坯橫向和縱向的晶粒都比較均勻,是典型的等軸晶,并存在部分退火孿晶組織,平均晶粒尺寸為60μm左右。銅排的抗拉強度為220 MPa左右,延伸率達66%。在連續(xù)擠壓過程中,坯料在擠壓輪的摩擦驅(qū)動下在腔體入口前產(chǎn)生激烈的塑性變形,在塑性變形熱和摩擦熱的共同作用下使坯料進入模腔時的溫度升高到700℃以上,擠壓過程中銅發(fā)生完全動態(tài)再結(jié)晶,因此銅排組織均勻,塑性高。

    圖3 連續(xù)擠壓銅排坯顯微組織Fig.3 Microstructure of copper strip by continuous extrusion

    銅排坯沿寬度方向的硬度分布如圖4所示。從圖4可以看出,連續(xù)擠壓后的銅排沿寬度的硬度分布不均勻,中間低,邊緣高,最高硬度值為55HB。這是由于連續(xù)擠壓變形過程中,金屬進入擴展腔后產(chǎn)生擴展變形,中間區(qū)域的金屬流動速度快、溫度高,而向邊緣擴展的金屬流速慢、溫度低。

    圖4 連續(xù)擠壓銅排硬度分布Fig.4 Hardness distribution of copper strip by continuous extrusion

    圖5 連擠連軋銅排的顯微組織Fig.5 Microstructure of copper strip by continuous extrusion and rolling

    2.3 軋制壓下量對銅排顯微組織和性能的影響

    圖5為4種軋制壓下量時連擠連軋銅排橫向、縱向顯微組織。從圖4可以看出,壓下量從2 mm增加到6 mm時,銅排微觀組織由沿軋制方向被拉長的扁平狀晶粒組成,相鄰晶界間距隨著壓下量增大而顯著減小。當壓下量為8 mm時,沿軋制方向形成纖維組織。

    圖5a為軋制壓下量為2 mm的組織,連續(xù)擠壓銅排坯的等軸晶粒沿厚度方向被壓扁,沿軋制方向被拉長,由于變形量小,晶界仍然清晰。由橫向顯微組織可以看到,在大量的尺寸為60μm左右的等軸晶中分布著大量尺寸細小的晶粒,細晶尺寸僅為20μm;而沿縱向晶粒分布較為均勻,晶粒沿厚度方向有被壓扁的趨勢,平均尺寸為60μm左右。

    圖5b為壓下量4 mm時的顯微組織。從圖5b可以看出,晶粒沿厚度方向明顯被壓扁,沿軋制方向被拉長,晶粒長度達到120μm。橫向晶粒尺寸不均勻,大晶粒中分布著少量30μm左右的小尺寸晶粒。圖5c為壓下量6 mm時的顯微組織,此時晶粒呈扁條狀,再結(jié)晶組織被破壞,50μm左右的晶粒中分布著少量尺寸為20μm左右的小晶粒,晶內(nèi)出現(xiàn)大量滑移帶。

    圖5d為壓下量8 mm時的顯微組織,軋制后銅排厚度僅為2 mm,在低速軋制時溫度降低明顯,此時的加工率達到80%。從圖5可以看出,銅排橫向中大量晶粒破碎,尺寸僅20μm左右,而縱向晶粒取向更加集中,軋制流線明顯,為典型的纖維組織。

    圖6、圖7分別為連擠連軋后銅排的抗拉強度和延伸率與軋制壓下量的關(guān)系。從圖6和7可以看出,銅排的抗拉強度隨著軋制壓下量的增加而升高。當壓下量從2 mm增加到6 mm時,抗拉強度由250 MPa增加到300 MPa;而當壓下量由6 mm增加到8 mm時,抗拉強度增加了100 MPa,達到400 MPa。

    圖6 銅排抗拉強度與壓下量的關(guān)系Fig.6 Relationship of tensile strength of copper strip with rolling reduction

    圖7 銅排延伸率與壓下量的關(guān)系Fig.7 Relationship of elongation of copper strip with rolling reduction

    延伸率隨著軋制壓下量增加而降低。壓下量為2 mm時,延伸率為48%,當壓下量增加到8 mm時,延伸率明顯降低,僅為13%。

    沿4個不同壓下量的銅排寬度方向均布的12個點測量硬度,結(jié)果如圖8所示。從圖8可以看出,連擠連軋后銅排的硬度有所提高,并且沿寬度的分布要均勻些。與連續(xù)擠壓的銅排相比,中心位置與邊緣位置硬度數(shù)值更接近。壓下量為8mm的銅排硬度明顯高于其他3個壓下量的銅排,其平均硬度達119HB,而其他3個軋制壓下量的平均硬度都在72HB左右。

    圖8 不同壓下量銅排的硬度分布Fig.8 Hardness distribution of copper strip by continuous extrusion and rolling with different rolling reductions

    軋制后的銅排力學(xué)性能呈現(xiàn)上述特征,是由于壓下量為2 mm到6 mm時,對于層錯能較低的銅,在一定的溫度和變形程度下部分晶粒發(fā)生了動態(tài)再結(jié)晶,隨著變形程度增加,強度、硬度增加,塑性降低。而當壓下量為8 mm時,銅排溫度低,單道次加工率達到了80%,變形劇烈,顯微組織中具有較高的位錯密度,位錯邊界形成束狀而不是均勻分布于晶粒中[16],因此此時銅排的抗拉強度、硬度顯著升高,塑性明顯降低。

    3 結(jié)論

    1)經(jīng)連續(xù)擠壓的銅排坯為等軸的再結(jié)晶組織,平均晶粒尺寸為60μm左右,抗拉強度220 MPa,延伸率為66%,沿寬度的硬度分布不均勻,中間低,邊緣高。

    2)隨著連擠連軋壓下量的增加,銅排的晶粒逐漸被壓扁,當壓下量為8 mm時,晶粒破碎,沿縱向形成明顯的纖維組織,橫截面晶粒尺寸僅20μm左右。

    3)當壓下量由2 mm增加到8 mm時,銅排的抗拉強度由250 MPa增加到400 MPa,延伸率由48%降低到13%,硬度由72HB左右增加到119HB,并且硬度沿銅排寬度分布較連續(xù)擠壓排坯更加均勻。

    [1]王碧文.科技創(chuàng)新引領(lǐng)中國銅加工業(yè)[J].中國有色金屬,2013,33(16):27—29. WANG Bi-wen.Technological Innovation to Lead Chinese Copper Processing Industry[J].China Nonferrous Metals, 2013,33(16):27—29.

    [2]龔壽鵬.高精度銅板帶材生產(chǎn)技術(shù)[J].上海有色金屬, 2012,34(1):46—49. GONG Shou-peng.High Precision Copper Strip Projects Fabrication Technology[J].Shanghai Nonferrous Metals, 2012,34(1):46—49.

    [3]韓晨,余金海,陳加圣.國內(nèi)銅板帶生產(chǎn)技術(shù)與加工裝備現(xiàn)狀概述[J].銅業(yè)工程,2012,114(2):12—16. HAN Chen,YU Jin-hai,CHEN Jia-sheng.Overview of Domestic Processing Technology and Equipment for Copper Strip and Sheet[J].Copper Engineering,2012,114(2): 12—16.

    [4]龔壽鵬.銅板帶材產(chǎn)品的現(xiàn)狀及發(fā)展[J].上海有色金屬,2011,32(3):140—143. GONG Shou-peng.The Status and Development of Copper Strip Products[J].Shanghai Nonferrous Metals,2011,32 (3):140—143.

    [5]王碧文.銅和銅合金板帶生產(chǎn)與市場[J].世界有色金屬,2007(12):34—36. WANG Bi-wen.Production and Market of Copper and Copper Alloy Strip[J].World Nonferrous Metals,2007(12): 34—36.

    [6]王碧文.銅和銅合金板帶生產(chǎn)與市場(續(xù))[J].世界有色金屬,2008(1):34—35. WANG Bi-wen.Production and Market of Copper and Copper Alloy Strip[J].World Nonferrous Metals,2008(1): 34—35.

    [7]金偉,任學(xué)平,張芮,等.西昌2050熱軋板形控制研究[J].精密成形工程,2013,5(3):48—50. JINWei,REN Xue-ping,ZHANG Rui,et al.Research on Control Strategy of Strip Profile for Xichang 2050 Hot Rolling Mill[J].Journal of Netshape Forming Engineering, 2013,5(3):48—50.

    [8]隋賢,宋寶韞,李冰,等.H65黃銅合金連續(xù)擠壓過程中的組織和性能演變特征[J].中國有色金屬學(xué)報,2009, 19(6):1049—1054. SUIXian,SONG Bao-yun,LI Bing,et al.Characteristic of Microstructure and Properties Evolution of H65 Brass Alloy during Continuous Extrusion Process[J].The Chinese Journal of Nonferrous Metals,2009,19(6):1049—1054.

    [9]孫健,劉平,劉新寬,等.Cu-Ni-Si合金連續(xù)擠壓過程中的組織演變及性能[J].中國有色金屬學(xué)報,2014,24 (4):944—949. SUN Jian,LIU Ping,LIU Xin-kuan,et al.Microstructure E-volution and Properties of Cu-Ni-Si Alloy during Continuous Extrusion Process[J].The Chinese Journal of Nonferrous Metals,2014,24(4):944—949.

    [10]WU Peng-yue,XIE Shui-sheng,LIQing-hua,et al.Effect of Extrusion Wheel Angular Velocity on Continuous Extrusion Forming Process of Copper Concave Bus Bar[J].Transactions of Nonferrous Metals Society of China,2007,17(2): 280—286.

    [11]程禹霖,運新兵,楊俊英,等.軋制變形量對連續(xù)擠壓純銅板帶組織性能的影響[J].塑性工程學(xué)報,2014,21 (5):77—81. CHENG Yu-lin,YUN Xin-bing,YANG Jun-ying,et al. Effect of Rolling Deformation on Microstructure and Mechanical Properties of Continuous Extrusion Copper Strip [J].Journal of Plasticity Engineering,2014,21(5):77—81.

    [12]YUN Xin-bing,YOUWei,ZHAO Ying,et al.Study on Continuous Extrusion and Rolling Forming Velocity of Copper Strip[J].Transactions of Nonferrous Metals Society of China,2013,23(4):1108—1113.

    [13]游偉.銅板帶連擠連軋工藝理論研究[D].大連:大連交通大學(xué),2013. YOU Wei.Theory Research on Continuous Extrusion and Rolling Process of Copper Strip[D].Dalian:Dalian Jiaotong University,2013.

    [14]劉富東,祁偉,運新兵.基于神經(jīng)網(wǎng)絡(luò)PID的連擠連軋速度控制系統(tǒng)[J].大連交通大學(xué)學(xué)報,2014,35(5):92—94. LIU Fu-dong,QIWei,YUN Xin-bing.Speed Control System Based on the Continuous Extrusion and Rolling of Neural Network PID[J].Journal of Dalian Jioatong University, 2014,35(5):92—94.

    [15]RODRIGUEZ JM,ESTEVA A,MEZA S.A Note on the Control of the Solidification Front in the Continuous Casting of Copper Tubes[J].Journal Materials Processing Technology,1999,96:42—47.

    [16]黃曉旭,蔡大勇,姚枚,等.冷軋多晶銅與多晶鋁形變顯微組織演變的研究[J].材料科學(xué)與工藝,2000,8(3): 1—5. HUANG Xiao-xu,CAIDa-yong,YAOMei,et al.Microstructure Evolution in Aluminum and Copper Deformed by Cold Rolling[J].Material Science&Technology,2000,8(3): 1—5.

    Effects of Rolling Reduction on Microstructure and Properties of Copper Strips during Continuous Extrusion and Rolling

    YUN Xin-bing,WANG Cong,TIAN Tian,ZHAO Ying,PEI Jiu-yang
    (Engineering Research Centre of Continuous Extrusion,Ministry of Education, Dalian Jiaotong University,Dalian 116028,China)

    The aim of this study was to investigate effects of rolling reduction onmicrostructure and properties of copper strips during continuous extrusion and rollingwhich was a new strip production technology combining the features of continuous extrusion and hot rolling.The microstructure and properties of copper strip during continuous extrusion and rolling were investigated by using opticalmicroscopy,universal testingmachine and Brinell hardnessmeasurement.The results indicated that recrystallized grainswere obtained by continuous extrusion,the average grain size,the tensile strength,and elongation were about60μm,220 MPa and 66%respectively,and the hardness distribution along the width of the copper strip was not uniform.The grains were elongated during continuous extrusion and rolling.With the rolling reduction increased,the adjacentgrain boundaries spacing gradually decreased and themicrostructures of copper strip gradually formed fibrous tissues,and hardness distribution became more uniform along the width direction of copper strip.The tensile strength increased from 250 MPa to 400 MPa,the elongation decreased from 48%to 13%and the hardness increased from 72HB to 119HB when the rolling reduction increased from 2 mm to 8mm.The influence pattern of rolling reduction onmi-crostructure and properties of copper strips during continuous extrusion and rolling was obtained.

    copper strip;continuous extrusion and rolling;rolling reduction;microstructure and properties

    10.3969/j.issn.1674-6457.2015.04.001

    TG376.51

    :A

    :1674-6457(2015)04-0001-05

    2015-05-16

    國家自然科學(xué)基金(51175055);高等學(xué)校博士學(xué)科點專項科研基金博導(dǎo)類資助(20132124110003)

    運新兵(1969—),男,天津?qū)幒尤?教授,博士生導(dǎo)師,主要研究方向為塑性成形CAE、連續(xù)擠壓理論與技術(shù)、模具CAD/CAM。

    猜你喜歡
    壓下量銅排銅板
    基于溫升試驗的載流銅排與接觸器連接結(jié)構(gòu)優(yōu)化
    重型機械(2022年2期)2022-04-18 07:48:32
    退火溫度及冷軋壓下量對低碳鋁鎮(zhèn)靜鋼退火織構(gòu)的影響①
    礦冶工程(2022年1期)2022-03-19 07:07:02
    中壓開關(guān)柜異性主母線動穩(wěn)定分析
    壓下量對工字鋼矯直質(zhì)量的有限元分析
    用于結(jié)晶器銅板表面強化的鎳基復(fù)合鍍層的制備與研究
    十個銅板
    特別健康(2017年11期)2017-03-07 11:38:21
    十個銅板
    益壽寶典(2017年36期)2017-02-26 06:10:06
    波譜法在覆銅板及印制電路板研究中的應(yīng)用
    動態(tài)輕壓下技術(shù)在軸承鋼GCr15連鑄矩形坯生產(chǎn)中的實踐
    冶金與材料(2015年5期)2015-08-20 02:14:18
    某電站發(fā)電機中性點銅排發(fā)熱分析
    天天操日日干夜夜撸| 一级毛片女人18水好多 | 精品少妇久久久久久888优播| 久久精品久久久久久噜噜老黄| 日韩大码丰满熟妇| 亚洲一区二区三区欧美精品| 国产精品二区激情视频| 精品亚洲乱码少妇综合久久| 精品人妻1区二区| 亚洲国产欧美日韩在线播放| 久久精品国产综合久久久| 黑人欧美特级aaaaaa片| 亚洲av成人精品一二三区| 国产黄频视频在线观看| 中文字幕另类日韩欧美亚洲嫩草| 国产精品麻豆人妻色哟哟久久| 秋霞在线观看毛片| 青青草视频在线视频观看| 丝袜美腿诱惑在线| 在线观看一区二区三区激情| 一级黄片播放器| 国产片内射在线| 麻豆国产av国片精品| 高清黄色对白视频在线免费看| 精品人妻1区二区| 热99国产精品久久久久久7| 久久国产精品人妻蜜桃| 国产一区二区在线观看av| www.av在线官网国产| 国产日韩欧美视频二区| 婷婷色综合大香蕉| 啦啦啦 在线观看视频| 亚洲图色成人| 国产亚洲一区二区精品| 亚洲av片天天在线观看| 男女边吃奶边做爰视频| 如日韩欧美国产精品一区二区三区| 国产不卡av网站在线观看| 久久精品亚洲熟妇少妇任你| 一边亲一边摸免费视频| 久久久久国产一级毛片高清牌| 少妇的丰满在线观看| 操出白浆在线播放| 久久精品久久久久久噜噜老黄| 男的添女的下面高潮视频| 日韩熟女老妇一区二区性免费视频| 80岁老熟妇乱子伦牲交| 国产精品久久久人人做人人爽| 两个人免费观看高清视频| 亚洲精品一区蜜桃| 亚洲熟女毛片儿| 丝袜在线中文字幕| 久久久久久人人人人人| 亚洲专区中文字幕在线| 日韩 欧美 亚洲 中文字幕| 久久精品国产a三级三级三级| 国产精品一区二区在线观看99| 国产高清视频在线播放一区 | 中国国产av一级| 成人国语在线视频| 18在线观看网站| 国产成人精品久久久久久| 99国产精品免费福利视频| 国产又爽黄色视频| 黄色视频在线播放观看不卡| 高清不卡的av网站| av天堂久久9| 国产精品 欧美亚洲| 久9热在线精品视频| 夫妻性生交免费视频一级片| 国产av一区二区精品久久| 欧美 日韩 精品 国产| 午夜日韩欧美国产| 青春草亚洲视频在线观看| 七月丁香在线播放| av网站免费在线观看视频| 欧美xxⅹ黑人| 天天操日日干夜夜撸| 精品久久久久久久毛片微露脸 | 成人黄色视频免费在线看| 中文字幕另类日韩欧美亚洲嫩草| 搡老岳熟女国产| 亚洲 国产 在线| 99热全是精品| 亚洲欧美清纯卡通| 亚洲欧美一区二区三区久久| 中文欧美无线码| 国产熟女欧美一区二区| 婷婷色综合大香蕉| 久久久久久久久免费视频了| 国产精品久久久久久精品古装| 午夜福利乱码中文字幕| 51午夜福利影视在线观看| 七月丁香在线播放| 手机成人av网站| 亚洲国产看品久久| 中国美女看黄片| 国产精品 欧美亚洲| 国产精品一区二区精品视频观看| 考比视频在线观看| 91国产中文字幕| 久久热在线av| 午夜视频精品福利| 色网站视频免费| 桃花免费在线播放| 女性被躁到高潮视频| 天天影视国产精品| 久久久亚洲精品成人影院| 777米奇影视久久| 老司机影院成人| 日韩视频在线欧美| 麻豆av在线久日| 男女高潮啪啪啪动态图| 婷婷成人精品国产| 成人免费观看视频高清| 可以免费在线观看a视频的电影网站| 亚洲av国产av综合av卡| 久久国产精品影院| 777米奇影视久久| 久久精品人人爽人人爽视色| 午夜免费男女啪啪视频观看| 一区二区三区乱码不卡18| 久久精品成人免费网站| 精品国产一区二区三区四区第35| 啦啦啦中文免费视频观看日本| 国产成人精品无人区| 久久狼人影院| 亚洲精品中文字幕在线视频| 中文字幕高清在线视频| 久久久精品94久久精品| 日本wwww免费看| 国产成人精品无人区| 狂野欧美激情性xxxx| 老司机亚洲免费影院| 久久亚洲精品不卡| 如日韩欧美国产精品一区二区三区| 一级毛片女人18水好多 | 久久天躁狠狠躁夜夜2o2o | 亚洲精品美女久久av网站| 精品熟女少妇八av免费久了| 欧美国产精品va在线观看不卡| avwww免费| 一级,二级,三级黄色视频| 中文字幕最新亚洲高清| 国产欧美日韩一区二区三区在线| 中文字幕另类日韩欧美亚洲嫩草| 亚洲欧洲精品一区二区精品久久久| 午夜两性在线视频| 亚洲成色77777| 亚洲av男天堂| 国产视频一区二区在线看| 尾随美女入室| 在线av久久热| 欧美成人午夜精品| 亚洲av电影在线进入| 久久久久久亚洲精品国产蜜桃av| 97精品久久久久久久久久精品| 男女床上黄色一级片免费看| e午夜精品久久久久久久| 免费在线观看视频国产中文字幕亚洲 | 亚洲欧美精品综合一区二区三区| 19禁男女啪啪无遮挡网站| 亚洲国产av新网站| 老司机在亚洲福利影院| 国产在线视频一区二区| 成年女人毛片免费观看观看9 | 久久人妻福利社区极品人妻图片 | 国产成人一区二区在线| 性少妇av在线| 一级黄片播放器| 久久鲁丝午夜福利片| 国产一区二区三区综合在线观看| 日本欧美视频一区| 亚洲色图 男人天堂 中文字幕| 99热国产这里只有精品6| 婷婷色综合大香蕉| 国产色视频综合| 777米奇影视久久| 看免费av毛片| 午夜激情久久久久久久| 男女高潮啪啪啪动态图| 中文字幕av电影在线播放| 不卡av一区二区三区| 国产老妇伦熟女老妇高清| 国产视频一区二区在线看| 欧美日韩精品网址| 日日摸夜夜添夜夜爱| 五月天丁香电影| 亚洲精品在线美女| 日韩视频在线欧美| 国产精品av久久久久免费| 观看av在线不卡| 免费观看人在逋| 日韩一本色道免费dvd| 国产欧美日韩综合在线一区二区| 亚洲av男天堂| 脱女人内裤的视频| 中文字幕精品免费在线观看视频| 国产高清国产精品国产三级| 午夜免费鲁丝| 两个人看的免费小视频| 一本—道久久a久久精品蜜桃钙片| 久久久久国产一级毛片高清牌| 18禁黄网站禁片午夜丰满| 大型av网站在线播放| 老汉色av国产亚洲站长工具| 亚洲精品一二三| 亚洲国产日韩一区二区| 国产有黄有色有爽视频| 久久天躁狠狠躁夜夜2o2o | 9色porny在线观看| 国产97色在线日韩免费| 午夜av观看不卡| 一级毛片黄色毛片免费观看视频| 美女脱内裤让男人舔精品视频| 交换朋友夫妻互换小说| 欧美成狂野欧美在线观看| 19禁男女啪啪无遮挡网站| 国产成人精品在线电影| 久久久久精品人妻al黑| 女人久久www免费人成看片| 久久中文字幕一级| 国产精品av久久久久免费| 精品人妻熟女毛片av久久网站| 另类亚洲欧美激情| 在线观看免费视频网站a站| 好男人电影高清在线观看| 妹子高潮喷水视频| 国产一区二区 视频在线| 美女主播在线视频| 成年美女黄网站色视频大全免费| 亚洲国产看品久久| 国产日韩欧美视频二区| 国产淫语在线视频| 最近中文字幕2019免费版| 伊人久久大香线蕉亚洲五| 搡老乐熟女国产| 校园人妻丝袜中文字幕| 国产高清videossex| 欧美大码av| 国产1区2区3区精品| 国产成人精品久久二区二区免费| 国产成人精品久久二区二区免费| 在线观看国产h片| 亚洲精品国产一区二区精华液| av片东京热男人的天堂| 爱豆传媒免费全集在线观看| 国产国语露脸激情在线看| 麻豆国产av国片精品| 嫁个100分男人电影在线观看 | 黄色怎么调成土黄色| 欧美少妇被猛烈插入视频| 亚洲欧洲日产国产| 日本午夜av视频| 男女之事视频高清在线观看 | 欧美黑人欧美精品刺激| 亚洲第一av免费看| 国产无遮挡羞羞视频在线观看| 国产精品久久久久成人av| 黑人猛操日本美女一级片| 女警被强在线播放| 久久免费观看电影| 看十八女毛片水多多多| 日韩视频在线欧美| 99国产精品一区二区三区| 久久久久精品国产欧美久久久 | 高清黄色对白视频在线免费看| 亚洲第一青青草原| 另类亚洲欧美激情| 欧美日韩综合久久久久久| 日本一区二区免费在线视频| 人人妻人人添人人爽欧美一区卜| 另类精品久久| www.av在线官网国产| 色婷婷av一区二区三区视频| 高清欧美精品videossex| 国产淫语在线视频| 久久久久久久久久久久大奶| 熟女少妇亚洲综合色aaa.| 久久精品亚洲熟妇少妇任你| 欧美黑人精品巨大| 国产精品 国内视频| www.熟女人妻精品国产| av不卡在线播放| 在线观看免费视频网站a站| 男女边摸边吃奶| 亚洲国产中文字幕在线视频| 日韩 亚洲 欧美在线| 每晚都被弄得嗷嗷叫到高潮| 在线av久久热| 99久久精品国产亚洲精品| 中国国产av一级| 另类精品久久| 色94色欧美一区二区| 国产精品人妻久久久影院| 亚洲美女黄色视频免费看| 丁香六月欧美| h视频一区二区三区| 女警被强在线播放| 亚洲欧美一区二区三区国产| videosex国产| 2018国产大陆天天弄谢| 激情视频va一区二区三区| 狠狠婷婷综合久久久久久88av| 国产视频首页在线观看| 极品少妇高潮喷水抽搐| 亚洲精品久久久久久婷婷小说| 一区二区三区四区激情视频| 久久精品国产a三级三级三级| 久久女婷五月综合色啪小说| 亚洲人成网站在线观看播放| 操出白浆在线播放| 一二三四在线观看免费中文在| 啦啦啦 在线观看视频| 亚洲综合色网址| 啦啦啦啦在线视频资源| 欧美日本中文国产一区发布| 中文欧美无线码| 中文字幕av电影在线播放| 亚洲国产看品久久| 亚洲av欧美aⅴ国产| 亚洲av电影在线观看一区二区三区| 久久人人97超碰香蕉20202| 久久人妻熟女aⅴ| 久久ye,这里只有精品| 久久久久久久大尺度免费视频| 久久久国产精品麻豆| 一边亲一边摸免费视频| 嫩草影视91久久| 欧美亚洲 丝袜 人妻 在线| 亚洲中文日韩欧美视频| 成年动漫av网址| 最新的欧美精品一区二区| 青春草亚洲视频在线观看| 欧美精品高潮呻吟av久久| 日本午夜av视频| www日本在线高清视频| 久久久久精品人妻al黑| 高清av免费在线| 男人舔女人的私密视频| 国产精品 国内视频| 久久久久久久精品精品| 搡老岳熟女国产| 极品人妻少妇av视频| 久久久精品区二区三区| 肉色欧美久久久久久久蜜桃| xxx大片免费视频| 老汉色∧v一级毛片| 国产伦人伦偷精品视频| 久久影院123| 国产一区有黄有色的免费视频| 久久精品亚洲av国产电影网| 黄片播放在线免费| 男人舔女人的私密视频| cao死你这个sao货| 欧美大码av| 嫩草影视91久久| 亚洲av日韩精品久久久久久密 | 精品一区二区三区四区五区乱码 | 无遮挡黄片免费观看| 国产有黄有色有爽视频| 一级毛片电影观看| 国产成人欧美| 黄色一级大片看看| 免费在线观看黄色视频的| 午夜福利影视在线免费观看| 免费在线观看完整版高清| 国产片内射在线| avwww免费| 美女扒开内裤让男人捅视频| 考比视频在线观看| 制服人妻中文乱码| 一本一本久久a久久精品综合妖精| 欧美大码av| 欧美激情 高清一区二区三区| 欧美大码av| 欧美黄色片欧美黄色片| 青春草亚洲视频在线观看| 亚洲av美国av| 日日爽夜夜爽网站| 成人亚洲欧美一区二区av| 精品久久久精品久久久| 国产免费福利视频在线观看| 97人妻天天添夜夜摸| 精品福利永久在线观看| 麻豆乱淫一区二区| 亚洲色图 男人天堂 中文字幕| 老汉色∧v一级毛片| 别揉我奶头~嗯~啊~动态视频 | 看十八女毛片水多多多| 人妻人人澡人人爽人人| 大型av网站在线播放| 老司机在亚洲福利影院| 嫁个100分男人电影在线观看 | 十分钟在线观看高清视频www| 无遮挡黄片免费观看| 精品久久蜜臀av无| 午夜福利一区二区在线看| 欧美精品av麻豆av| 国产在线视频一区二区| 99久久99久久久精品蜜桃| 国产男女超爽视频在线观看| 中文字幕精品免费在线观看视频| 伊人亚洲综合成人网| 国产精品99久久99久久久不卡| 久久天躁狠狠躁夜夜2o2o | 亚洲国产av影院在线观看| 国产日韩欧美亚洲二区| 一边亲一边摸免费视频| 亚洲,欧美精品.| 久久综合国产亚洲精品| 亚洲av日韩精品久久久久久密 | 一二三四社区在线视频社区8| 亚洲精品av麻豆狂野| 国产精品.久久久| 国产成人精品久久二区二区免费| 免费女性裸体啪啪无遮挡网站| 中文乱码字字幕精品一区二区三区| 一级片免费观看大全| 亚洲熟女毛片儿| 一区在线观看完整版| 自线自在国产av| 亚洲免费av在线视频| 精品一区二区三卡| 伦理电影免费视频| 久久鲁丝午夜福利片| 王馨瑶露胸无遮挡在线观看| 久久99一区二区三区| 一二三四在线观看免费中文在| 只有这里有精品99| 自线自在国产av| 亚洲精品乱久久久久久| 亚洲精品久久成人aⅴ小说| 国产高清国产精品国产三级| 岛国毛片在线播放| 中文字幕精品免费在线观看视频| 日韩一本色道免费dvd| 建设人人有责人人尽责人人享有的| 亚洲熟女精品中文字幕| 女人高潮潮喷娇喘18禁视频| 日本猛色少妇xxxxx猛交久久| 18禁国产床啪视频网站| 91精品国产国语对白视频| 久久女婷五月综合色啪小说| 亚洲一区中文字幕在线| 国产成人影院久久av| 每晚都被弄得嗷嗷叫到高潮| 国产亚洲av高清不卡| 色网站视频免费| 久久久久网色| 成人手机av| 自线自在国产av| 精品久久蜜臀av无| 熟女av电影| xxxhd国产人妻xxx| 精品国产乱码久久久久久男人| 美女国产高潮福利片在线看| 国产黄频视频在线观看| 亚洲国产精品国产精品| 成人国语在线视频| 成年动漫av网址| 久久久久久久久免费视频了| 老司机影院毛片| 久久精品亚洲熟妇少妇任你| 在线观看免费日韩欧美大片| 成人国产一区最新在线观看 | 亚洲av美国av| 99久久99久久久精品蜜桃| 亚洲一码二码三码区别大吗| 妹子高潮喷水视频| 亚洲免费av在线视频| 日韩欧美一区视频在线观看| 青春草亚洲视频在线观看| 国产三级黄色录像| 超碰成人久久| 久久性视频一级片| 亚洲少妇的诱惑av| 国产亚洲午夜精品一区二区久久| 久久精品国产亚洲av涩爱| 黄色毛片三级朝国网站| 国产精品.久久久| 在线观看免费高清a一片| 看免费成人av毛片| 久久青草综合色| 黄片小视频在线播放| 久久久久精品国产欧美久久久 | 婷婷成人精品国产| 久久99精品国语久久久| 精品少妇一区二区三区视频日本电影| 电影成人av| 欧美日韩av久久| 男女下面插进去视频免费观看| 老司机亚洲免费影院| 51午夜福利影视在线观看| 欧美人与性动交α欧美软件| 一级毛片黄色毛片免费观看视频| 亚洲国产最新在线播放| 亚洲av电影在线进入| 99久久99久久久精品蜜桃| 国产精品一区二区在线观看99| 国产成人精品久久二区二区免费| 视频区欧美日本亚洲| 国产av国产精品国产| 美女高潮到喷水免费观看| 日日爽夜夜爽网站| 亚洲av日韩精品久久久久久密 | 亚洲第一av免费看| 中文精品一卡2卡3卡4更新| 国产又爽黄色视频| 精品久久蜜臀av无| 无遮挡黄片免费观看| 成人国产av品久久久| 国产精品一国产av| 免费看av在线观看网站| 国产精品偷伦视频观看了| 性色av一级| 波多野结衣一区麻豆| 亚洲国产欧美日韩在线播放| 欧美人与性动交α欧美精品济南到| 999精品在线视频| 亚洲色图 男人天堂 中文字幕| 亚洲精品国产区一区二| 波多野结衣一区麻豆| 纯流量卡能插随身wifi吗| 日韩伦理黄色片| 男人舔女人的私密视频| 亚洲av成人精品一二三区| 亚洲伊人色综图| 久久久久久亚洲精品国产蜜桃av| 一个人免费看片子| 国产精品人妻久久久影院| 日韩 欧美 亚洲 中文字幕| 国产成人啪精品午夜网站| 18禁国产床啪视频网站| 久久久久久久精品精品| 久久久久精品人妻al黑| 黄色毛片三级朝国网站| 大陆偷拍与自拍| 欧美性长视频在线观看| cao死你这个sao货| 亚洲五月色婷婷综合| 18在线观看网站| 色婷婷久久久亚洲欧美| 新久久久久国产一级毛片| 老司机午夜十八禁免费视频| 日本91视频免费播放| 免费久久久久久久精品成人欧美视频| 国产伦理片在线播放av一区| 在线av久久热| 国产一区有黄有色的免费视频| 一级毛片电影观看| 中文字幕人妻丝袜一区二区| 欧美精品av麻豆av| 黄色视频不卡| 91九色精品人成在线观看| 国产女主播在线喷水免费视频网站| 夜夜骑夜夜射夜夜干| 国产高清不卡午夜福利| 成年人午夜在线观看视频| 国产成人精品久久二区二区91| 久热爱精品视频在线9| 亚洲精品av麻豆狂野| 亚洲精品国产色婷婷电影| 99re6热这里在线精品视频| 亚洲成人手机| 你懂的网址亚洲精品在线观看| 老司机在亚洲福利影院| 久久99精品国语久久久| 亚洲国产欧美日韩在线播放| 在线观看免费午夜福利视频| 黑人巨大精品欧美一区二区蜜桃| 日韩大片免费观看网站| 久久亚洲精品不卡| 久久人人爽av亚洲精品天堂| 五月开心婷婷网| 一本久久精品| 满18在线观看网站| 一边摸一边做爽爽视频免费| 99香蕉大伊视频| 日本91视频免费播放| 午夜久久久在线观看| 欧美黄色片欧美黄色片| 久久 成人 亚洲| 欧美激情高清一区二区三区| 国产片特级美女逼逼视频| 亚洲人成电影观看| 亚洲精品国产av蜜桃| 18禁裸乳无遮挡动漫免费视频| 在线观看免费视频网站a站| 亚洲情色 制服丝袜| 国产免费现黄频在线看| 老司机影院成人| 欧美亚洲 丝袜 人妻 在线| 中文字幕亚洲精品专区| 亚洲成国产人片在线观看| avwww免费| 亚洲国产精品一区三区| 国产精品一区二区在线观看99| 国产片特级美女逼逼视频| 久久99精品国语久久久| 欧美精品高潮呻吟av久久| 久久 成人 亚洲| 免费高清在线观看视频在线观看| 少妇精品久久久久久久| 啦啦啦视频在线资源免费观看| 亚洲精品久久久久久婷婷小说| 久久国产精品男人的天堂亚洲| 丝袜美足系列| 制服诱惑二区| 国产午夜精品一二区理论片| 欧美人与性动交α欧美软件| 18禁黄网站禁片午夜丰满| 欧美黄色片欧美黄色片| 午夜激情av网站| 亚洲成国产人片在线观看|